Bo Chen Yingche Ma Ming Gao Kui Liu
材料科学技术（英文）
Experimental studies on the melting process of titanium aluminum alloy have been pursued from the viewpoint of contamination. TiAl alloys were prepared with vacuum induction melting (VIM) in calcia crucibles at 1873 K and 1923 K in order to determine the behavior of the oxygen content as a function of temperature, time and frequency of power. The experiment results showed that alloys were uncontaminated except for the increasing of oxygen content which was introduced from the reaction CaO(s)=Ca(in TiAl)+O(in TiAl), and the standard Gibbs energy of the reaction was determined to be ?G0=274000−102.8T (J/mol). Oxygen content increased slowly with the melting time by about 50×10-6 wt pct/min, and decreased with induction melting frequency. Lower superheat and higher melting frequency can be used to reduce oxygen content increasing rate.
关键词:
TiAl alloys
,
induction melting
,
calcia crucible
,
oxygen content.
Journal of Alloys and Compounds
A solid solution with formula (Y1-xTbx)(3)GaO6 (x = 0-0.5) was prepared by solid-state reaction method. Powder X-ray diffraction (XRD) shows that Y3GaO6 is isostructural to Gd3GaO6 (Cmc2(1)), and the lattice parameters are a = 8.8364(1) angstrom, b = 11.0899(1) angstrom and c = 5.3937(1) angstrom. Atomic parameters were derived by Rietveld refinement of the XRD pattern. Photoluminescence (PL) spectra show a strong green emission of 543 nm from the D-5(4) -> F-7(5) transition of Th3+ at room and liquid nitrogen temperature. There is a wide saturation range of the PL intensity for the Th3+ content from x = 0.04-0.20, and a long life time about 1200 mu s for the green 543 nm emission at room temperature. (c) 2006 Elsevier B.V. All rights reserved.
关键词:
Y3GaO6;crystal structure;Tb3+ doped;photoluminescence;luminescence properties;dependence;y3al5o12;phosphor;ions;ce3+;tb-3;uv
李开明
,
李亚洲
,
冯维贵
,
林长
量子电子学报
doi:10.3969/j.issn.1007-5461.2007.05.014
采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.
关键词:
混沌
,
Chen系统
,
不动点
,
Lyapunov指数
,
反馈控制
Journal of Solid State Chemistry
The crystal structures of a series of compounds with the composition Ln(3)GaO(6)(Ln = Nd, Sm, Eu, Gd, Tb, Dy, Ho and Er) synthesized by solid-state reaction at 1400degreesC are investigated. X-ray diffraction shows that Ln3GaO6 has a non-centro symmetric orthorhombic structure (space group Cmc2(1)). Lattice parameters a, b, c and cell volume and the average distances between Ln(l)-O, Ln(2)-O of these compounds decrease with the decreasing of the radii of trivalent Ln ions, which accord with the expected lanthanide contraction behavior. There are two sites of seven-fold coordination for Ln atoms with oxygens, and Ga atoms are in oxygen tetrahedra which are distorted and elongated along the a-axis. Magnetization measurements indicate that the susceptibility X changes with temperature in Curie-type manner. (C) 2004 Elsevier Inc. All rights reserved.
关键词:
Ln(3)GaO(6);crystal structure;Rietveld refinement;X-ray diffraction;garnets
Journal of Luminescence
Ln(3+) (Ln = Nd, Sm, Eu, Gd, Dy, Ho, Er)-doped Y3GaO6 compounds were prepared by solid-state reaction, and their optical spectra such as absorption, photoluminescence, excitation and time-resolved spectra have been measured for Ln Nd, Sm, Dy, Ho, Er. X-ray powder diffraction shows that the lattice parameters of the compounds (Y(0.96)Ln(0.04))(3)GaO6 decrease with the decrease of the radii of trivalent Ln(3+) ions, indicating that Ln(3+) ions have substituted for y(3+) ions in the lattice. Optical spectra show that there are obvious absorptions at ultraviolet to visible region. The strong emissions in visible and infra-red region show that Y3GaO6 is a suitable host for rare-earth-doped laser crystal and phosphor materials. (C) 2004 Elsevier B.V. All rights reserved.
关键词:
crystal-field;absorption-spectra;luminescence;y3ga5o12;glasses;garnet;y2o3;ions;laf3;tb3
Journal of Solid State Chemistry
A serial of samples in Y2O3-Ga2O3-Tm2O3 pseudo-ternary system are prepared by solid-state chemical reaction method. The range of solid solution in (Y1-xTmx)(3)GaO6 is 0 < x < 0.384. Powder X-ray diffraction shows that the compounds crystallize in Gd3GaO6 (Cmc2(1))-type structure. The solid solubilities of Y3+xGa5-xO12 (x = 0-0.77) and Tm3+xGa5-xO12 (x = 0-0.62) are 37.5-47.11 at% Y2O3, and 37.5-45.26 at% Tm2O3, respectively. PL spectra of Tm-doped Y3GaO6 show that there is a sharp blue emission at similar to 456 nm from the D-1(2) -> F-3(4) transition at room temperatures with two lifetimes (similar to 5 and similar to 15 mu s) and a narrow saturation range of PL intensity for the Tm3+ content from x = 0.005 to 0.03. The sharp emission and long lifetime of (Y1-xTmx)(3)GaO6 indicate that Y3GaO6 is a potential phosphor and laser crystal host material. (c) 2005 Elsevier Inc. All rights reserved.
关键词:
Tm3+ -doped Y3GaO6;Y2O3-Ga2O3-Tm2O3 system;(Y1-xTmx)(3)Ga5O12 solid;solution;luminescence;crystal-structure;luminescence;phosphor;cations;ions;tb3
张兰河
,
李德生
,
王旭明
,
张海丰
硅酸盐通报
为了提高生物除磷效率,研究采用AOA-SBR工艺进行了长期连续除磷实验,考察不同温度下碳源(乙酸钠、丙酸钠、葡萄糖)对PAO与GAO竞争的影响.结果表明:当温度由10℃升高至25℃时,利用丙酸钠作为碳源时,污泥含磷量与含糖量分别从7.2％和5.1％升高至7.9％和6.3％,PHA转化量升高了23.1 mg/L,厌氧释磷量从105.9 mg/L升高至149.9 mg/L,VSS/MLSS由71％降低至65％;利用乙酸钠作为碳源时,污泥含磷量与含糖量分别从6.9％和5.3％升高至7.6％和6.7％,PHA转化量升高了23.9 mg/L,厌氧释磷量从73.8 mg/L升高至108.8 mg/L,VSS/MLSS由73％降低至71％;利用葡萄糖作为碳源时,污泥含磷量与含糖量分别从5.8％和6.3％升高至6.6％和8.8％,PHA转化量升高了33.2 mg/L,厌氧释磷量从37.4 mg/L升高至43.2 mg/L,VSS/MLSS由80％升高至88％.当温度升高至30℃时,3个反应器均出现厌氧末期PHA浓度下降和糖原浓度升高,厌氧释磷量减少,污泥含磷量均下降,污泥含糖量上升,VSS/MLSS均很高.与葡萄糖相比,采用乙酸钠和丙酸钠作为碳源,有利于PAO生长繁殖,PAO为优势菌种,抑制GAO增殖.同时,低温更有利于PAO的生长繁殖.
关键词:
温度
,
碳源
,
SBR
,
PAO与GAO
刘国栋
,
张利英
,
王艳丽
,
郭丹
,
程翠然
高分子材料科学与工程
采用前期提出的共聚物Tg-组成关系方程研究了MA-EA、MA-n-BA二元共聚物的Tg,新方程中的周期共聚物Tg通过最小二乘法由无规共聚物Tg数据求取,相关周期共聚物的Tg为:Tg[ME]=274.6K、Tg[MB]=246.3K、Tg[MME]=286.3K、Tg[MMB]=262.8K、Tg[EEM]=262.3K、Tg(BBM]=236.7K,由此计算得到的理论值与实验值偏差极小,说明新方程能够更好地解释丙烯酸甲酯二元共聚物Tg与其组成及序列结构之间的关系.进一步预测了不同取代基时有序取代密度对聚丙烯酸甲酯Tg的影响规律,发现与对聚甲基丙烯酸甲酯Tg的影响规律不同,取代基的影响在高取代密度时才能显现.
关键词:
二元共聚物
,
玻璃化温度
,
组成
,
取代基
罗军
,
钟真武
,
范世(马豈)
,
王锦昌
人工晶体学报
doi:10.3969/j.issn.1000-985X.2000.01.005
本文首次报道了Ca4YO(BO3)3(YCOB)晶体的坩埚下降法生长.在1600～1650℃炉温下,固液界面处的纵向温度梯度为40～60℃/cm,以0.2～0.6mm/h的生长速率,在近封闭的Pt坩埚中生长出了直径达25mm、长度超过50mm的完整透明YCOB晶体.介绍了生长工艺和原料制备,观察发现晶体中的主要宏观缺陷是包裹体.分析了包裹体生成的原因.
关键词:
布里奇曼法
,
Ca4YO(BO3)3晶体
,
非线性光学材料
,
包裹体
Physica B-Condensed Matter
Nanocapsules consisting of B2O3/H3BO3 encapsulating Fe-Gd cores have been synthesized by an arc-discharge process using metal-boron alloys as cathode. Most of the nanocapsules have a well-constructed shell/core structure with a uniform B2O3/H3BO3 shell. Heat-treatment induces reactions between the shell and the core, resulting in the formation of a Fe3BO5+GdBO3 matrix embedded with Fe nanoparticles, reduction of the metallic-core size and decrease of the blocking temperature T-B. Above T-B, the magnetization curves plotted vs. H/T overlap and show zero coercivity. Below T-B, the coercivity shows a linear dependence when plotted vs. T-1/2. However, the coercivity-T-1/2 curve below 60 K has a different slope from that above 60 K, indicating the existence of two different magnetic phases in the nanocapsules. Different from bulk Fe3BO5, nanoscale Fe3BO5 particles have a lower transition temperature to the weak-ferromagnetic state. and magnetic hysteresis is absent due to size effects. (C) 2004 Elsevier B.V. All rights reserved.
关键词:
nanocapsules;transmission electron microscopy (TEM);X-ray;photoelectron spectroscopy (XPS);magnetic properties;arc-discharge;boric-acid;boron;carbon;oxide;nanoparticles;particles;diborane;iron