Viscosities Behavior of CaO-SiO2-MgO-Al2O3 Slag With Low Mass Ratio of CaO to SiO2 and Wide Range of Al2O3 Content

TANG Xu-long , ZHANG Zuo-tai , GUO Min , ZHANG Mei , WANG Xi-dong

The present paper is aimed at recycling of coal ash and blast furnace slag to produce mineral wool. Considering the mineralogical constitutions of coal ash and blast furnace slag, the primary quaternary slag compositions of CaO-SiO2-MgO-Al2O3 with basicity (mass ratio of CaO to SiO2) ranging from 05 to 09 and alumina ranging from 5% to 20% were investigated through a rotating cylinder method. The experimental results indicated that the viscosities decreased with increasing basicity above the liquidus temperature, and increased with increasing alumina content, and the maximum values were reached and as the alumina content was 20%, followed by the decrease with further increasing alumina content due to its amphoteric behavior. The amphoteric behavior of Al2O3 also performed in the relationship between viscosity and non-bridging oxygen per tetrahedrally-coordinated atom (NBO/T), and the viscosities decreased with increasing the NBO/T except the slag with a basicity 05 and Al2O3 20% which have a low NBO/T value and a low viscosity than others.-

关键词: viscosity , mineral wool , NBO/T , slag-

THEREVERSSE TRANSFOR MATION OF THE STERSS INDUCEDεMIN FE 17MN 10CR 5SI 4NIALLOY

Q.S. Liu1 , 2 , 3) , L.C. Zhao3) , G.X. Dong2) and N.J. Gu1) 1) Heibei University of Technology , Tianjin 300130 , China 2) Tianjin Institute of Technology , Tianjin 300191 , China 3) Harbin University of Technology , Harbin 150001 , China

金属学报(英文版)

Theconstruction changinginthereversetransformation ofthestress induced εMin Fe 17 Mn 10 Cr 5 Si 4 Ni alloy is carefully inspected in transmission electron microscope, and then stress induced εM procedure of reverse transformation is analyzed. The behavior of reverse transformationisdissimilar when the organization of εMis different. The reversetransfor mation ofεM withtheshapeofsingle plateandstripisrelativelyeasy,anditsreversibilityincrystallographiciseasilytocarryout,fortheεM with multilayerstructure,thereversetrans formationtakes placein isolatedlayers, fortheεMthat grows well,thereversetransforma tion isrelatively difficult becauseofthe ductile harmonization between itsinternalorganiza tion structures.

关键词: stress induced εM , null , null

[C16min]Br修饰的多壁碳纳米管及其与低密度聚乙烯复合材料的制备及介电性能

徐佩 , 卢旭鑫 , 汪传斌 , 杨善中 , 孙晓红 , 丁运生

高分子材料科学与工程

为改善多壁碳纳米管(MWNT)在低密度聚乙烯(LDPE)中的分散性及复合材料的界面特性,采用溴化-1-十六烷基-3-甲基咪唑基离子液体([C16min]Br)对MWNT进行表面改性,并用Raman光谱对改性效果进行了表征.将经过修饰的碳纳米管(MIL)与LDPE熔融共混得到MIL/LDPE复合材料,采用场发射扫描电子显微镜(FESEM)和阻抗分析仪(LCR)对复合材料的结构与介电性能进行了分析.结果表明,相比与MWNT/LDPE(渗流阈值为5.2％,介电常数为82,介电损耗为0.93),MIL/LDPE(渗流阈值为9.1％,介电常数为169,介电损耗为0.51)介电常数增大,介电损耗降低.并且在低温时,MIL/LDPE介电常数随温度的变化甚小,显示出良好的温度-介电常数特性.

关键词: 咪唑基离子液体 , 碳纳米管 , 低密度聚乙烯 , 介电性能

住友金属用QSP工艺进行8m／min的高拉速试验

上海金属

关键词:

1998 COMPREHENSIVE TABLE OF CONTENTS

中国腐蚀与防护学报

N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....

关键词:

提高本钢265 m2冷烧结矿及原料检验代表性的实践

李凤娟 , 吕国光

金属世界 doi:10.3969/j.issn.1000-6826.2014.04.14

通过对烧结配料所需原料及对冷烧结矿成品检验采制样方法的分析，找出影响检验结果真实性的因素，采取有效的改进措施，使本钢原料厂一次配料、本钢炼铁厂265 m2烧结二次配料及265 m2烧结系统各项稳定率有了很大的提高，烧结矿实物质量和各项技术质量指标有了很大的进步，保证了高炉的稳定顺行。
　　提高本钢265 m2冷烧结矿及原料检验代表性的实践
　　Practice of Improving the 265 m2 Cold Sinter and Raw Material Inspection Representative
　　供稿|
　　李凤娟,吕国光/
　　LI Feng-juan, LV Guo-guang
　　DOI：10.3969/j.issn.1000-6826.2014.04.14
　　导读内容
　　本钢炼铁厂265 m2烧结机生产所需要的含铁原料比较复杂，一次配料料种较多，且烧结含铁原料是由本钢原料厂二车间供料，原料质量的不稳定，会影响烧结矿质量的提高和新一号高炉的强化及高炉技术指标的改善。本钢质量管理中心驻冷烧检查站加强了对烧结配料所需原料及对冷烧结矿成品检验采制样代表性的研究，采取了一些改进措施，达到了良好的效果。含铁料成分稳定率、烧结矿各项质量和技术指标在稳步地提高。下面，对本钢质量管理中心驻冷烧检查站就提高采样及检验过程的准确性所采取的措施和办法进行说明。
　　烧结矿采样是半自动采样，每两小时采样一次，作为一个批次，来代表整个2h烧结矿的成份。

关键词:

尼龙612的等温结晶动力学

王玉东 , 付鹏 , 李晓光 , 刘民英 , 赵清香

高分子材料科学与工程

用差示扫描量热(DSC)研究了尼龙612的等温结晶动力学.实验结果表明,在所研究的等温结晶温度范围内(184℃、186℃、188℃、190℃、192℃),尼龙612达到最大结晶速率时的时间、半结晶期和动力学结晶速率常数分别为:O.12min、0.19 min、0.22 min、0.29 min、0.59 min;0.15 min、0.22 min、0.24 min、0.33 min、0.64 min和22.03 min<'-1>、23.28min<'-1>、8.85 min<'-1>、5.15 min<'-1>、1.93 min<'-1>.等温结晶过程符合Avrmi方程,二次结晶现象不明显.在等温结晶过程中得到的Avrmi指数n在1.81～2.32之间,由理论分析可知,尼龙612等温结晶是一维生长和二维盘状生长.由Arrhenius方程求得尼龙612的等温结晶活化能ΔE=-209.5 kJ/mol.

关键词: 尼龙612 , 等温结晶动力学 , 结晶活化能

在不同时间下退火对非晶硅薄膜晶化的影响

靳瑞敏 , 陈兰莉 , 罗鹏辉 , 郭新峰 , 卢景霄

材料导报

用玻璃作衬底在不同温度下用PECVD法直接沉积非晶硅(a-Si∶H)薄膜,在400℃和500℃分别光退火5min、10min、20min、30min、40min、60min、120min,用拉曼光谱分析前后样品,发现随着晶化时间的延长晶化效果越好,500℃退火的薄膜比400℃的晶化效果好.

关键词: PECVD法 , 非晶硅薄膜 , 光退火晶化 , 拉曼光谱

冷却速度对T91相变速度和产物的影响

殷红旗 , 刘永长 , 宁保群 , 徐荣雷 , 张尧卿 , 韩雅静

材料科学与工程学报 doi:10.3969/j.issn.1673-2812.2007.01.030

本文研究了T91钢冷却过程中,不同冷却速度(10 k/min(200 k/min)对相变速度和产物的影响.研究表明不同的冷却速度生成的组织差别较大,在较低速冷却下(10 k/min和30 k/min)的组织为较多的先共析铁素体和板条马氏体,中速冷却(30 k/min和50 k/min)基本都为板条马氏体,在较高速冷却过程中(100 k/min和200 k/min)组织中除了板条马氏体还出现了片状马氏体,另外冷却速度还影响了相变开始点和相变速度.

关键词: T91 , 冷却速度 , 相变