THERMAL STABILITY AND PERPENDICULAR ANISOTROPY OF AMORPHOUS TbFeCo FILMS

L(?) Jian WANG Yinjun Institute of Physics , Academia Sinica , Beijing , ChinaMA Ruzhang University of Science and Technology Beijing , Beijing , China LU Jian Dept.No.2 , Institute of Metallurgy , Shoudu Iron and Steel Company , Beijing 100085 , China

金属学报(英文版)

The perpendicular anisotopy,coercivity and Kerr rotation angle of the amorphous Tb_(32)Fe_(54)Co_(14) films were studied.The X-ray,electron diffraction,XPS and AES profile con- firmed that no obvious change in their amorphous structure and oxygen concentration is ob- served after annealing at 100℃,while their properties alter evidently under bending stress.It seems to be believed that the perpendicular anisotropy in the Tb_(32)Fe_(54)Co_(14) films mainly arises from the induced stress during preparation and the magnetostriction coupling stress,as well as,the thermal instability of the film relates closely to the stress relaxation during annealing.

关键词: amorphous TbFeCo film , null , null

Effects of Phase Composition on Microstructure and Mechanical Properties of Lu₂O₃-doped Porous Silicon Nitride Ceramics

Quan Li

材料科学技术（英文）

Porous silicon nitride ceramics (Si₃N₄) were fabricated by pressureless sintering using different particle size of silicon nitride powder. Lu₂O₃ was used as sintering additive. According to phase relationships in the ternary system Si₃N₄-SiO₂-Lu₂O₃, porous Si₃N₄ ceramics with different phase composition were designed through the change of the content of SiO₂ which was formed by the oxidation at 800°C in air. Porous Si₃N₄ with different phase compositions was obtained after sintering at 1800°C in N₂atmosphere. A small content of SiO₂ favored the formation of secondary phase Lu₄Si₂O₇N₂, while large content of SiO₂ favored the formation of secondary phase Lu₂Si₂O₇ and Si₂N₂O. Porous Si3N4 ceramics with secondary phase Lu₄Si₂O₇N₂ had a flexural strength of 207 MPa, while that with secondary phase Si₂N₂O and Lu₂Si₂O₇ had lower flexural strength.

关键词: Porous silicon nitride ceramics

Fabrication of Porous Si₃N₄-Lu₂Si₂O₇ Composite Ceramics

Pengfei Zhang Litong Zhang Xiaowei Yin

材料科学技术（英文）

To improve the corrosion resistance of porous Si₃N₄ used in the high temperature environments, which contain water vapor and volatile species, porous Si₃N₄-Lu2Si₂O₇composite ceramics were fabricated by a process of oxidation bonding and pressureless sintering in flowing N₂atmosphere at the temperatures lower than 1550°C. The pores in ceramics were formed by removing the pore-forming agent (phenolic resin). SiO₂ derived by the oxidation of Si₃N₄ at 1250°C in air reacted with Lu₂O₃ at various sintering temperatures, leading to the formation of Lu₂Si₂O₇ with excellent oxidation and corrosion resistance. The phase composition, microstructure, and mechanical properties of the porous ceramics depended on the sintering temperatures. Si₃N₄-Lu2Si₂O₇ composite ceramics with the porosity of 52% and the pore size of 0.2μm were obtained by oxidation bonding at 1250°C for 1 h and pressureless sintering at 1550°C for 2 h using 4 wt pct Lu₂O₃ additive.

关键词: Porous ceramics , 氮化硅 , 焦硅酸镥 , 无压烧结

TEMPERATURE-DEPENDENCE OF THE MAGNETIC-PROPERTIES OF THE RARE-EARTH TRANSITION-METAL INTERMETALLIC LU2FE14C

Journal of Magnetism and Magnetic Materials

Magnetization curves of the ternary tetragonal compound Lu2Fe14C were measured in an extracting-sample magnetometer in the temperature range from 1.5 to 300 K. The temperature dependence of the magnetic properties of Lu2Fe14C is discussed.

关键词: anisotropy

Lu2O3和Lu2O3∶Eu3+单分散球形粉体合成及其荧光性能研究

马畅 , 李晓东 , 董宇 , 刘绍宏 , 朱琦 , 李继光 , 霍地 , 孙旭东

中国稀土学报 doi:10.11785/S1000-4343.20130411

以Lu(NO3)3和尿素为原料,采用均相沉淀法合成镥盐前驱体,研究Lu3+浓度、尿素/Lu3+摩尔比R对前驱体形貌的影响.结果表明,在反应温度为95℃时,低Lu3+浓度有利于单分散球形粉体的合成,并且适当的调整R值可将单分散球形颗粒尺寸控制在180 ～ 270 nm之间.在此基础之上,研究Eu3+掺杂Lu2O3单分散球形荧光粉体的合成,探讨了Eu3+的掺杂量(1％,3％,5％,7％,9％(原子分数))及煅烧温度(600～ 1200℃)对颗粒形貌及其荧光性能的影响.结果表明,Eu3+的掺杂使所得(Lu,Eu)盐前驱体颗粒尺寸远小于单纯的Lu盐前驱体,且Eu含量对荧光粉的荧光强度有着显著的影响,荧光淬灭浓度为5％.在考察的煅烧温度范围内,荧光粉的荧光强度随煅烧温度的提升而增强.

关键词: Lu2O3 , Eu3+ , 均相沉淀 , 单分散球形 , 前驱体 , 荧光性能 , 稀土

溶剂热法制备不同形貌纳米Lu2O3粉体

邱华军 , 施鹰 , 谢建军 , 谢杰

人工晶体学报

本文以水、丙酮、乙醇、乙二醇为溶剂,采用溶剂热法制备了不同形貌的纳米氧化镥(Lu2O3粉)粉体前驱体,将前驱体在400～800 ℃条件下煅烧2 h制得了不同形貌的Eu3+:Lu2O3粉体.研究发现,所用溶剂的物理性质对产生特定形貌的样品具有重要的影响,以水和丙酮为溶剂,可制得具有较高长径比的Lu2O3纳米棒,而当溶剂为乙醇和乙二醇时,所得Lu2O3粉体为等轴状的纳米颗粒.

关键词: 溶剂热法 , 氧化镥 , 纳米粉体 , 形貌

Lu2O3对球形Ni(OH)2高温充放电性能的影响

任俊霞 , 王小建 , 李宇展 , 高学平 , 阎杰

中国稀土学报

为了改善镍电极的高温充电效率,采用机械混合的方式将球形Ni(OH)2与不同比例的Lu2O3混合后制成粘结式镍正极.充放电测试、循环伏安和XRD等实验结果表明,掺杂Lu2O3后镍电极的析氧过电位明显提高,高温充电效率得到了很大改善,在充电后的电极中β-NiOOH生成; 而且Lu2O3的掺杂比例对镍电极的高温性能在不同的充放电倍率下有不同程度的影响,3.5%是最好的掺杂比例,掺杂对高温小电流充电效率的改善作用要大于高温大电流充电.

关键词: 球形Ni(OH)2 , 高温性能 , Lu2O3 , 析氧过电位 , 稀土

稀土Lu2O3对氮化硅陶瓷性能的影响

仝建峰 , 李宝伟 , 王岭 , 陈大明

材料工程 doi:10.3969/j.issn.1001-4381.2010.z1.001

以稀土氧化物Lu2O3作为单一添加剂,研究了稀土氧化物的添加量对氮化硅在相变过程密度、力学性能的影响规律.指出了氮化硅粉体的α→β相变率与稀土氧化物的添加量、粉体的热处理温度之间的关系.研究表明:加入Lu2O3添加剂后,β-Si3N4相的比率随着温度的升高呈明显上升趋势,当热处理温度达到1750℃时,β-Si3N4相的比率几乎接近或达到100％.随着Lu2O3含量的增加,在烧结过程中所形成的液相量随之增多,相对密度随之提高.随Lu2O3添加量的增加,试样的抗弯强度也增大,在10％时达到峰值,抗弯强度为1259.90MPa;氮化硅陶瓷的硬度随Lu2O3添加量的变化规律与抗弯强度的变化规律相似.Lu2O3含量在10％时,试样的断裂韧性值达到最大,为6.277MPa·m1/2.

关键词: 氮化硅 , 氧化镥

Tb∶Lu2SiO5光学薄膜的结构演变和发光性能

孙智 , 谢建军 , 王宇 , 施鹰 , 雷芳

人工晶体学报

采用溶胶-凝胶法结合旋涂工艺在单晶硅(111)上制备了Tb3+离子不同掺杂浓度的硅酸镥光学薄膜(Tb∶Lu2SiO5),利用热重差热分析(TG-DSC)、X射线衍射(XRD)、傅里叶红外光谱仪(FTIR)、原子力显微镜(AFM)和紫外可见荧光光谱(PL)对Tb∶Lu2SiO5薄膜的不同温度热处理的结构演变和发光性能进行了表征.研究结果表明Tb∶Lu2SiO5光学薄膜表面均匀、平整、无裂纹,薄膜样品从800℃开始晶华,1100 ℃时晶化完全.Tb∶Lu2SiO5的发光性能表现为Tb3+离子的4f→5d和5D4(5D3)→7FJ(J =6,5,4,3)跃迁结果(监测波长分别为480～650 nm和350～470 nm),激发主峰位于～240 nm,发射光谱主峰为542 nm的绿光发射.研究表明Tb3掺杂浓度对Tb∶Lu2SiO5光学薄膜的发光强度会产生明显影响,掺杂15mol％的Tb3+时,Tb∶Lu2SiO5薄膜的发光强度最强.

关键词: Sol-gel法 , Tb∶Lu2SiO5光学薄膜 , 结构演变 , 发光性能