MICROSTRUCTURAL MORPHOLOGIES AND MECHANICAL BEHAVIORS OF NICKEL-BASE SINGLE CRYSTAL SUPERALLOY CMSX-2 DURING PROLONGED TENSION

Z.F. Peng , Y Y Ren , B.Z. Fan , J. W Qin , P. Yan , J. C. Zhao , Y Q. Wang and J.H. Sun (Wuhan University of Hydraulic and Electric Engineering , Wuhan 430072 , China)(Central Iron and Steel Research Institute , Beijing 100081 , China)

金属学报(英文版)

Prolonged tension tcsts were caTried out by comblning elevated temperatures with declined stresses over thc range of 760-1050° C and 780-115MPa. The effects of temperature and applied stress on rupture life, and the relations of temperuture, applied stress and mpture life to characteristic dimensions of coherent phases (γ matrix channel width and mpcd γ precipitate thickness), and to the elongation as well as to the cross sectional area reduction of thc tested specimens were investigated. Under all testing conditions, longittLdinal coalescence of seveml adjacent armys of γ precipitates could occur to dtherent extents along the direction of the applied stress axis in addition to their normal directional coarsening. The extent of γ Longitudinal coalescence became increased and its morphology tended to be irmpular with the increase of temperuture although the applied stresses were relatively lower.

关键词: superalloy CMSX-2 , null , null , null

Alloy Model for the Stacking Fault Energy

Xiliang NIE , Yumei ZHOU , Lieping ZHONG and Dingsheng WANG(Lab. for Surface Physics , Institute of Physics , Chinese Academy of Sciences , Beijing 100080 , China)Renhui WANG(Dept. of Physics , Wuhan University , Wuhan 430072 , China)Yiying YE(Center of Instrument

材料科学技术（英文）

An accurate and simple model of stacking fault energy for alloys (solid solutions) has beendeveloped based on the embedded-atom method. The calculated value of stacking fault energy35 mJ/m2 for 304 austenitic stainless steel, is in a good agreement with the experimental one,30 mJ/m2. In the present model we find that the Hirth's empirical relationship is also suitablefor alloy.

关键词:

Practice for Extending Blast Furnace Campaign Life at Wuhan Iron and Steel Corporation

ZHANG Shourong

钢铁研究学报(英文版)

One of the problems encountered in 60′s to 80′s of 20th century in China′s steel industry was short life of blast furnace shaft as well as the excessive erosion of blast furnace hearth. A series of research work was carried out in order to extend blast furnace campaign life. The concept of research and development was integrated in the construction of BF (blast furnace) No5 at WISCO (Wuhan Iron and Steel Corporation), and in October, 1991, the BF No5 was blown in. The blast furnace has worked smoothly for more than 15 years without any medium repair even guniting. It is expected that the campaign life of BF No5 would be longer than 16 years with a production over 11 000 t per unit inner volume (m3). A new blast furnace with an inner volume of 3 400 m3 is under construction, and is designed with a campaign life of 20 years without any medium repair. The campaign life of blast furnaces in China has been extended in recent years.

关键词: blast furnace;campaign life;erosion

Practice for Extending Blast Furnace Campaign Life at Wuhan Iron and Steel Corporation

钢铁研究学报(英文版)

关键词:

欢迎投稿、订阅《Journal of Wuhan University of Technology-Materials Science Edition》

武汉理工大学学报-材料科学版(英文版)

关键词:

Application of Low-penetration Concrete as the Protecting Layer in Wuhan Yangtse River Tunnel Tube

武汉理工大学学报-材料科学版(英文版)

关键词:

Effects of TMCP Parameters on Microstructure and Mechanical Properties of Hot Rolled Economical Dual Phase Steel in CSP

TAN Wen , HAN Bin , WANG Shui-ze , YANG Yi , ZHANG Chao , ZHANG Yong-kun

钢铁研究学报(英文版)

Effects of chemical compositions, finish rolling temperature, isothermal temperature on runout table and coiling temperature on microstructure and mechanical properties of economical dual phase steel produced on CSP line were investigated. Experimental results showed that martensite volume fraction could be enhanced and banding microstructure could be reduced by controlling Mn, Si contents and applying proper finish rolling temperature. Optimized processing-parameters were obtained for DP580 production on CSP line of Wuhan Iron and Steel (group) Co (WISCO) in China. Optimal microstructure and mechanical properties could be achieved when the strip was finished rolling at the range of 790 to 830 ℃, isothermally holding at 680 to 740 ℃ and coiling below 250 ℃.

关键词: economical dual phase steel , mechanical property , banding microstructure , processing-parameter

Reply to "Comment on 'Low-temperature lattice excitation of icosahedral Al-Mn-Pd quasicrystals' "

Physical Review B

In response to the comment by Wang and Qin, we have rewritten our equation (22) following the coordinate system of Dina, et al. [J. Wuhan Univ. (Nature Science Edition) 3, 23 (1992)]. According to the thermodynamic stability condition and the experiment of Capitan et al., we have chosen the new parameters of the phason elastic constants. Based on this, we have recalculated the coefficients of the expressions on the vibrational denty of states and the specific heat of the icosahedral Al-Nin-Pd quasicrystal. Our results are still in agreement with the experimental data measured by Walti et al. [Phys. Rev. B 57, 10 504 (1998)]. It demonstrates that our method is useful for dealing with the low-temperature vibrational excitation of icosahedral quasicrystals.

关键词: quasi-crystals;diffuse-scattering

Treatment of Reused Comprehensive Wastewater in Iron and Steel Industry With Electrosorption Technology

ZHANG Yunhua , GAN Fuxing , LI Meng , WANG Dihua , HUANG Zhongmai , GAO Yunpeng

钢铁研究学报(英文版)

Electrosorption technology was used to treat the reused comprehensive wastewater from iron and steel industry. A problem of relatively high conductivity of wastewater which greatly affects the reuse was examined, and industrial test was conducted for the reused water advanced deionization and purification in a comprehensive wastewater treatment plant of WISCO [Wuhan Iron and Steel (Group) Corporation]. The results of the onsite industrial test showed a satisfactory treatment performance for the reused water even at a flow rate of 1000 L/h in a standard 500 L/h unit. The average conductivity decreased by about 70%, from 580-780 μS/cm to 100-350 μS/cm. The average removal efficiency of Cl- and Ca2+ was about 75% and 68%, respectively, and CODCr of the treated water was also reduced in some degree while the pH value was almost unchanged. The energy consumption was as low as 06 kWh/t, which was remarkably superior to the conventional technologies. Therefore, it is entirely feasible that the novel electrosorption technology can be used in enhanced desalination and purification treatment of reused comprehensive wastewater in iron and steel industry.

关键词: electrosorption , desalination , purification , conductivity , industrial reused water

Optimal Control of a Tandem Cold Rolling System for Tracking Problem

WU Guofa XU Zhe ZHUO Bing Central Iron and Steel Research Institute , Beijing , China.

材料科学技术（英文）

The optimal control principle and procedure of a tandem cold rolling system for tracking problem have been proposed in this paper for the first time. The state-space description of the tandem cold rolling system for the cold-strip mill of Wuhan Iron and Steel Company is: x_(k+1)=Ax_k+(_k,y_k=Cx_k+η_k The optimum performance index of the system for tracking problem is: J_(min)=minEr[(1/2)sum from k=0 to m e'_kOe_k sum from k=0 to m-1 u'_kRu_k] The authors have deduced the optimal control of the system for tracking problem as follows u_k~*=-S_k(Ay_k+_(k+1)-) the feedback gain matrix S_k is given by S_k=(B'P_(k+1)B-R)~(-1)B'P_(k+1) Pk satisfies the matrix difference equation p_k=P_(k+1)-[(S_k~(-1))'-B']~(-1)R(S_k~(-1)-B)~(-1)+Q with terminal condition P_m=Q. On the above-mentioned principle of optimal control,an optimal control procedure of the tandem cold rolling system has been obtained, and a computer simulation has been performed. The results of the simulation are satisfactory.

关键词: optimal control , null , null , null