Titanium-aluminium-nitride (Ti1-xAlxN) coatings were deposited by close-field unbalanced magnetron sputtering on M42 steel substrates and WC-6wto inserts at 450℃. The tribological behavior was analyzed by sliding against steel and WC-6wt0o balls, while the turning performance was evaluated by a conventional turning machine at high cutting speeds without using coolants. In the tribological tests, the formation of transfer layer and the variations of hardness of the coatings played an important role for sliding against steel balls. For the coatings sliding against WC-6wto balls, the Ti-Al-N coatings showed a similar friction coefficient, but the TiN coating exhibited a lower value. The difference could be explained by the tri-oxidation wear mechanism. In the turning tests, a superior cutting performance of the coating was found at x=0.45, which endured 38 minutes before the tool flank wear reached the maximum value of 0.3mm, whereas only 20 minutes were endured for the TiN coating. The excellent performance of the coatings in the turning tests could be explained by the enhanced mechanical properties and oxidation/diffusion resistance of the coatings.
关键词:
hardness
,
null
,
null
,
null
A.Vyas
,
K.Y.Li
,
Z.F.Zhou
,
Y.G.Shen
金属学报(英文版)
Carbon nitride ( CNx thin films have been deposited onto Si(100) (for structural and mechanical analyses) and M42 high-speed-steel (for tribological measurements) substrates at room temperature by closed-field unbalanced magnetron sputtering. The mechanical and tribological properties of these films were highly dependent on the N/C concentration ratio that was adjusted by the F(N2)/F(Ar) flow-rate ratio at fixed substrate biasing of -60V during deposition. The films were characterized by employing scanning electron microscopy (SEM), atomic force microscopy (AFM), nano-indentation measurements, X-ray photoelectron spectroscopy (XPS), Raman scattering and Fourier transform infrared (FTIR) spectroscopy, pin-on-disc tribometer, scratch tester, and Rockwell-C tester. The results showed that the N content in the films increased with the N2 pressure. However, the maximum N/C ratio obtained was 0.25. The nanohardness was measured to be in the range of 11.7-20.8 GPa depending on the N/C ratios. The XPS N 1s spectra showed the existence of both N-C sp^2 and N-C sp^3 bonds in films. Raman and FTIR spectra exhibited that N-C bonds were fewer when compared to other N-C bonds. The friction coefficient of the film deposited onto steel substrate with N/C=0.26 was measured to be -0.08 and for film with N/C=0.22 a high critical load of 70N was obtained. The tribological data also showed that the wear rates of these films were in the range of -10^-16m^3/Nm, indicating excellent wear resistance for CNx films.
关键词:
carbon nitride
,
null
,
null
Journal of Superconductivity and Novel Magnetism
The local structure and the g factors (g(x), g(y), and g(z)) of the Cu(2+) site in Y(2)BaCuO(5) are theoretically studied using the perturbation formulas of the g factors for a 3d(9) ion in orthorhombically elongated octahedra. The orthorhombic field parameters in these formulas are determined from the superposition model and the local geometry of the system. From the calculations, the oxygen octahedron is found to undergo the local elongation Delta Z (approximate to 0.05 angstrom) along c-axis and the relative bond length variation Delta X (approximate to 0.1 angstrom) along a- and b-axes, respectively. The calculated g factors based on the above local structure are in good agreement with the experimental data. The relationships between the anisotropies of the g factors and the low symmetrical (orthorhombic) distortions of the Cu(2+) site in Y(2)BaCuO(5) are discussed.
关键词:
Crystal fields and spin Hamiltonians;Electron paramagnetic resonance;Cu(2+);Y(2)BaCuO(5);crystal
于萍
,
王亚权
腐蚀学报（英文）
研究了添加0.1mass%稀土Y的铸造K38G高温合金在1000℃的恒温氧化行为.结果表明,较之不含Y的合金，含Y铸态K38G合金的氧化速率显著降低； 氧化时形成双层的外氧化膜，表层为以Cr2O3和TiO.2为主的混合氧化物层，内层为连续的Al2O3层；没有内氧化和内氮化，没有氧化膜的剥落，加入稀土Y有效地提高了氧化膜的粘附性能.
关键词:
高温氧化
,
null
,
null
,
null
于萍
,
王亚权
腐蚀学报（英文）
doi:10.3969/j.issn.1002-6495.2007.03.010
研究了添加0.1 mass%稀土Y的铸造K38G高温合金在1000℃的恒温氧化行为.结果表明,较之不含Y的合金,含Y铸态K38G合金的氧化速率显著降低;氧化时形成双层的外氧化膜,表层为以Cr2O3和TiO2为主的混合氧化物层,内层为连续的Al2O3层;没有内氧化和内氮化,没有氧化膜的剥落,加入稀土Y有效地提高了氧化膜的粘附性能.
关键词:
高温氧化
,
K38G
,
高温合金
,
稀土元素
,
Y
于萍
,
王亚权
,
王文
腐蚀学报（英文）
对加入0.05mass%～0.5mass%稀土Y铸造的K38G高温合金800 ℃恒温的氧化行为进行了研究.结果表明,含Y铸态K38G合金的氧化动力学曲线偏离了抛物线规律，接近于立方规律；Y有效抑制了该合金的内氧化；当Y含量达0.5mass%时，该合金中析出富Y相，降低了其氧化抗力.
关键词:
高温氧化
,
null
,
null
Physica Status Solidi B-Basic Research
The perturbation formulas of EPR g factors g(\\) g(perpendicular to) and hyperfine structure constants A(\\) A(perpendicular to) for the trigonal octahedral 3d(7) cluster are derived considering not only the configuration interaction effect due to the admixture among ground and excited states, but also the covalency effect due to the admixture between the d electrons of the 3d(7) ion and the p electrons of ligands. In these formulas, the parameters related to both effects and the trigonal field parameters are estimated from the optical spectra and the structural parameters of the studied system. According to these formulas, the EPR parameters g(\\), g(perpendicular to), A(\\) and A(perpendicular to) for Co2+ in the octahedral sites of Y3Al5O12 and Y3Ga5O12 garnets are satisfactorily explained from the optical spectra and the structure data. The role of the covalency effect is discussed.
关键词:
superposition model;phase-transition;absorption;linbo3;ions