The fractal and spinodal decomposition models combined Monte Carlo method were used in computer simulation of phase separation from CaO MgO Fe 2O 3 Al 2O 3 SiO 2 glass. The fractal dimension was applied to quantitative analysis. The mechanism of phase separation was investigated. The results showed that the fractal dimensions and simulated micrographs of phase separation were in good agreement with the experimental results. And the mechanism of phase separation was spinodal decomposition.
关键词:
glass
,
null
,
null
,
null
,
null
,
null
,
null
Chinese Physics Letters
The magnetic properties of 1 T-TaS2 and 1 T-Fe-0.07 Ta-0.93 S-2 have been studied, Experimental results show that the phase transition temperature of 1 T-TaS2 is a function of the magnetic field, At low temperatures, both compounds are in a mixed state of charge density wave -spin density wave due to the coherent superposition of antiferromagnetic coupling.
关键词:
density
Physical Review B
The magnetic properties and phase transitions of 1T-TaS2 and 1T-Fe0.07Ta0.93S2 have been studied in the interval of 1.5-300 K and over the range of 100 Oe-60 kOe. Experimental results show that at high temperatures the compounds are in a diamagnetic state and the commensurate-charge-density-wave-triclinic-nearly-commensurate transition temperature of 1T-TaS2 decreases with increasing magnetic field. The amount of variation is a function of the magnetic field. At low temperatures both 1T-TaS2 and 1T-Fe0.07Ta0.93S2 are in a paramagnetic state owing to the localized moments that come from the single Anderson-Mott localization state. The curves of magnetization versus temperature do not follow the Curie law or Curie-Weiss law, but can be described fairly well as M = M(0) + gamma T--n. The fitting parameters of experimental curves show that a part of the neighboring moment appears as antiferromagnetic coupling due to exchange interaction between the moments. The magnetic-field dependence of magnetization exhibits a complicated feature at low temperature. It shows that the compounds may undergo a phase transition at the maximum value of magnetization and then they are probably in a mixed charge-density-wave-spin-density-wave (CDW-SDW) state or SDW state due to the coherent superposition of the antiferromagnetic coupling.
关键词:
metal-insulator-transition;density-wave domains;high magnetic-fields;charge-density;doped 1t-tas2;coexistence;microscopy;systems;silicon;2h-tas2
桂晓露
,
张宝祥
,
高古辉
,
赵平
,
白秉哲
,
翁宇庆
金属学报
doi:10.11900/0412.1961.2015.00660
<p>对20Mn2SiCrNiMo贝氏体/马氏体复相高强钢进行淬火-配分-回火(Q-P-T)工艺处理, 并采用紧凑拉伸试样进行疲劳实验. 结果表明, Q-P-T工艺参数对贝氏体/马氏体复相高强钢的疲劳断裂特性具有显著影响, 经过合理的Q-P-T工艺处理的贝氏体/马氏体复相高强钢具有较高的疲劳门槛值(ΔKth=13.2 MPam1/2)及较低的裂纹扩展速率. 显微组织及裂纹扩展路径观察显示, Q-P-T处理的贝氏体/马氏体复相高强钢的显微组织包括贝氏体、马氏体和残余奥氏体薄膜, 其中“柳叶状”贝氏体及纳米级残余奥氏体薄膜可以阻碍裂纹扩展, 迫使裂纹转折、分叉或“间断”, 这是贝氏体/马氏体复相高强钢疲劳断裂性能改善的主要因素.p>
关键词:
疲劳断裂
,
贝氏体
,
淬火-配分-回火工艺
,
残余奥氏体
,
显微组织
桂晓露
,
张宝祥
,
高古辉
,
赵平
,
白秉哲
,
翁宇庆
金属学报
doi:10.11900/0412.1961.2015.00660
对20Mn2SiCrNiMo贝氏体/马氏体复相高强钢进行淬火-配分-回火(Q-P-T)工艺处理,并采用紧凑拉伸试样进行疲劳实验.结果表明,Q-P-T工艺参数对贝氏体/马氏体复相高强钢的疲劳断裂特性具有显著影响,经过合理的Q-P-T工艺处理的贝氏体/马氏体复相高强钢具有较高的疲劳门槛值(△Kth=13.2 MPa·m1/2)及较低的裂纹扩展速率.显微组织及裂纹扩展路径观察显示,Q-P-T处理的贝氏体/马氏体复相高强钢的显微组织包括贝氏体、马氏体和残余奥氏体薄膜,其中“柳叶状”贝氏体及纳米级残余奥氏体薄膜可以阻碍裂纹扩展,迫使裂纹转折、分叉或“间断”,这是贝氏体/马氏体复相高强钢疲劳断裂性能改善的主要因素.
关键词:
疲劳断裂
,
贝氏体
,
淬火-配分-回火工艺
,
残余奥氏体
,
显微组织