The behavior of void swelling and segregation in Fe-15Cr-xMn alloys and an alloy con- taining small amount of W and V was investigated by electron-irradiation.The compositional analysis in the irradiated regions including grain boundaries was performed.The resultdts show that there are many common features of irradiuation tehavior in the Fe-Cr-Mn and Fe-Cr-Ni systems while there are some significant differences,In the Fe-Cr-Mn alloy sys- tems void swelling was rematrkably suppressed and at the same time the radiation-induced segregation was also retarded,furthermore,the segregation was strongly retarded in an Fe-15Cr-15Mn alloy containing small amount of W and V.The results also show that Ni re- placed by Mn does not in general confer immunity from either swelling or phase instabilities. The phase instability is due to the different diffusion behavior of Ni and Mn in reponse to the operation of the inverse-Kirkendall effecr.Fe segregates to the microstructural sinks in the Fe-Cr-Mn alloys.The segregation of Fe often leads to the formation of ferrite.This fact is beneficial to reducing the swelling rate and segregation on the grain boundaries.
关键词:
electron irradiation
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,