Aluminizing of Cu by a pack cementation process was performed to improve its surface properties.The effect of variation of pack aluminizing temperature from 800 to 900℃ and aluminizing time from 1 to 6 h on the microstructure and the thickness of the aluminide coating of Cu was investigated. Pack aluminizing of Cu significantly improved the microhardness and the oxidation resistance. The microhardness was increased about seven times and the oxidation resistance,after 96 h exposure in air at 900℃, was extremely increased ten times by aluminizing Cu at 900℃ for 3 h.

关键词:

Microstructure and Tensile Properties of ZK60 Alloy Fabricated by Simplified Rapid Solidification Powder Metallurgy (S-RS P/M) Process

Zhenya Zhang

材料科学技术（英文）

This study investigated the microstructures and mechanical properties of ZK60 alloy prepared by a simplified rapid solidification powder metallurgy (RS P/M) processing system (S-RS P/M), which consists of warm press in dry air and hot extrusion. Microstructure characterizations showed that S-RS P/M alloy consisted of magnesium matrix and oxide stringers of ~1 μm in width. TEM (transmission electron microscopy) observations illustrated nano-size magnesia particles (10{30 nm) constituted oxide stringer in detail. Due to a relatively higher volume of nano-size magnesia particle produced during S-RS P/M process, 0.2% yield strength of S-RS P/M ZK60 alloy was found to be as high as 382 MPa, which is 10% higher than that of RS P/M alloy. The improvement in mechanical properties is mainly attributed to the combination effects of Orowan mechanism and coe±cient of thermal expansion (CTE) mismatch because of the approximately same average grain size.

关键词: Microstructure

用DEPT135测定Resol的组成及微细结构参数

杨金瑞 , 余尚先 , 顾江楠

高分子材料科学与工程

通过对resol(羟甲基酚化合物和低分子量羟甲基酚树脂)DEPT135图谱的分析讨论,得到一系列计算resol微细结构参数的经验公式.根据DEPT135图谱可判断是否发生缩聚反应,根据经验公式可计算酚单体各个活性点参与反应百分率或酚羟基导入率、不同类型缩聚所占百分率及低分子量羟甲基酚树脂的平均核体数.

关键词: 羟甲基酚化合物 , 羟甲基酚树脂 , DEPT135 , 结构参数

Oxygen reduction mechanism on copper in a 0.5 M H(2)SO(4)

Electrochimica Acta

The mechanism of the oxygen reduction reaction (ORR) in a naturally aerated stagnant 0.5 M H(2)SO(4) Was studied using electrochemical methods. The cathodic polarization curve showed three different regions; electrochernical impedance spectroscopy (EIS) measurement was used accordingly. The EIS data were analyzed, and the mechanism for the ORR was proposed consequently. The three regions include a limiting current density region with the main transfer of 4e(-) controlled by diffusion (-0.50V < E < -0.40V), a combined kinetic-diffusion region (-0.40V

关键词: Oxygen reduction;Hump phenomenon;Chemical redox;Copper;Electrochemical impedance spectroscopy;sulfuric-acid electrolyte;anodic-dissolution;sulfate-solutions;corrosion;behavior;adsorption;chloride;cu(111);alloy;model

Application of Microwave Radiation to Extractive Metallurgy

LIU Chunpeng XU Yousheng HUA Yixin Kunming Institute of Technology , Kunming , 650093 , China.

材料科学技术（英文）

In applying the microwave radiation to extractive me- tallurgy,it is essential first of all to find the extent of microwave energy absorbed by various minerals experi- mentally.In this paper,more than 25 kinds of common useful minerals have been individually irradiated by a 500 W,2450 MHz microwave source in an enclosed quartz crucible to ascertain their heating temperature in a definite time.In addition,the reduction and cbloridization tests were also carried out on the titanomagnetite concentrate and pentlandite with microwave heating,respectively. These experiments indicate potential applications of util- izing microwave energy in extractive metallurgy.

关键词: microwave radiation , null , null , null

SYNTHESIS OF NANO-ZnO PARTICLES FOR ALUMINUM METALLURGY AS INERT ANODE MATERIAL

A.A.A. Saleh , Y. Fu , X.J. Zhai

金属学报(英文版)

Nano-ZnO particle was produced by evaporating zinc powders in air at air °ow-rate from 0.2 to 0.6m3/h. Nano-ZnO particles was formed by the oxidation of the evapo- rated zinc vapor. X-ray di®raction shows the powders to be ZnO with lattice parame- ters of a=0.3249nm and c=0.5205nm. The particle size is dependent upon the transit time from the source to the collection area. The size of particles was ranged between 81 to 103nm. The average density resulted was 4.865g/cm3. Normal ZnO and nano-ZnO were investigated to use them in aluminum metallurgy as an inert anode material. A certain amount of both oxides were molded subsequently inserted to the molten cryolite-aluminum oxide to investigate the corrosive behavior of both oxides. When the sintering temperature increased up to 1300±C, the weight loss ratio rose to 5.01%{7.33% and up to 7.67%{10.18% for nano-ZnO and normal ZnO, respectively. However, when the samples in the molten cryolite aluminum oxide were put for long time, the corrosive rate was found to be higher. It was found that the corrosive loss weight ratio of nano-ZnO anode was much lower than the normal one made from ordinary-ZnO providing that the nano-ZnO is more possible to be use inert anode material.

关键词: reactive evaporation method , null , null

Simulations of Coarsening Behavior for M23C6 Carbides in AISI H13 Steel

Xinbin HU , Mei ZHANG , Xiaochun WU , Lin LI

材料科学技术（英文）

Based on the local equilibrium assumption, coarsening behavior of M23C6 carbide at 700℃ in H13 steel was simulated by DICTRA software. The results from the calculations were compared with transmission electron microscopy (TEM) observations. The results show the interfacial energy for M23C6 in H13 steel at 700℃ is thus probably 0.7 J•m-2, which fits the experiments well. The influence of composition and temperature on the coarsening rate was also investigated by simulations. Simulations show a decrease in the coarsening rate when V/Mo ratio is increased, while the coarsening rate increases with increasing temperature.

关键词: DICTRA Simulation , 碳化物粗化 , 界面能 , H13钢

OXIDE METALLURGY-ITS PURPOSES AND PRACTICAL APPROACHES

Z. T. Ma and D. Janke(Institute of Iron and Steel Technology , Freiberg University of Mining and Technology , Germany)

金属学报(英文版)

Useder certain conditions, nonmctallic inclusions such as oxides, sulfides, nitrides and carbides are no longer harmful to sted service properties. With the new concept of oxide metallurgy, these properties can be improved by generating fine oxide inclusions which serve as heterogeneous nuclei for sulfide and fine ferrite[1-4]. A novel continuous casting (CC) process is expected to be created with the utilization of oxide metallurgy. This is also useful for the forthcoming technologies of direct rolling and near-net-shape casting. The main idea of oxide metallurgy consists of an alternative oxidation technology. It is based on steels treated by complex metals such as Ti, Zr, Ti-Zr alloys and rare earth metals. The selected deoxidants should follow the required conditions which are concluded in this paper.

关键词: oxide , null , null , null

A Novel near Net-Shape Technique for P/M Parts with Large H/D Ratio

Yong LIU , Baiyun HUANG , Kechao ZHOU , Hongwu OUYANG , Yuehui HE

材料科学技术（英文）

In order to overcome the shortcomings of conventional hot pressing, a novel near net-shape technique, called radial hot pressing, for P/M parts with large height-to-diameter (H/D) ratio was introduced. Effects of processing parameters on the microstructures and density of P/M TiAl base alloy valves were studied. Results show that the radial hot pressing is an effective technique for manufacturing valves with a H/D ratio of about 10:1, and the perfect joint interface between the Mo sheet and the parts is helpful for subsequent HIPing.

关键词: Near net-shape technique , null , null