金属学报(英文版)
Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null
Carbon
Preparation of dense carbon materials without use of any binder was attempted, effect of grinding treatment on the characteristics of raw petroleum needle coke and on the properties of the sintered carbon compacts was investigated, and the sintering mechanizm of the coke after grinding was discussed. It was found that the coke particle size and crystalline size was decreased and the specific surface area of the coke was increased with grinding, and the influence was obvious up to 20 hours grinding treatment. The interlayer spacing of the coke after graphitization at 2773 K was gradually increased and the a-axis constant was marginally reduced with the grinding time. Results from the sintering experiment show that carbon materials can be sintered from the ground coke, and the density and flexural strength of the sintering compacts reached stable values of 1.8 g cm(-3) and about 70 MPa, respectively, after 20 hours grinding of the coke. The sintering ability of the coke after grinding was considered to result from the increase of surface energy, lattice distortion energy and fraction of volatile matters of the coke, which were induced by grinding treatment. (C) 1997 Elsevier Science Ltd
关键词:
needle coke;semicoke;baking;mechanical properties;particle size;graphite
MA Zongyi YAO Zhongkai Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
The SiC_w/Al composite prepared by squeeze casting has a combination of superior room temperature specific strength and modulus together with excellent thermal properties.The extrusion can make an improvement on the strength and ductility of the composite from 582 MPa as squeeze casted up to 639 MPa,and on the transformation from isotropic to the anisotropic structure.This seems to be explained by the orientation of whiskers and the densification of dislocations in matrix.TEM observation indicates that the stacking fault is the usual planar defect on the SiC_w surface. composite;;SiC whisker;;Al alloy;;microstructure
关键词:
composite
,
null
,
null
,
null
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null
Yang LUO
材料科学技术（英文）
Due to continued growth in key markets, a broadening of application base and performance improvements, the market demands of NdFeB magnet increased steadily in 1998, and the global output of sintered NdFeB magnet exceeded 10,000 t, in spite of the economic recession in Asia. In 1998 China produced 3,850 t sintered NdFeB block magnet, with an annual growth rate of +22% over the output in 1997.
关键词: