A.Wiengmoon
,
T.Chairuangsri
,
N.Chomsang
,
N.Poolthong
,
J.T.H.Pearce
材料科学技术（英文）
Effects of heat treatments on hardness and dry wear properties of a semi-solid processed Fe-26.96 wt pct Cr-2.91 wt pct C cast iron were studied. Heat treatments included tempering at 500℃, destabilisation at 1075℃ and destabilisation at 1075℃ plus tempering at 500℃, all followed by air cooling. Electron microscopy revealed that, in the as-cast condition, the primary proeutectic austenite was round in shape while the eutectic M7C3 carbide was found as radiating clusters mixed with directional clusters. Tempering did not change the microstructure significantly when observed by scanning or transmission electron microscopy. Destabilisation followed by air cooling led to a precipitation of secondary M23C6 carbide and a transformation of the primary austenite to martensite. Precipitation behaviour is comparable to that observed in the conventionally cast iron. Tempering after destabilisation resulted in a higher amount of secondary carbide precipitation within the tempered martensite in the eutectic structure. Vickers macrohardness and microhardness in the proeutectic zones were measured. Dry wear properties were tested by using a pin-on-disc method. The maximum hardness and the lowest dry wear rate were obtained from the destabilisation-plus-tempering heat treatment due to the precipitation of secondary carbides within the martensite matrix and a possible reduction in the retained austenite.
关键词:
Semi-solid process
,
null
,
null
,
null
,
null
孙银洁
,
胡胜泊
,
李秀涛
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2010.02.027
利用SEM、TEM、XPS、XRD、Raman和元素分析仪分析了M40J和T300的表面化学、物理及微观结构特征.研究发现:M40J含碳量高于T300纤维,而含氮量低于T300纤维,且表面活性基团比T300纤维低;M40J和T300碳纤维表面具有大量沟槽,前者相对长而浅,后者相对短而深;T300纤维端面皮芯结构明显,而M40J端面结构较均匀;M40J的微晶结构及取向性优于T300碳纤维.
关键词:
M40J碳纤维
,
微观结构
,
化学特征
,
物理特征
谢兰清
,
王彩霞
兵器材料科学与工程
基于重整化平均场理论,在二维空穴掺杂t-t′-J-U模型的框架下,用Gutzwiller平均场近似理论研究高温超导体的基态相图,分析了次近邻跃迁电子(t′)对电子平均双重占据数(d)的影响.发现在掺杂浓度δ≠0的掺杂Gossamer超导态,次近邻跃迁的引入使d的数值在欠掺杂浓度区增大,在过掺杂浓度区显著减少.
关键词:
高温超导体
,
相图
,
电子态
,
电子次近邻跃迁
,
双重占据
王昂
,
公茂琼
,
吴剑峰
工程热物理学报
微微型节流制冷器在微小元件和制冷应用中有广阔的前景.本文通过对搭建一微型压缩机驱动的微型混合工质节流制冷器系统,取得初步结果.该微微型J-T节流制冷器采用3D打印技术,通道特征尺寸为0.1 mm,突破了传统机械加工的极限.通道深宽比达到8:1.初步实验表明,微微型J-T节流制冷器达到了230 K温区.由于采用微型压缩机驱动,系统结构紧凑,可在便携生物储存设备、低温医疗以及电子器件冷却等领域应用并能长期运行.
关键词:
微微型节流制冷器
,
混合工质
,
3D打印
Communications in Theoretical Physics
By using strong-field scheme, the complete d(5) energy matrix with D-2d symmetry has been constructed. Then, by diagonalization of this matrix at normal and various pressures, the whole energy spectrum [including the ground-state zero-field splitting (GSZFS)] and its pressure-induced shift (PS) of ZnTe:Mn2+ have uniformly been calculated. The results are in very good agreement with experimental data. According to the eigenfunctions and PS, the assignments of four absorption bands have been given. By taking into account the effect of different deformations of t(2) and e radial wavefunctions on t(2)(3)((4)A(2))e(2)((3)A(2))(4)A(1) and t(2)(3)(E-2)e(2)((3)A(2))E-4, the position of the third absorption band at normal pressure has been estimated. The tetragonal field is important for GSZFS of ZnTe:Mn2+ and its PS, which supports the existence of tetragonal Jahn-Teller distortion in ZnTe:Mn2+. The physical essentials of typical levels, GSZFS and their PS have been revealed.
关键词:
crystal fields;high pressure;optical properties;energy spectrum;Jahn-Teller effect;covalency effect;ZnTe : Mn2+;ligand-field calculation;theoretical calculations;zn1-xmnxte;ruby;epr
王迎芬
,
彭公秋
,
李国丽
,
谢富原
,
刘勇
材料科学与工艺
doi:10.11951/j.issn.1005-0299.20150420
为了研究T800H碳纤维的表面特性及其与BA9918树脂的界面匹配性，分别采用SEM、AFM、XPS和TGA对T800H碳纤维表面形貌、表面化学特性以及碳纤维上浆剂热稳定性进行表征，测试了T800H／BA9918复合材料湿热处理前后0°压缩强度、90°拉伸强度和层间剪切强度，并得到了其在湿热处理前后的开孔压缩和冲击后压缩性能。测试发现T800H碳纤维表面有明显的沟槽，有利于表面机械啮合作用；T800H／BA9918复合材料经29 J能量冲击后压缩强度为314 MPa；在130℃湿态环境下其0°压缩强度和层间剪切强度保持率高于58％，开孔压缩强度保持率高于60％。试验结果证明T800H碳纤维与BA9918树脂具有良好的界面匹配性，T800H／BA9918复合材料具有优异的耐湿热性能。
关键词:
T800H碳纤维
,
复合材料
,
力学性能
,
湿热处理
孙建春
,
盛光敏
,
陈登明
,
周安若
,
朱光俊
功能材料
1J50软磁合金的性能主要是通过H_2热处理获得的,在1130℃和H2气氛保护下对冷轧态1J50软磁合金进行了热处理.运用MATS-2010SA软磁测试仪对处理前后1J50软磁合金的磁性能进行了检测,运用金相显微镜、XRD等手段对处理前后1J50软磁合金的组织结构进行了分析.结果表明,通过H_2热处理,1J50软磁合金的矫顽力显著降低,起始磁导率和最大磁导率提高;组织结构发生明显变化,冷轧态1J50软磁合金组织为孪晶奥氏体,平均晶粒尺寸为200μm,处理过后,晶粒显著长大,平均晶粒尺寸为100μm;由于在600℃时采取了快冷,处理后1J50软磁合金中未出现大量FeNi相和FeNi_3相.
关键词:
H2热处理
,
1J50
,
组织结构
,
性能
井敏
,
谭婷婷
,
王成国
,
冯志海
,
杨云华
,
潘月秀
材料科学与工艺
doi:10.11951/j.issn.1005-0299.20150208
东丽T800H和T800S是分别采用湿纺和干湿纺制备的两种力学性能相近的碳纤维，为弄清不同纺丝方法对T800级碳纤维微观结构的影响，采用扫描电镜、X射线衍射仪、小角X射线散射仪和高分辨透射电镜对这两种碳纤维进行测试，比较其表面形貌、断口形状和形貌、石墨微晶结构和微孔结构等．研究结果表明，湿纺制备的T800H比干喷湿纺制备的T800S的表面粗糙、断口圆度差、原纤尺寸较大、石墨微晶致密度差且发育不完善、内部微孔尺寸大、石墨微晶条带韧性差，这正是T800H的拉伸强度和断裂伸长率不如T800S的重要微观结构因素，但T800H的石墨微晶取向度不如T800S，孔隙率略高于T800S．
关键词:
碳纤维
,
微观结构
,
力学性能
,
表面形貌
,
孔结构
,
石墨微晶
李新梅
,
张忠文
,
邹勇
,
杜宝帅
,
邹增大
材料导报
根据新型耐热钢T92和Super304H钢的焊接特点制定了适宜的焊接工艺,研究了焊制的T92/Super304H异种钢焊接接头的力学性能.结果表明,T92/Super304H异种钢接头的各项力学性均能满足使用要求.焊缝金属的韧性远低于T92钢侧热影响区,焊缝金属的结晶形态对焊缝韧性有很大的影响.焊接接头中焊缝金属的硬度值最高,而T92钢侧热影响区硬度最低,并且不同热影响区部位显微硬度变化较大,Super304H钢侧热影响区硬度变化不大.
关键词:
T92钢
,
Super304H钢
,
新型耐热钢
,
异种钢
,
焊接接头