材料科学技术（英文）
To study the osteogenesis and transformation process of calcium phosphate bioceramic in vivo, biodegradable porous beta-tricalcium phosphate ceramics (β-TCP, 5×8 mm) were implanted in the tibia of rabbits. β-TCP ceramics with surrounding bone tissue were retrieved and observed by SEM, TEM and EPMA every month after implantation. The results showed that osteogenesis was active and β-TCP ceramics bonded to bones directly. The new bones were forming and maturing as materials were continuously degrading, and materials were finally replaced by new bone. Parts of the materials were degraded, absorbed and recrystallized, while the rest were dispersed to the spongy bone and the Haversian lamella in an irregular arrangement, becoming incorporated into bone formation directly by remodeling the structure. Some β-TCP crystals cleaved along its (001) rhombohedral plane and formed lath-like crystals in vivo.
关键词:
Calcium phosphate ceramics
,
null
,
null
,
null
,
null
Honglian DAI
,
Xianying CAO
,
Haichen SHAO
,
Chunhua SHEN
,
Shipu LI
材料科学技术（英文）
Electron probe and X-ray energy spectrum were used to investigate the chemical composition of the interface between material and new bone after porous tricalcium phosphate ceramic implanted in tibia of rabbits. The element changes of the interface, the materials transformation and the situation of new bone formation at different implantation period were observed. The results showed that the carbon element content decreased gradually in new bone tissue, and the content of calcium and phosphor element increased by degrees with the implantation time. At the same time, calcium-phosphor ratio in the new bone kept a higher level. New bone grew into the materials interior, material dispersed and degraded simultaneously. Both composition of materials and new bone tended to be consentient. Finally, the materials were substituted by new bone. After implantation, not only the materials itself dissolved and degraded partially, but also new bone formed on the outer and pore surface of β-TCP porous bioceramics, which showed that the degradation products of lifeless calcium phosphate inorganic materials took part in constituting of new bone tissue.
关键词:
Calcium phosphate
,
null
,
null
,
null
李志宏
,
柳卫平
,
白希祥
,
郭冰
,
连钢
,
颜胜权
,
王宝祥
,
陆昀
,
曾晟
,
苏俊
原子核物理评论
doi:10.3969/j.issn.1007-4627.2005.01.006
利用8Li次级束测量了质心系能量7.8 MeV 2H(8Li, 9Li)1H反应的角分布, 导出了8Li(d, p)9Li反应的天体物理S因子及9Li→8Li+n虚衰变的渐近归一化系数.
关键词:
8Li(d,p)9Li反应
,
角分布
,
天体物理S因子
,
渐近归一化系数
HUANG Jianshun CHEN Junming Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai
,
China Research Associate
,
Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai 200050
,
China
金属学报(英文版)
Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,the crystal structure is keeping original spinel; while at higher current density or by thermal activation,owing to violent movement of Li~+ ions,part of crystal structure transforms into rock type similar to face-centered cubic structure of ferrous oxide.The transition channels during insertion of Li~+ ions and limitation of Li~+ ions inserted were discussed.
关键词:
null
,
null
,
null
Journal of Materials Research
The effect of Li(3)N additive on the Li-Mg-N-H system was examined with respect to the reversible dehydrogenation performance. Screening Study with varying Li(3)N additions (5, 10, 20, and 30 mol%) demonstrates that all are effective for improving the hydrogen desorption capacity. Optimally, incorporation of 10 mol% Li(3)N improves the practical capacity from 3.9 wt% to approximately 4.7 wt% hydrogen at 200 degrees C, which drives the dehydrogenation reaction toward completion. Moreover, the capacity enhancement persists well over 10 de-/rehydrogenation cycles. Systematic x-ray diffraction examinations indicate that Li(3)N additive transforms into LiNH(2) and LiH phases and remains during hydrogen cycling. Combined structure/property investigations suggest that the LiNH(2) "seeding" should be responsible for the capacity enhancement, which reduces the kinetic barrier associated with the nucleation of intermediate LiNH(2). In addition, the concurrent incorporation of LiH is effective for mitigating the ammonia release.
关键词:
complex hydrides;improvement;mixtures;imides;amide;h-2
MANG Weishi WANG Guozhi ZHANG Yongchang HU Zhuangqi SHI Changxu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China Yongchang Associate Professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
A rapidly solidified microcrystalline Al-Li-Cu-Mg-Zr alloy and its superplasicity have been investigated.An optimum tensile elongation of 585% was obtained at 540℃ and strain rate 1.67×10~(-2)s~(-1).The superplastic Al-Li alloy is manufaetured using thermomechanical pro- cessing:solution,overaging,warm rolling and recrystallization.Microstructural changes in thermomechanical processing and cavitation occurred during superplastic deformation have been observed.The superplastic failure of alloy may be caused mainly by nucleation and growth of cavities as well as the linkage around grains.
关键词:
superplasticity
,
null
,
null
,
null
Zhijian LIU
,
Zhiyou LI
,
Wei DUAN
,
Xuanhui QU
,
Baiyun HUANG
,
Siqi ZHANG
材料科学技术（英文）
A LI-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated. Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the Li7B6 would be more finery distributed in the metal Li by means of intensified stirring. The discharge characteristic of the Li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.
关键词: