The sintering additives such as Al2O3 and/or Y2O3 were coated on the surfaces of Si3N4 particles via heterogeneous nucleation processing using a buffered pH solution as the precipitation reagent. They nucleated and grew only on the surfaces of Si3N4 and did not form sol particles in solution by TEM observation. The isoelectric point (IEP) of coated Si3N4 was different from that of as-received Si3N4. The IEP of Al(OH)3-coated Si3N4 occurred at pH8.4, which is close to that of alumina. When Al(OH)3-coated Si3N4 particles were coated with Y(OH)3, the IEP of coated Si3N4 powder shifted from pH8.4 to pH9.2, similar to that of yttria. In addition, the rheological data showed that Al2O3 and/or Y2O3 coated Si3N4 suspension is nearly Newtonian and that added Si3N4 suspension shows a shear rate thinning behavior.
关键词:
Si3N4 powder
,
null
,
null
,
null
Juxian ZHANG
,
Jinjun FENG
,
Longqiao GAO
材料科学技术（英文）
Properties of Al2O3-coated nano-SiC have been compared with those of as-received SiC. The isoelectric point (IEP) of SiC changed from pH3.4 to pH7.3 after coating with the alumina precursor, which is close to that of alumina. Because both surfaces of coated SiC and Al2O3 possess higher positive charge at pH=4.5~5.0, they are uniformly dispersed in the two-phase aqueous suspensions, Then a mixed powder containing nano-SiC dispersed homogeneously into the Al2O3 matrix was achieved from flocculating the two-phase suspension. Finally, Al2O3/SiC nanocomposites were obtained by coating nano-SiC with Al2O3, in which the majority of SiC particles were located within the Al2O3 grains. The observation by transmission electron microscopy (TEM) and the analysis by the X-ray photoelectron spectroscopy (XPS) showed that cracks propagated towards the intragranular SiC rather than along grain boundaries.
关键词:
Coated nano-SiC
,
null
,
null
,
null
李凤娟
,
吕国光
金属世界
doi:10.3969/j.issn.1000-6826.2014.04.14
通过对烧结配料所需原料及对冷烧结矿成品检验采制样方法的分析，找出影响检验结果真实性的因素，采取有效的改进措施，使本钢原料厂一次配料、本钢炼铁厂265 m2烧结二次配料及265 m2烧结系统各项稳定率有了很大的提高，烧结矿实物质量和各项技术质量指标有了很大的进步，保证了高炉的稳定顺行。
提高本钢265 m2冷烧结矿及原料检验代表性的实践
Practice of Improving the 265 m2 Cold Sinter and Raw Material Inspection Representative
供稿|
李凤娟,吕国光/
LI Feng-juan, LV Guo-guang
DOI：10.3969/j.issn.1000-6826.2014.04.14
导读内容
本钢炼铁厂265 m2烧结机生产所需要的含铁原料比较复杂，一次配料料种较多，且烧结含铁原料是由本钢原料厂二车间供料，原料质量的不稳定，会影响烧结矿质量的提高和新一号高炉的强化及高炉技术指标的改善。本钢质量管理中心驻冷烧检查站加强了对烧结配料所需原料及对冷烧结矿成品检验采制样代表性的研究，采取了一些改进措施，达到了良好的效果。含铁料成分稳定率、烧结矿各项质量和技术指标在稳步地提高。下面，对本钢质量管理中心驻冷烧检查站就提高采样及检验过程的准确性所采取的措施和办法进行说明。