D.F. Wu
,
S.S. Cheng
金属学报(英文版)
Turbulent flow and heat transfer coupled with solidification in slab continuous casting mold was studied by numerical simulation method. Volume of fluid (VOF) model is used to solve steel-air two-phase flow problem and enthalpy-porosity scheme is introduced to solve the fluid flow problem involving solidification. Contributions of various nozzle port angles and port widths and heights on the free surface fluctuation and the thickness of solidifying shell in slab mold were particularly investigated, based on which the structure of submerged entry nozzle was optimized. Flow inside the common nozzle port cannot fill the entire outlet area, having a recirculation in the upper portion of the port, which is enlarged for the nozzle port with both larger height and width. Results show that the flow in mold cavity is mainly controlled by the nozzle port angle. The increase of the angle of upper face of the port to shape a roughly streamlined inner-wall improves the effective area fraction of the nozzle, resulting in less jet impingement, weaker free surface turbulence and thicker solidifying steel shell.
关键词:
continuous casting
,
null
,
null
,
null
赵梅
,
宗斌
,
王二平
,
王波
,
栗卓新
物理测试
在金属布氏硬度试验国家标准第一部分：试验方法中，有关选择压头球直径(D)和试验力压头球直径平方的比率（0.102 F/D2）的说明如下：试样厚度至少应为压痕深度的8倍； 0.102 F/D2应根据材料硬度值来选择；试验力的选择应保证压痕直径(d)在0.24<d/D<0.6之间；当试样尺寸允许时，应优先选用直径为10 mm的球压头进行试验。文章根据上述规定，通过实验分析，探讨了一种在实际测试时选择0.102 F/D2值及压头球直径D的具体方法。
关键词:
金属布氏硬度试验
,
national standard
,
a selection method.
赵梅
,
宗斌
,
王二平
,
王波
,
栗卓新
物理测试
doi:10.3969/j.issn.1001-0777.2007.02.015
在金属布氏硬度试验国家标准第一部分:试验方法中,有关选择压头球直径(D)和试验力-压头球直径平方的比率(0.102 F/D2)的说明如下:试样厚度至少应为压痕深度的8倍;0.102 F/D2应根据材料硬度值来选择;试验力的选择应保证压痕直径(d)在0.24＜d/D＜0.6之间;当试样尺寸允许时,应优先选用直径为10 mm的球压头进行试验.文章根据上述规定,通过实验分析,探讨了一种在实际测试时选择0.102 F/D2值及压头球直径D的具体方法.
关键词:
金属布氏硬度试验
,
国家标准
,
选择方法
郭艳青
,
任中洲
原子核物理评论
在单粒子势模型的框架下,计算了O同位素和F同位素的基态和某些低激发态的能级值、均方根半径值及密度分布.通过在伍兹-萨克逊势中引入同位旋依赖项,研究了同位旋效应对F同位素s-d能级间隙的影响.理论计算得到的均方根半径值和自旋宇称值与实验结果一致.尤其是,理论计算能够实现16F,15F和14F中2s1/2与1d5/2质子能级间的反转,且F同位素中s-d质子能级间隙及其整体变化趋势与已知实验结果符合较好.此外,理论结果表明12F的(1/2)+第一激发态为单质子晕态.
关键词:
同位旋效应
,
能级反转
,
质子晕
李铂
,
周建江
,
夏伟杰
,
吴连慧
液晶与显示
doi:10.3788/YJYXS20142904.0605
直线是机载座舱显示画面中最基本的图元,其显示质量对于整个画面的显示效果影响较大,尤其是小角度下直线显示的“麻花”现象一直是影响显示效果的关键问题之一.为了提高小角度下直线的显示效果,本文提出了一种基于Wu算法的亮度渐变改进算法.该算法通过渐进地展现直线从轴方向上的亮度变化过程,减少亮度畸变,有效地改进了显示效果.通过Matlab仿真和FPGA实现,验证了该算法反走样后的小角度直线显示效果明显优于其他算法,而且结合中点画线法后,绘制时间与Wu算法相当.同时该算法还可改善大角度直线和圆弧的显示效果,消除了大角度直线的边缘锯齿,解决了圆弧在小角度部分的虚化问题.因此本文算法可用于对实时性和显示效果要求高的机载座舱显示系统,以缓解飞行员的视觉疲劳.
关键词:
座舱显示
,
反走样
,
改进Wu算法
,
小角度
,
FPGA实现
初本莉
,
刘行仁
,
王晓君
,
蒋雪茵
功能材料
高温下合成了掺Pr3+的CaSiO3,研究了Pr3+在室温下的发射光谱和激发光谱,观测到Pr3+的4f5d态的两个能级,其最低能级向4f2组态的3H4,3H6和1G4发生辐射跃迁,其中以向3H4的跃迁最强,而向3P0和1D2的无辐射跃迁几率可以忽略,从而得到了一种在短波紫外发光效率很高的新型材料.
关键词:
Pr3+离子
,
偏硅酸钙
,
4f5d态
,
UV辐射跃迁
,
荧光光谱
汪海清
,
王义
材料导报
采用先驱体浸渍裂解工艺制备了2.5D-SiO2f/(SiO2+硅树脂)透波材料,并对其力学性能、耐环境性能和耐大功率微波辐照性能进行了研究.结果表明,环境试验前后,2.5D-SiO2f/(SiO2+硅树脂)透波材料的力学性能和介电性能变化均较小.采用功率密度为60 W/cm2的微波考核1h后,透波材料表面无变化,表面温升仅为82℃.
关键词:
2.5D-SiO2f/(SiO2+硅树脂)
,
透波材料
,
弯曲强度
,
介电性能
刘静宇
,
陈朝辉
,
简科
,
方志薇
,
彭霞辉
稀有金属材料与工程
以三维碳纤维织物和廉价的硅树脂为原料,采用先驱体转化工艺制备3D C_f/Si-O-C材料,考察了硅树脂浓度对材料微观结构与力学性能的影响.结果表明:随着硅树脂浓度的增加,3D C_f/Si-O-C材料的密度增加,孔隙率下降,材料的弯曲强度增加,当硅树脂浓度达到54.5%时,材料的弯曲强度达到360.6 MPa;而随着硅树脂浓度的进一步增加,材料的密度虽然进一步增加,但弯曲强度和断裂韧性却明显下降,这主要是由于硅树脂浓度过高时,所制备的材料基体与纤维结合较紧,界面结合较差的原因造成的.
关键词:
先驱体转化法
,
硅树脂
,
3D
,
C_f/Si-O-C材料
,
力学性能
,
微观结构
刘海韬
,
程海峰
,
王军
,
唐耿平
,
周旺
,
郑文伟
稀有金属材料与工程
对PIP法制备2D-SiC_f/SiC复合材料成形浆料中惰性填料SiC含量对2D-SiC_f/SiC复合材料孔隙率、纤维体积分数以及力学性能影响进行研究.研究表明,SiC微粉含量较低时,浆料粘度过低,导致层间存在较大气孔,纤维体积分数不高,致使复合材料力学性能不佳,当SiC微粉含量过高时,浆料粘度过大,层间基体厚度增加,纤维体积分数下降,并且浸渍效率降低,孔隙率增大,复合材料力学性能下降.当SiC微粉含量为33.3%时,复合材料具有较低的孔隙率和较高的纤维体积分数,复合材料具有较好的力学性能,弯曲强度和断裂韧性分别达到211.7 MPa和8.56 MPa·m~(1/2).
关键词:
PIP工艺
,
SiC微粉
,
2D-SiC_f/SiC
,
力学性能
Philosophical Magazine
The error of Equation (15b) in my article [Z.D. Zhang, Phil. Mag. 87 (2007) p.5309] in the application of the Jordan-Wigner transformation does not affect the validity of the putative exact solution, since the solution is not derived directly from that equation. Other objections of Perk's comment [J.H.H. Perk, Phil. Mag. 89 (2009) p.761] are the same as those in Wu et al.'s comments [F.Y. Wu et al., Phil. Mag. 88 (2008) p.3093; p.3103], which do not stand on solid ground and which I have sought to refute in my previous response [Z.D. Zhang, Phil. Mag. 88 (2008) p.3097]. The conjectured solution can be utilized to understand critical phenomena in various systems, whereas the conjectures are open to rigorous proof.
关键词:
3D Ising model;exact solution;conjecture;critical phenomena;ferromagnetism;magnetic phase transition;model;analyticity