金属学报(英文版)
The amorphous Fe_(90-x)V_xZr_(10) alloy after electolytic hydrogenation procedure was studied by means of Mossbauer effect,magnetic measurement.X-ray diffaction and secondary ion mass spectroscopy(SIMS)techniques.The experimental results show that the magnetic properties of amorphous Fe_(90-x)V_xZr_(10) alloy are highly sensitive to the presence of hydrogen. The isomer shift(IS)has a small positive change and the magnetic properties transfer from paramagnetic to ferromagnetic State by hydrogenation,and the effect of hydrogen absorption is to raise Fe magnetic moment(from the increase of saturation maguetization)and Curie temperature T_c from 257 to 384 K.Finally.the considerable increase of magnetic properttes of amorphous Fe_(90-x)V_xZr_(10) alloy by hydrogenation is attributable to the change of hybridization effect between outer electrons of Zr atoms and 3d electrons of Fe atoms.From the results of SIMS experiment,it is concluded that the hydrogen atoms is localized around Zr atoms wheh hydrogen atoms enter into the allor.
关键词:
amorphous alloy
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,