The perpendicular anisotopy,coercivity and Kerr rotation angle of the amorphous Tb_(32)Fe_(54)Co_(14) films were studied.The X-ray,electron diffraction,XPS and AES profile con- firmed that no obvious change in their amorphous structure and oxygen concentration is ob- served after annealing at 100℃,while their properties alter evidently under bending stress.It seems to be believed that the perpendicular anisotropy in the Tb_(32)Fe_(54)Co_(14) films mainly arises from the induced stress during preparation and the magnetostriction coupling stress,as well as,the thermal instability of the film relates closely to the stress relaxation during annealing.
关键词:
amorphous TbFeCo film
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null