Effect of Aging Time and Temperature on Mechanical Properties and Microstructural Evolution of 2205 Ferritic-Austenitic Stainless Steel

H. Keshmiri

材料科学技术(英文)

Duplex stainless steels (DSS) with ferritic{austenitic microstructures offer good combination of resistance to pitting corrosion and high strength that are not concomitantly attainable using conventional single phase austenitic or ferritic stainless steels. The DSS used in this investigation was 2205 alloy having a stable microstructure consisting of about 45% ferrite and 55% austenite at ambient temperature. In order to investigate aging behavior of this steel and the influences on mechanical properties, different aging treatments were conducted at temperatures of 350−950°C for various aging time of 15, 30, 60 and 180 min. The aged specimens were subjected to impact testing and hardness measurements. Finally, the changes in microstructure due to aging were studied by optical and scanning electron microscopy. The results showed that aging at temperatures lower than 550°C for different time had negligible effects on mechanical properties. Besides, no considerable changes in term of precipitation of harmful intermetallic particles were observed in microstructure below this temperature. However, a critical temperature range, 550−650 °C, was introduced here. Aging in this range led to a significant decrease in toughness and notable increase in hardness. The formation of intermetallic phases such as σ was recognized as the major reason for the observed changes.

关键词: Duplex stainless steel , null , null , null

Dendritic coarsening of gamma ' phase in a directionally solidified superalloy during 24,000h of exposure at 1173 K

Materials Characterization

Dendritic coarsening of gamma' was investigated in a directionally solidified Ni-base superalloy during exposure at 1173 K for 24,000 h. Chemical homogeneity along different directions and residual internal strain in the experimental superalloy were measured by electronic probe microanalysis (EPMA) and electron back-scattered diffraction (EBSD) technique. It was indicated that the gradient of element distribution was anisotropic and the inner strain between dendrite core and interdendritic regions was different even after 24,000 h of exposure at 1173 K, which influenced the kinetics for the dendrite coarsening of gamma' phase. (C) 2010 Elsevier Inc. All rights reserved

关键词: Superalloy;Coarsening;Exposure;Segregation;ni-base superalloy;evolution;field

Corrosion of Y, Fe and Fe-15Y in H_2-H_2S Mixture under 10~(-3) Pa S_2 at 600~800℃

Yan NIU , Weitao WU and Chaoliu ZENG (State Key Lab. for Corrosion and Protection , Institute of Corrosion and Protection of Metals , Chinese Academy of Sciences , Shenyang 110015 , China)F. Gesmundo and F. Viani (Instituto di Chimica , Facolta di Ingegneria , Un

材料科学技术(英文)

The corrosion of an Fe-based alloy containing 15 wt pct Y in H2-H2S mixtures under 10-3 Pa S2 was studied at 600~800℃ in an attempt to find materials with improved sulphidation resistance with respect to pure Fe. The presence of Y has been shown to be beneflcial, but not sufficient to the level expected. In fact, the alloy is able to form at all tested temperatures an external FeS layer, beneath which a zone containing a mixture of the two sulphides is also present. Thus,Fe can still diffuse through this region to form the outer FeS layer with non-negligible rate. The corrosion rate of Fe is considerably reduced by the Y addition. but the alloy corrodes still much more rapidly than Y. The sulphidation kinetics is generally rather irregular for both the pure metals, while the corrosion rate of the alloy decreases with time and tends to become parabolic after an initial period of 12~17 h. The sulphidation behaviour of the alloys is discussed by taking into account the presence of an intermetallic compound Fe17Y2 and the limited solubility of Y in Fe

关键词:

EFFECT OF OXYGEN CONTENTS ON OXYGEN POTENTIALS OF H_2O-H_2 AND H_2O-H_2-INERTS GAS MIXTURES

FANG Zheng CHEN Xinmin(H.M.Chen) Central South University of Technology , Changsha , China FANG Zheng , Associate Professor , Department of Chemistry , Central South University of Technology , Changsha , China

金属学报(英文版)

By taking the effect of oxygen contents into account,a new set of formulae which represents the oxygen potentials of H_2O-H_2 and H_2O-H_2-inerts gas mixtures has been derived.Classi- cal representation is only a particular case of it.Some of the variables affecting equilibrium atmosphere when trace oxygen is present and optimum preparation of the gas mixtures to min- imize errors have been discussed.The reliability of some of previous equilibrium experiments under the oxygen potentials controlled by H_2O-H_2 or H_2O-H_2-inerts gas mixtures has also been criticized.

关键词: gas equilibration method , null , null , null

Corrosion of Y, Fe and Fe-15Y in H-2-H2S mixture under 10(-3) Pa S-2 at 600 similar to 800 degrees C

材料科学技术(英文)

The corrosion of an Fe-based alloy containing 15 wt pet Y in H-2-H2S mixtures under 10(-3) Pa S-2 was studied at 600 similar to 800 degrees C in an attempt to find materials with improved sulphidation resistance with respect to pure Fe. The presence of Y has been shown to be beneficial, but not sufficient to the level expected. In fact, the alloy is able to form at all tested temperatures an external FeS layer, beneath which a zone containing a mixture of the two sulphides is also present. Thus, Fe can still diffuse through this region to form the outer FeS layer with non-negligible rate. The corrosion rate of Fe is considerably reduced by the Y addition, but the alloy corrodes still much more rapidly than Y. The sulphidation kinetics is generally rather irregular for both the pure metals, while the corrosion rate of the alloy decreases with time and tends to become parabolic after an initial period of 12 similar to 17 h. The sulphidation behaviour of the alloys is discussed by taking into account the presence of an intermetallic compound Fe17Y2 and the limited solubility of Y in Fe.

关键词: high-temperature sulfidation;most-reactive component;ni-nb alloys;h2-h2s mixtures;behavior;600-degrees-c-800-degrees-c;oxidation

Ferromagnetism and superparamagnetism of ZnCoO : H nanocrystals

Applied Physics Letters

ZnCoO:H nanocrystals are weak ferromagnetic at room temperature with a small coercivity and a small remanence, whereas ZnCoO nanocrystals are paramagnetic. The thermal irreversibility of zero-field cooling and field cooling magnetizations of ZnCoO:H nanocrystals corresponds to the existence of superparamagnetism due to the nanosize effect. X-ray photoelectron spectra show the incorporation of Co(2+) ions inside the ZnO lattice without changing the wurtzite structure. Our data suggest that hydrogen can induce ferromagnetism in ZnCoO and that ferromagnetic ZnCoO:H crystals with small particle size can show the superparamagnetism. (C) 2008 American Institute of Physics.

关键词: magnetic semiconductors;zno;hydrogen;cobalt

H+4, H+5和H+7团簇离子的测量和确认

杨百方 , 缪竞威 , 杨朝文 , 师勉恭

原子核物理评论 doi:10.3969/j.issn.1007-4627.2002.z1.038

报告了H+4, H+5, H+7等团簇离子的测量结果. 确认可以由H+3与一个或多个HH2相互作用形成较大的H+4, H+5, H+7等团簇离子.

关键词: H+4团簇离子 , H+5团簇离子 , H+7团簇离子

H型钢裂纹成因分析

王硕明 , 丁志军 , 于恒 , 张彩军

钢铁钒钛

研究了某H型钢厂采用半敞开方式浇注的H型钢腹板裂纹产生的原因.在该厂选取了26块有代表性裂纹的试样进行了细致的研究,研究认为:H型钢腹板裂纹主要是由钢中夹杂物因素造成,通过对钢中T[O]的研究发现,中间包T[O]量平均为94×10-6,铸坯中T[O]平均为60.8×10-6,同时对比1流铸坯和2流铸坯的T[O]量变化可以发现,中间包流场分布不合理.对该厂现有的中间包进行FLUENT模拟后发现,中间包稳流器矮坝较低,不能完全消除短路流,尤其在浇注后期,矮坝损耗殆尽,基本不起作用,短路流严重,应加以优化.

关键词: H型钢 , 裂纹 , 夹杂物 , 数学模拟

亚稳态He(23S)原子与N2H4分子传能产物的发光研究

胡义华 , 刘美希 , 陈丽 , 王小涓 , 储焰南 , 曹德兆

量子电子学报 doi:10.3969/j.issn.1007-5461.2001.04.008

本文在流动余辉装置上,研究了亚稳态He(23S)原子与N2H4分子碰撞传能,观察到了激发态产物NH(A3II→X3∑+)、NH(c1II→a1△)、NH2(A2A1→X2B1)的发射光谱,由相对光谱强度求得了形成各产物的通道比;分析NH(A3II,v'=0)的转动分辨谱的结果表明,v'=0能级上的转动布居是"双模”分布,激发态产物NH(A)、NH2(A)的形成机理可能是: He(23S)+N2H4→N2H4*→NH(A)+NH2(A)+H.

关键词: 碰撞传能 , 化学发光 , NH(A3Ⅱ)的发射光谱

国内热轧H型钢工艺特点

徐峰 , 何彩红 , 徐勇

钢铁研究

简述了国内H型钢的发展现状,通过列举国内典型H型钢生产线,介绍分析了轧制H型钢的1-3-1、1-3和连轧三种工艺布置,以及目前轧制H型钢的X-X和X-H两种方法.根据目前国内生产状况,提出了H型钢技术改进的几项措施.

关键词: H型钢 , 生产工艺 , 万能轧机