金属学报(英文版)
The growth of thermoelastic martensite in a Cu-29% Zn-3% Al alloy has been investigated experimentally and theoretically.Metallographie observations showed that the growth oc- cured thermoelastically,i.e.reversibly,in the radial direction as well as in the thickening di- rection.This is not consistent with the theories of Conhen and some others.A model has been suggested to explain the thermoelasticity of the growth.The basic idea is:the elastic strain distribution is highly heterogeneous and the growth is controlled by the local elastic strain en- ergy at the growth frontier area.The calculated results from the model based on Eshelby's theory are consistent with the observations.
关键词:
thermoelasticity
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,