The effects of adjusting technological conditions on the phosphorous enrichment of adjusted converter slag were investigated. The results showed that the phosphorus could be effectively enriched to 2CaO·SiO2 and 2CaO·SiO2-3CaO·P2O5 solid solution (SS, namely phosphorus-rich phase) to be formed with the decreasing of basicity and cooling rate. Moreover, the morphology of the phosphorus-rich phase changed from granular for the original converter slag with higher basicity to the coexistence of granular shape and rod-like for the adjusted slag with lower basicity. P2O5 content in phosphorus-rich phase exceeded 30% while the basicity was 13 at the cooling rate of 10 ℃/min.
关键词:
phosphorous enrichment
,
adjusting technological condition
,
adjusted converter slag
,
phosphorus-rich phase
WANG Nan
,
LIANG Zhi-gang
,
CHEN Min
,
ZOU Zong-shu
钢铁研究学报(英文版)
The enrichment behavior of phosphorus in CaO-SiO2-FeOx-P2O5 slag was studied by making an investigation on the distribution of phosphorous content in the CaO-SiO2-FeOx-P2O5 molten slag. The research results showed that the 2CaO·SiO2 solid particles existing in molten slag were the condensation sites for the phosphorus enrichment. The enrichment process of phosphorus in the molten slag can be recognized as three substeps: mass transfer of phosphorus from bulk slag to the surface of 2CaO·SiO2 particle, superficial solid solution reaction of phosphorus around the 2CaO·SiO2 particle, and diffusion of phosphorus through the product layer of 2CaO·SiO2-3CaO·P2O5 solid solution to the inner of 2CaO·SiO2 particle. Moreover, higher temperature is favorable to the phosphorous enrichment from molten bulk slag to the 2CaO·SiO2 particles.
关键词:
enrichment behavior
,
phosphorus
,
2CaO·SiO2 particle
,
mass transfer
李开明
,
李亚洲
,
冯维贵
,
林长
量子电子学报
doi:10.3969/j.issn.1007-5461.2007.05.014
采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.
关键词:
混沌
,
Chen系统
,
不动点
,
Lyapunov指数
,
反馈控制
Q.S. Liu1
,
2
,
3)
,
L.C. Zhao3)
,
G.X. Dong2) and N.J. Gu1) 1) Heibei University of Technology
,
Tianjin 300130
,
China 2) Tianjin Institute of Technology
,
Tianjin 300191
,
China 3) Harbin University of Technology
,
Harbin 150001
,
China
金属学报(英文版)
Theconstruction changinginthereversetransformation ofthestress induced εMin Fe 17 Mn 10 Cr 5 Si 4 Ni alloy is carefully inspected in transmission electron microscope, and then stress induced εM procedure of reverse transformation is analyzed. The behavior of reverse transformationisdissimilar when the organization of εMis different. The reversetransfor mation ofεM withtheshapeofsingle plateandstripisrelativelyeasy,anditsreversibilityincrystallographiciseasilytocarryout,fortheεM with multilayerstructure,thereversetrans formationtakes placein isolatedlayers, fortheεMthat grows well,thereversetransforma tion isrelatively difficult becauseofthe ductile harmonization between itsinternalorganiza tion structures.
关键词:
stress induced εM
,
null
,
null
徐佩
,
卢旭鑫
,
汪传斌
,
杨善中
,
孙晓红
,
丁运生
高分子材料科学与工程
为改善多壁碳纳米管(MWNT)在低密度聚乙烯(LDPE)中的分散性及复合材料的界面特性,采用溴化-1-十六烷基-3-甲基咪唑基离子液体([C16min]Br)对MWNT进行表面改性,并用Raman光谱对改性效果进行了表征.将经过修饰的碳纳米管(MIL)与LDPE熔融共混得到MIL/LDPE复合材料,采用场发射扫描电子显微镜(FESEM)和阻抗分析仪(LCR)对复合材料的结构与介电性能进行了分析.结果表明,相比与MWNT/LDPE(渗流阈值为5.2％,介电常数为82,介电损耗为0.93),MIL/LDPE(渗流阈值为9.1％,介电常数为169,介电损耗为0.51)介电常数增大,介电损耗降低.并且在低温时,MIL/LDPE介电常数随温度的变化甚小,显示出良好的温度-介电常数特性.
关键词:
咪唑基离子液体
,
碳纳米管
,
低密度聚乙烯
,
介电性能
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
金属学报
Volu扣ne 27SeriesB1991AUTHOR INDEX CCAO Guanghan(曹光旱)············……6一B科6CAo weijie(曹卫恋)..················……5一B32oCAO Yilin(曹益林)··················……6一B443CHANG Xin(常听)···············……1一B48CHE Guang邻n(车广灿)·············一6一B科0CHEN Erbao(陈二保)···············……6一B410CHEN Jia....
关键词:
高诚
,
胥蕊娜
,
陈黎
,
姜培学
工程热物理学报
格子Boltzmann方法(LBM)在计算复杂结构物理模型时具有独特优势并在模拟两相流动过程中能够高效清晰捕捉相界面.本文介绍了基于Shan-Chen多相模型的格子Boltzmann方法的理论成果以及基于二氧化碳封存的超临界两相流的模拟研究.结果表明,Shan-Chen模型在模拟两相流时符合Laplace定律,且两相层流时的速度分布和相渗曲线均与理论值吻合.二氧化碳封存过程中,较大的注入速率在提高二氧化碳残余俘获量的同时会降低其化学俘获量.
关键词:
二氧化碳封存
,
超临界两相流
,
Shan-Chen模型