ELECTRON MICROANALYSIS FOR LASER MELTED ZONE IN 45 STEEL WITH Fe-Ni-Cr COATING

CHENG Yongxing LI Genfu YU Shaoluo Shanghai University of Engineering Science , Shanghai , China WANG Huimin No.11 Institute of China State Shipbuilding Corp. , Shanghai , China Associate Professor , Dept.No.5 , Shanghai University of Engineering Science , 350 Xianxia Road , Shanghai , China

金属学报(英文版)

The Fe-Ni-Cr coating laver has been alloyed with 45 steel base metal by transverse.flow type CO_2 gas laser of maximum output 5kW.The characteristics of the melted zone and the es- sence of the“bright band”has been investigated using the electron microscopy.The results show that the“bright band”belongs to the melted zone and is a vertical section of the plane crystal,The width of the“bright band”equals the height of the plane crystal,which decreases with the increase of laser beam scanning rate and the decrease of laser power.This has been explained in terms of constitutional supercooling G/R.

关键词: laser alloying , null , null

EFFECT OF Mg AND Zr ADDITION ON CREEP CRACK GROWTH BEHAVIOUR OF A Ni-BASE SUPERALLOY

GUO Encai XU Fengqin Central Iron and Steel Research Institute , Ministry of Metallurgical Industry , Beijing , China GUO Encai , Dept.No.5 , Central Iron and Steel Research Institute , Ministry of Metallurgical Industry , Beijing , China

金属学报(英文版)

The creep crack growth(CCG)and the time to carck initiation and rupture of specimen (t_(rc)and t_r)were measured by means of electrical potential method on single edge notched specimens at 700℃.The field near the crack tip under steady-state creep was represented by energy rate integral(C~*),and the CCG rate as a function of C~* has been obtained.The agreement between the predicted and observed t_(rc)values is quite good.It was found that the addition of small amount of Mg and Zr in the alloys causes t_(rc)and t_r of the specimens to in- crease significantly.

关键词: Ni-base alloy , null , null , null , null , null

用DEPT135测定Resol的组成及微细结构参数

杨金瑞 , 余尚先 , 顾江楠

高分子材料科学与工程

通过对resol(羟甲基酚化合物和低分子量羟甲基酚树脂)DEPT135图谱的分析讨论,得到一系列计算resol微细结构参数的经验公式.根据DEPT135图谱可判断是否发生缩聚反应,根据经验公式可计算酚单体各个活性点参与反应百分率或酚羟基导入率、不同类型缩聚所占百分率及低分子量羟甲基酚树脂的平均核体数.

关键词: 羟甲基酚化合物 , 羟甲基酚树脂 , DEPT135 , 结构参数

ANALYSIS OF THE MAGNETIC-ANISOTROPY IN SMCO5 AND GDCO5

Journal of Applied Physics

The temperature dependence of the magnetic anisotropy constant K1 for SmCo5 and GdCo5 is well reproduced by calculations based on a single-ion model taking into account the anisotropies of the R-Co exchange interaction and the Co-sublattice magnetic moment. The anisotropy of the R-Co exchange interaction plays an important role in reproducing the experimental K1(T) for SmCo5 and GdCo5. It is found that the absolute value of the second order crystalline electric field parameter A2(0) in SmCo5 decreases monotonically with increasing temperature.

关键词: intermetallics

金属间化合物CePd5,PrPd5和NdPd5的晶体结构

张康侯

稀有金属材料与工程

稀土金属对富Pd合金的氢化性能、磁学性能和催化性能有显著的影响,对Pd-RE合金系中最富Pd的化合物的研究是有意义的.本工作通过恰当的熔炼和热处理工艺制备出单相的金属间化合物CePd5,PrPd5和NdPd5,并应用X射线衍射分析确定了它们的晶体结构和晶格参数.研究发现:在Pd-Ce二元系中,最富Pd的化合物是具有CaCu5型六方结构的CePd5;而在Pd-Pr和Pd-Nd二元系中最富Pd的化合物分别是具有SmPt5型正交结构的PrPd5和NdPd5.报道了经指标化的这3种金属间化合物的x射线衍射数据,确定CePd5的晶格参数a=0.5372 nm,c=0.4178 nm;PrPd5和NdPd5的晶格参数分别是a=0.5278 nm,b=0.9239 nm,c=2.575 am和a=0.5265 nm,b=0.9219 nm,c=2.570 nm.并对Pd-RE合金系和Pt-RE合金系中最富Pd化合物的化学计量和晶体结构进行了对比.

关键词: 金属间化合物CePd5 , PrPd5 , NdPd5 , X射线衍射数据 , 晶体结构

ACTIVATION OF TiFe-LaNi_5 COMPOUND PARTICLES

(State Key Laboratory of RSA , Institute of Metal Research , Chinese Academy of Sciences , Shenyang 110015 , China)(Shenyang Institute of Technology , Shenyang 110015 , China)

金属学报(英文版)

Through controlled mechanical alloying treatment, TiFe and LaNi5 particles combined together on the surface of TiFe. This kind of compound particles can be easily activated at room temperature and an H2-pressure of 4.0 MPa. LaNi5 particles provided "window" and "path" for entrance of hydrogen from the surface to the interior of TiFe alloy.

关键词: TiFe-LaNi_5 compound particle , null , null

RECo_5热膨胀反常研究

杨应昌 , 何文望 , 林勤

金属学报

本文研究了RECo_5在居里温度附近热膨胀反常的特点。利用高温X射线衍射方法从室温到600℃测定了CeCo_5,Ce(Co_(0.6)Cu_(0.2))_5和Ce(Co_(0.9)Fe_(0.1))_5晶格常数α和c随温度的变化。在居里点附近,CeCo_5的晶格常数c随温度的变化存在明显的拐折,在磁有序区域内具有因瓦反常,而晶格常数α随温度基本保持连续线性的变化,没有反常效应.用Cu原子部分取代Co原子以后,Ce(Co_(0.3)Cu_(0.2))_5沿c轴的热膨胀反常显著减弱。利用中子衍射研究了RE(Co,Cu)_5结构的有序性,从中子衍射的谱线分析表明,在CaCu_5型结构的RE(Co,Cu)_5金属间化合物中,Cu原子优先占据2c位置,由此解释了RECo_5热膨胀反常的原因。

关键词:

Crystal structure and phase relationships in the pseudobinary system Nd5Si4-Nd5Ge4

Journal of Alloys and Compounds

Phase relationships at ambient temperature in the pseudobinary system Nd5Si4-Nd5Ge4 were studied by X-ray powder diffraction (XRD). Four structurally distinct phase regions exist in this system. The Nd5Si4-based solid solution in which Ge statistically substitutes for Si crystallizes in the tetragonal Zr5Si4-type structure with space group P4(1)2(1)2. The Nd5Ge4-based solid solution in which Si statistically substitutes for Ge crystallizes in the orthorhombic Gd5Ge4-type structure with space group Pnma. There are two ternary intermediate phases, which crystallize in the orthorhombic Gd5Si4-type structure with space group Pnma and the monoclinic Gd5Si2Ge2-type structure with space group P112(1)/a. The Rietveld powder diffraction profile fitting technique was used for refinement of the crystal structure. The lattice parameters, atomic positions and interatomic distances for Nd5Si4, Nd5Si2.8Ge1.2, Nd5Si2Ge2 and Nd5Ge4 were derived. (C) 2002 Elsevier Science B.V. All rights reserved.

关键词: rare earth compounds;crystal structure;X-ray diffraction;gd-5(si2ge2);transition;gd-5(sixge1-x)(4)

V5Cr5Ti合金的高温拉伸性能及其断口特征

李明 , 宋月清 , 崔舜 , 于兴哲 , 李增德

稀有金属 doi:10.3969/j.issn.0258-7076.2007.04.004

采用真空自耗重熔法制备了V5Cr5Ti合金,测试了V5Cr5Ti合金的高温拉伸性能,分析了高温拉伸断口的宏观、微观形貌,探讨了钒合金的断裂机理.结果表明:随温度升高,V5Cr5Ti合金的强度性能下降,塑性性能先降低后升高;在700～900 ℃,V5Cr5Ti合金仍具有良好的强韧性综合性能;其高温断口特征表现为韧性断裂为主,韧性和脆性特征共存的现象.

关键词: 真空自耗重熔 , V5Cr5Ti , 高温拉伸性能 , 韧性断裂 , 脆性断裂

V-5Cr-5Ti合金再结晶规律及其动力学

李增德 , 崔舜 , 林晨光 , 李明

稀有金属 doi:10.3969/j.issn.0258-7076.2009.06.004

研究了V-5Cr-5Ti合金在900～1100 ℃之间的再结晶规律, 概括了V-5Cr-5Ti合金的再结晶动力学机制. 结果表明, 合金冷变形板材在950～1050 ℃下退火处理, 可获得细小、均匀的等轴晶; 初步推导了V-5Cr-5Ti合金再结晶动力学机制, 符合Avrami-Erofeev形核长大机制; 并计算了V-5Cr-5Ti合金再结晶激活能Q_r, 其值为261.91～289.67 kJ· mol~(-1).

关键词: V-5Cr-5Ti合金 , 再结晶 , 动力学机制 , 激活能