THR EFFECT OF OXIDE LAYER FORMATION ON THE ADHESION OF CONDUCTIVE POLYMER COATING TO A MILDSTEEL

Y. L. Zhang1) and G. Spinks2) 1) Departmentof Mechanical Engineering , Ngee Ann Polytechnic , 535 Clementi Road , Singapore5994892) Intelligent Polymer Research Institute , University of Wollongong , Northfields Ave , Wollongong , NSW , Australia , 2522

金属学报(英文版)

Arolled mild steel wascoated byconductive polymers( polyaniline/ MMPand polyaniline/HCSA) andthenim mersedin hot water(50 ℃) fordifferenttimesforstudytheadhesion ofcoatings.It wasfound thatthe adhesion tendsto decrease over time. Thestudyshown that onebrittle and porous Fe3 O4 layer formed between conductive polymercoating and steelsub stratein a moistenvironmentand, asa result, decreased thecoating adhesions.

关键词: conductive polymercoating , null , null

Investigation of Instability of Lattice of Bi_2Sr_2CaCu_2O_x

Han ZHANG and Qingrong FENG (Dept. of Physics , Peking University , Beijing 100871 , China)Y.Zhao(School of Materials Science and Engineering , University of New South Wales , Sydney 2052 , NSW , Australia)F.Ritter and W.Assmus (Physikalisches Institut , J.W.Goet

材料科学技术(英文)

Bi2Sr2CaCu2Ox superconductor was studied by differential scanning calorimetry (DSC) and thermogravimetry (TG) in different atmospheres. It is discovered that there is a thermal anomaly in the DSC curve, associated with a weight loss in the TG curve before the melting of the sample. Careful thermal analysis and high temperature X-ray diffraction reveal that the thermal anomaly and the weight loss show an instability of the crystalline Iattice. By annealing the sample in oxygen and argon, respectively and then by TC measurement and thermal analysis, the coincidence of transition temperature with the instability is found. The coincidence is further confirmed by Y-doped 2212 phase.

关键词:

渗锌涂层钢腐蚀行为的电化学阻抗谱研究

武传杰 , 林志峰 , 李相波 , 马伯江 , 许立坤

腐蚀学报(英文) doi:10.11903/1002.6495.2013.305

研究了粉末渗锌涂层钢在3.5%NaCl溶液、人工海水(ASW)和天然海水(NSW)中的腐蚀行为.结果表明,渗锌层主要成分为Zn-Fe合金.渗锌涂层在3.5%NaCl溶液中的腐蚀速率要大于ASW和NSW.这可能是由于两种介质中含有的成分能够与Zn反应,生成更难溶的物质堆积于涂层表面,导致腐蚀速率降低.

关键词: 粉末渗锌涂层 , 腐蚀 , 电化学阻抗谱 , 极化曲线