材料科学技术（英）
Microstructure performance in the welding zone of T91 heat-resistant steel under the condition of TIG welding was researched by means of metallography, X-ray diffraction and scanning electron microscope (SEM).Experimental results indicated that microstructure of T91 weld metal was austenite + a little amount of d ferrite when using TGS-9cb filler wire.Substructure inside the austenite grain was crypto-crystal lath martensite, on which some Cr23C6 blocky carbides were distributed. The maximum hardness (HRC44) in the welding zone is near the fusion zone. There existed no obvious softening zone in the heat-affected zone (HAZ). For T91 steel tube of F63 mm×5 mm, when increasing welding heat input (E) from 4.8 kJ/cm to 12.5 kJ/cm, fracture morphology in the fusion zone and the HAZ changed from dimple fracture into quasi-cleavage fracture (QC). Controlling the welding heat input of about 9.8 kJ/cm is suitable in the welding of T91 heat-resistant steel.
关键词:
T91 heat-resistant steel
,
null
,
null
刘文鹏
,
张庆礼
,
杨华军
,
周鹏宇
,
孙敦陆
,
高进云
,
谷长江
,
罗建乔
,
王迪
,
殷绍唐
量子电子学报
doi:10.3969/j.issn.1007-5461.2011.02.018
采用固相反应法制备了Bi3+、Eu3+、Tb3+掺杂的Lu3TaO7.测量了样品的X射线衍射谱、激发和发射光谱及荧光衰减曲线.三种离子掺杂的Lu3TaO7均呈现出强的荧光发射,其中Bi3+具有峰位在431 nm处的一强发射宽带,衰减寿命为16.8μs,Eu3+、Tb3+则表现出稀土离子的特征锐发射峰,衰减寿命分别为1.26 ms和1.20 ms.因此,它们均是具有潜在应用前景的重闪烁体材料.
关键词:
材料
,
闪烁体
,
Lu3TaO7
,
发光
季振国
,
周荣福
,
毛启楠
,
霍丽娟
,
曹虹
无机材料学报
doi:10.3724/SP.J.1077.2009.09217
利用反应磁控溅射法制备了半导体锡锑氧化物薄膜 (TAO). 根据霍尔效应测试结果,当Sn/Sb 原子比处于0.22~0.33范围内时,TAO薄膜是p型导电的,在此范围之外,TAO薄膜是n型导电的. 光学带隙测量结果表明,不同Sn/Sb比的TAO薄膜的禁带宽度基本相同(～3.9eV).构造了一个全透明的PN结,其中n区为Sn/Sb原子比为0.5的TAO薄膜, p区为Sn/Sb原子比为0.33的TAO薄膜.n区TAO的电极用铟锡氧化物(ITO),p区TAO的电极用Cu薄膜.实验结果表明,由于两种导电类型的TAO薄膜具有相同的禁带宽度,上述透明PN结构具有典型的准同质PN结的整流特性.
关键词:
透明半导体薄膜
,
锡锑氧化物
,
PN结
Physics of Life Reviews
Commentaries by Philip W.T. Pong, Nongyue He, S.D. Liang, Tao Song, Yuri Gaididei and Sergey Volkov and Alexander Y. Grosberg on my review article (Pang, 2011 [1]) are answered. The validity of Davydov's mechanism of bio-energy transport, the completeness of theory, outstanding problems, the normalization and validity of wave function of the system in Pang' model as well as other related problems are elucidated in detail. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
biological temperature;3 channels;soliton;model
成艳
,
蔡伟
,
李洪涛
,
郑玉峰
,
赵连城
功能材料
采用多弧离子镀的方法在Ti-50.6%(原子分数)Ni形状记忆合金表面沉积了钽镀层.通过X射线光电子能谱(XPS)剖面分析发现TiNi合金表面钽镀层厚度均匀,并且在镀层与基体之间形成一薄层过渡层.将镀钽TiNi合金曝露于空气中后,通过XPS的全谱和高分辨谱图对其表面的成分和价态分析发现,镀钽层表面由于钽在空气中自然氧化形成了一层很薄的钽的氧化膜,最表面为高价钽的氧化物(Ta2O5),次表面为低价钽氧化物的混合物TaO2、TaO和TaOx(x＜1).
关键词:
TiNi形状记忆合金
,
多弧离子镀
,
钽
,
镀层
李江鸿
,
张红波
,
熊翔
,
肖鹏
,
黄伯云
稀有金属材料与工程
报道了一种在C/C复合材料基体上制各抗烧蚀TaC涂层的新方法.采用红外光谱、XRD及SEM表征了生成TaC涂层的Ta源:TaO2F·rH2O·TaF5.采用SEM观察了不同温度下转变生成的TaC涂层的形貌.在1200℃高温热处理,TaC涂层形貌为细颗粒状,在1800℃高温热处理后,TaC涂层为柱状晶.TaC的生成机制为:TaO2F·rH2O·TaF5高温分解凝聚生成的Ta2O5沉积在C/C复合材料基体表面,碳原子在Ta2O5中扩散反应生成TaC,TaC涂层形貌可由生成Ta2O5的凝聚成核理论解释.
关键词:
TaC涂层
,
制备
,
生成机制
吴维兰
,
许立坤
,
侯文涛
,
辛永磊
材料保护
以金属钽层作为钛阳极的中间层可提高阳极的使用寿命,而热分解法制备涂层操作方便、工艺简单且成本低.考察了五氯化钽正丁醇溶液在氮气(≥99.99%)中的热分解过程,并以五氯化钽正丁醇溶液为先驱体,在氩气(≥99.99%)中采用涂覆烧结的热分解法在钛基体上制备了含钽涂层,考察了热分解温度、涂覆次数对涂层表面形貌、相结构和结合力的影响.结果表明:五氯化钽正丁醇溶液在300℃时已基本分解完全,热分解最终产物含钽、氧和少量残余的氯,采用高纯惰性气氛可减少钽的氧化;钛基上含钽涂层表面呈龟裂状;涂层的相结构受烧结温度和涂覆次数的影响,主要为Ta,TaO2或Ta,TaO2,Ta2O5;热分解温度对涂层结合力的影响较大,而涂层厚度对结合力的影响相对较小.
关键词:
热分解法
,
钽涂层
,
钛基体
,
五氯化钽
,
形貌
,
相结构
,
结合力
李江鸿
,
张红波
,
熊翔
,
肖鹏
,
赵磊
,
黄伯
无机材料学报
doi:10.3724/SP.J.1077.2007.00973
液相先驱体浸渍法制备的C/C-TaC复合材料可望提高C/C复合材料的烧蚀性能. 本研究借助XRD、SEM对含钽树脂先驱体不同温度热处理后物质的成分与形貌进行分析, 并结合钽液的DSC-TG曲线揭示了含钽树脂转变生成TaC过程的反应机理. 研究表明: 含钽树脂中钽液是作为呋喃树脂的固化剂起作用, 显著降低了呋喃树脂的固化温度, 100℃低温热处理树脂便固化, 同时钽液中的TaF5水解生成TaO2F. 在真空保护气氛下, 温度升高到800℃以上, 含钽树脂中的部分TaO2F会分解成Ta2O5和气体TaF5. 随后, Ta2O5在1000℃时开始被树脂炭还原化合生成颗粒尺寸<1μm的TaC颗粒. 要控制钽的损失可通过长时间低温处理(室温～100℃)和通无水氨(150～500℃)来实现.
关键词:
含钽树脂
,
TaC
,
formation mechanism