W.M. Mao
,
Z.S. Zhen
,
H.T. Chen
,
X.Y. Zhong
金属学报(英文版)
With the help of an electromagnetic stirring device and alloy melt quenching technology, the microstructure of semi-solid AZ91D magnesium alloy slurry stirred by a rotationally electromagnetic field was studied and the experimental results are shown as the following. The primary α-Mg grains are refined obviously when the slurry is stirred by a rotational electromagnetic field during continuously cooling and they are eventually changed to fine rosette grains or spherical grains. If the above semi-solid slurry is further stirred isothermally for some time, much more spherical primary α-Mg grains can be obtained. If the melt is first cooled down to a given semi-solid temperature and then starts being stirred by the rotational electromagnetic field, the primary α-Mg dendrites will be large, and a longer time will be taken and a larger stirring power will be needed for the secondary arms of the dendrites to be remelted on the roots to prepare an ideal semi-solid slurry. Theoretical analysis indicates that the strong flow motion leads to a more even temperature field and a solute field and stronger man-made temperature fluctuation in the AZ91D magnesium alloy melt so that the spherical primary α-Mg grains are increased in the slurry. Moreover, all the measures promoting the temperature fluctuation will be favorable to the formation of spherical primary α-Mg grains and all the factors increasing the arm's root remelting difficulty will be favorable to the formation of rosette-type primary α-Mg grains.
关键词:
AZ91D magnesium alloy
,
null
,
null
窦强
,
王斌
高分子材料科学与工程
研究了β晶型成核剂(酰胺化合物)成核改性纤维级聚丙烯Z30S的力学性能,进行了广角X射线衍射和DSC分析.发现成核改性后生成了β晶型聚丙烯,因而聚丙烯Z30S的冲击性能提高.通过纺丝-拉伸实验和对纤维进行广角X射线衍射分析、SEM观察,发现成核改性纤维在纺丝拉伸过程中发生了晶型转变,产生大量微孔隙.
关键词:
聚丙烯
,
β晶型
,
成核剂
,
纤维
程俊梅
,
张萍
,
于广水
,
赵树高
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2009.06.016
在比表面积相近的情况下,探讨白炭黑(Z125)及碳黑(N234)对天然橡胶(NR)和溶聚丁苯橡胶(S-SBR)硫化胶的抗割口增长能力及动态力学性能的影响.结果表明,Z125和N234对NR和S-SBR两种硫化胶的增强效果相差不大;NR硫化胶的抗割口增长能力明显好于S-SBR硫化胶;NR中填充Z125的抗割口增长能力好于N234且随疲劳次数的增加Z125的优势更加明显,而S-SBR中填充N234的抗割口增长能力好于Z125且两者的抗割口增长速率基本不随疲劳次数的增加而改变;Z125使NR和S-SBR硫化胶在0℃和70℃下的tanδ值分别低于N234增强相应硫化胶.
关键词:
NR
,
S-SBR
,
白炭黑
,
炭黑
,
动态力学性能
,
抗割口增长能力
唐波
,
朱丽慧
机械工程材料
利用RD-2型高温持久试验机、高分辨透射电子显微镜和能谱仪研究了国产S30432耐热钢在供货态及不同温度、应力条件下持久断裂后的第二相,尤其是Z相的析出行为及影响因素.结果表明:供货态S30432钢中只存在MX相;在650℃、170 MPa、10 712 h持久条件下析出了M23 C6碳化物和富铜相;在700℃、150MPa、937 h条件下,不仅析出了M23 C6碳化物和富铜相,还出现了Z相及包含MX相和Z相的颗粒;在700℃、150 MPa、1 944 h条件下Z相粗化缓慢,在700℃、100MPa、11 832 h条件下Z相粗化明显;高温和应力均会加速Z相的析出.
关键词:
耐热钢
,
Z相
,
显微组织
陈立志
,
张亚军
材料开发与应用
doi:10.3969/j.issn.1003-1545.2011.05.010
分别采用三点弯曲SE(B)与紧凑拉伸C(T)试样,通过-20℃的低温裂纹尖端张开位移CTOD断裂韧性试验及疲劳裂纹扩展速率da/dN试验,研究了S355N及S355N-Z25结构钢的裂纹启裂与扩展的抗力.研究结果表明:S355N钢抵抗裂纹启裂及前期扩展的能力比S355N-Z25钢强,但前者抵抗裂纹后期扩展的能力比后者弱；当应力强度因子范围,△K小于34.3MPa·√m时,S355N钢的疲劳抗力比S355N-Z25钢弱,当△K等于34.3MPa·√m时,两者具有相同的疲劳抗力,当△K大于34.3MPa·√m时,前者的疲劳抗力比后者强.研究结果对两种钢板在工程上应用及结构的安全评定提供了参考.
关键词:
S355N及S355N-Z25钢板
,
低温CTOD断裂韧性
,
疲劳裂纹扩展速率da/dN
,
裂纹启裂
,
裂纹扩展
,
抗力
唐郑磊
,
丁健
,
许少普
,
李忠波
,
杨阳
,
康文举
钢铁研究
根据265 mm厚S500Q-Z35钢板的化学成分,评估冷裂敏感性和再热裂倾向,并对钢板进行Z向窗形层状撕裂试验和T型接头模拟件焊接试验,试验未发现裂纹.按美国ASME标准进行焊接工艺评定,可焊接的最大厚度为350 mm.气体保护焊GMAW和手工焊SMAW焊接后母材组织为粒状贝氏体+索氏体+少量铁素体,热影响区靠近母材区域为索氏体组织,近焊缝区为板条马氏体,并有网状析出物,焊缝区组织为针状铁素体+网状、半网状的先共析铁素体.
关键词:
S500Q-Z35
,
焊接
,
裂纹敏感性
,
微观组织
Li XING
,
Jie ZHAO
,
Fuzhong SHEN
,
Wei FENG
材料科学技术（英文）
A Z-parameter method is used to evaluate the damage process of HK40 austenitic steel. By using Z-parameter based on the Larson-Miller method, the nonlinear master curve of the log stress vs Larson-Miller parameter P can be expressed as: P=27.74-3.4lgσ-0.032σ, and a family of curves parallel to the master curve can be written as: P=(27.74-Z)-3.4lgσ-0.032σ, where Z represents the magnitude of the deviation from the master curve. According to the creep rupture data both from different segments of a serviced tube and from the same segment locations with different service time, the value of parameter Z has close relationship with the deterioration of creep rupture properties. The damage state of the samples is evaluated by monitoring the changes in natural frequency f and Young0s modulus E, and the relationships between Z and the damage parameters are discussed.
关键词:
Damage evaluation
,
蠕变断裂
,
奥氏体钢
,
Z参数
王晓旭
,
陈利
材料工程
doi:10.3969/j.issn.1001-4381.2011.11.001
通过单根Z-pin从复合材料层合板中拔出的试验方法,测试了Z-pin的拔出强度,计算了Z-pin的临界埋入深度,并引入抗拉强度利用率概念来表征Z-pin的抗拉强度在拔出过程中的利用程度.结果表明,直径0.50mm和0.28mm的Z-pin临界埋入深度分别约为5.1mm和3.1mm.当Z-pin的埋入深度小于临界埋入深度时,Z-pin从层板中拔出；Z-pin拔出强度与埋入深度成正比,与Z-pin的直径成反比；当Z-pin的埋入深度大于临界埋入深度时,Z-pin发生断裂,Z-pin的抗拉强度利用率达到100％.最后提出了提高抗拉强度利用率的建议.
关键词:
Z-pin
,
拔出强度
,
复合材料
,
拔出试验
,
抗拉强度
潘晶
,
刘新才
,
郭鹏举
,
徐峰
,
肖军
功能材料
在V=15m/s淬速下制备Sm(Co0.68Fe0.20Cu0.08Zr0.04)z(z=10、12)合金的快淬薄带,对薄带的相结构和微观形貌进行了研究.薄带自由表面SEM分析表明,微观组织由取向生长的胞柱晶束呈编织状构成,当z=10时,一个胞柱晶尺寸大约为(1～1.5)μm×(15～25)μm,而一个胞柱晶束的尺寸大约为(18～13)μm×(15～25)μm,当z值由10增大至12时,胞柱晶束变窄、变短.薄带自由表面XRD和EDAX分析显示,z=10的合金快淬薄带的微观组织以1∶7H结构为主,伴有少量的2∶17H结构,而z=12的合金快淬薄带相结构是2∶17H.取向生长的胞柱晶的c轴[001]在薄带平面内取向,每一束胞柱晶内各柱晶的c轴是互相平行的,而不同胞柱晶束的c轴取向不同.
关键词:
Sm-Co合金
,
快淬薄带
,
微观组织形貌
,
相结构