金属学报(英文版)
The mechanical properties and deformation mechanisms of unidirectional carbon fiber reiopreed magnesium composites under tensile loading are studied. Two different materials are used as fiber coatings: a single silica and a gradient C/SiC/SiO2. The results show that, under the same preparation conditions, composite with the former coating is broken in a non-cumulative mode and its failure stress is rather low. Conversely, the latter coating demonstrates much better efficiency and the cormsponding composite is broken in a cumttlative mode.
关键词:
tensile properties
,
null
,
null
B.W. Wang
,
H. Shen
金属学报(英文版)
Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null
SU Zuwu MENG Guowen GUO Hongzhen LIU Jianchao YAO Zekun Northwestern Polytechnical University
,
Xi'an
,
ChinaYANG Zhaosu HU Zongshi Baoji Non-Ferrous Metals Mill
,
Baoji
,
China
金属学报(英文版)
The formation reason and elimination method of non-uniform microstructure defects in Ti al- loy TC11 bar have been studied.The coagulating and coarsening into block of the part of grain boundary α and secondary α seem to be caused by the ingot cogging and initial forging temperature in the β region as well as no more enough deformation and uneven distribution. The grain α,elongated α and blocky α may be finally eliminated by adopting the technique of (α+β)thermomechanical processing+β processing,W.Q.+recrystallization annealing,A.C., thus the size of uniform and fine equiaxed α structure is believed to be reduced to 1.9258μm.
关键词:
TC11 Ti alloy
,
null
,
null
,
null
Transactions of Nonferrous Metals Society of China
The corrosion behavior of LY11 aluminum alloy in acid, alkaline and neutral soil after burying for 1, 3 and 5 a was studied. It is shown that localized corrosion is the major behavior of LY11 aluminum alloy in soil, and corrosion of LY11 depends on the soil texture: severe corrosion occurs in the heterogeneous alkaline and acid soil, and slight corrosion occurs in homogeneous neutral and acid clay soil.
关键词:
LY11 aluminum alloy;soil corrosion;corrosion behavior