金属学报(英文版)
doi:10.1007/s40195-016-0370-9
Three high-nitrogen stainless steels with different N contents were successfully processed by equal-channel angular pressing for one pass, and their microstructures and mechanical properties were investigated. It was found that the microstructure of the billet was heterogeneous across the billet thickness, resulting in the difference in the mechanical properties due to the different deformation conditions. A relatively low strength, high uniform elongation, and high work-hardening rate for the samples at the bottom of the billet was achieved in comparison with those processed at the top. Meanwhile, it was observed that the density of deformation twins increased with the content of N; accordingly, the strength and elongation of the alloys increase with the content of N, resulting in a good strength-ductility combination.
关键词:
High-nitrogen
,
stainless
,
(HNS)
,
steels
,
Equal-channel
,
angular
,
pressing
,
(ECAP)
,
N
,
content
,
Twinning
,
Strength
,
Ductility
王丽
,
吴希文
,
张晨鼎
,
张通
,
简丽
,
武朝军
,
周涛
稀土
doi:10.3969/j.issn.1004-0277.1999.02.003
采用湿渣法研究了0℃时碘化钇(YI3)-乌洛托品氢碘酸盐(C6H12N4.HI)-水(H2O)的三元体系相平衡,绘制了该体系的等温溶解度相图,相图分析结果表明,该体系中有组成为YI3.C6H12N4.HI.14H2O的配合物生成,对所得配合物进行了化学分析、X-射线粉末衍射、红外光谱、差热-热重分析,测定了其密度、晶体轴性,确定了配合物结构中的配位关系.
关键词:
相平衡
,
碘化钇
,
乌洛托品氢碘酸盐
,
配合物
张麦仓
,
董建新
,
曾燕屏
,
谢锡善
,
罗子健
金属学报
利用热力耦合有限元程序FORMT,对PM René 95合金中等尺寸(外径尺寸约为630 mm)涡轮盘的等温锻造工艺进行了模拟式设计.结果表明,采用TZM钼基合金模具,在1050℃以接近10-3s.的应变速率进行闭式模锻和开式模锻,模具材料均能满足使用要求,且开式模锻设备最大载荷不超过31×103kN;采用K21合金模具,在1000℃以相同条件等温成形,模具材料因变形热效应及边界摩擦引起温升而失效且所需设备吨位相对较大.
关键词:
PM
,
null
,
null
,
null
张麦仓
,
董建新
,
曾燕屏
,
谢锡善
,
罗子健
金属学报
doi:10.3321/j.issn:0412-1961.2002.10.022
利用热力耦合有限元程序FORMT,对PM René 95合金中等尺寸(外径尺寸约为630 mm)涡轮盘的等温锻造工艺进行了模拟式设计.结果表明,采用TZM钼基合金模具,在1050℃以接近10-3s.的应变速率进行闭式模锻和开式模锻,模具材料均能满足使用要求,且开式模锻设备最大载荷不超过31×103kN;采用K21合金模具,在1000℃以相同条件等温成形,模具材料因变形热效应及边界摩擦引起温升而失效且所需设备吨位相对较大.
关键词:
PM René 95合金,等温锻造,热力耦合有限元,模拟式工艺设计
付锐
,
陈希春
,
任昊
,
冯涤
航空材料学报
doi:10.3969/j.issn.1005-5053.2011.3.002
自行设计开发了适合工业化生产高纯净,低偏析,无宏观缺陷铸锭的电渣重熔连续定向凝固技术(ESR-CDS)的设备和工艺,利用该技术成功制备了直径为φ150mm的René88DT合金定向凝周铸锭.采用XRD测试了定向凝固柱状晶的生长取向,结果表明,ESR-CDS René88DT铸锭柱状晶择优生长方向为<100>系晶向;ERS-CDS铸锭与传统ESR铸锭相比,枝晶组织生长方向保持一致,二次枝晶臂均匀细小,元素偏析程度低,且晶间一次析出相呈颗粒状,尺寸细小;等温热压缩实验结果表明,ESR-CDS René88DT合金热压缩试样在1100℃,0.0-50.1s-1应变速率下可达到70%以上压缩变形量并获得均匀细小的动态再结晶组织;ESR-CDS René88DT合金铸锭经等温锻造制备出了φ170mm×73mm的饼坯件,锻压变形量超过70%,饼坯件除上下两端的变形死区外均发生了动态再结晶,晶粒尺寸约50μm.
关键词:
电渣重熔连续定向凝固
,
热变形
,
动态再结晶
李晓
,
董建新
,
张丽娜
,
张麦仓
,
胡尧和
,
谢锡善
,
国为民
金属学报
经不同固溶时效处理的PM René 95合金于650℃分别在蠕变、保载5和90 s疲劳载荷条件下进行了裂纹扩展速率实验.结果表明,相同热处理制度下,疲劳保载时间越长,裂纹扩展速率越高;相同载荷条件下,增加一次高温固溶并缓冷,有利于降低合金的裂纹扩展速率,且固溶温度越高裂纹扩展速率越低;1200℃一次固溶缓冷并于1160℃二次固溶热处理比1140℃一次固溶的裂纹扩展速率约降低一个数量级;基体晶粒尺寸适当加大,强化相粒子γ′c数量增加、形状趋于田字形,有利于降低裂纹扩展速率.
关键词:
René
,
null
,
null
李晓
,
董建新
,
张丽娜
,
张麦仓
,
胡尧和
,
谢锡善
,
国为民
金属学报
doi:10.3321/j.issn:0412-1961.2001.10.012
经不同固溶时效处理的PM René 95合金于650℃分别在蠕变、保载5和90 s疲劳载荷条件下进行了裂纹扩展速率实验.结果表明,相同热处理制度下,疲劳保载时间越长,裂纹扩展速率越高;相同载荷条件下,增加一次高温固溶并缓冷,有利于降低合金的裂纹扩展速率,且固溶温度越高裂纹扩展速率越低;1200℃一次固溶缓冷并于1160℃二次固溶热处理比1140℃一次固溶的裂纹扩展速率约降低一个数量级;基体晶粒尺寸适当加大,强化相粒子γ′c数量增加、形状趋于田字形,有利于降低裂纹扩展速率.
关键词:
René 95粉末高温合金,裂纹扩展速率,热处理
宁远涛
贵金属
评述了合金元素对Au的漂白效果和机制，介绍了白色开金的几种色度参数，如CIE-L a*b*色度参数和颜色盒，CIE-LAB-C-H-L米制色度参数和基于CIE-XYZ色度参数的ASTM D1925黄色指数YI，讨论了某些白色开金的色度参数与冶金学特征。基于金合金的漂白效应与合金成分的密切关系，ASTM D1925黄色指数YI为设计白色开金成分提供了基本的指南。
关键词:
金属材料
,
Au合金
,
白色开金
,
色度参数
,
色度图
徐旸
,
汪艳
,
傅轶
合成材料老化与应用
采用多次挤出的方法和氧化诱导期(OIT)方法考察了抗氧剂对聚丙烯热氧稳定性的影响,测定了各次挤出试样的熔体流动速率(MFR)、黄度指数(YI)、力学性能以及氧化诱导期(OIT).实验结果表明:添加由主抗氧剂1010和辅抗氧剂168组成的复合抗氧剂后聚丙烯的熔体流动速率(MFR)、黄度指数(YI)、拉伸强度和冲击强度、氧化诱导期(OIT)与未添加抗氧剂的聚丙烯相比降低明显减缓,说明抗氧剂可有效抑制聚丙烯的老化,延长其使用寿命.
关键词:
聚丙烯
,
抗氧剂
,
热稳定性