By means of Precipitation hardening, a cast copper alloy with high strength and heatresistance named Cu-6Ti-Cr-Al has been developed. This alloy has good castability. After water quenching at 860℃ for 1 h and aging at 450℃ for 4 h, the tensile strength, σ_b, is greater than 890MPa and the compressive strength, σ_(bc), reaches 1300MPa, while the ratio of compression, ε_c, is maintained at 20%. When the environmental temperature is raised to 450℃, the mechanical properties do not show any appreciable loss. These copper alloy castings have been used on the roll sleeves of rubber formers and the journal bearings of sheet mills. The results have shown that the service life of these parts is much longer than that of aluminium bronze and 904alloy castings. In the present work, the microstructure, mechanical properties and strengthening mechanism were investigated.
关键词:
: cast copper alloy
,
null
,
null
,
null
SUN Wenqiang
,
CAI Jiuju
,
MAO Hujun
,
GUAN Duojiao
钢铁研究学报(英文版)
As the largest energy consuming manufacturing sector and one of the most important sources of carbon dioxide (CO2) emissions, the China′s iron and steel industry has paid attention to the study of changing trend and influencing factors of CO2 emissions from energy use. The logarithmic mean Divisia index (LMDI) technique is used to decompose total change in CO2 emissions into four factors: emission factor effect, energy structure effect, energy consumption effect, and steel production effect. The results show that the steel production effect is the major factor which is responsible for the rise in CO2 emissions; whereas the energy consumption effect contributes most to the reduction in CO2 emissions. And the emission factor effect makes a weak negative contribution to the increase of CO2 emissions. To find out the detailed relationship between change in energy consumption or steel production and change in CO2 emissions, the correlation equations are also proposed.
关键词:
CO2 emissions
,
energy use
,
LMDI technique
,
steel production
,
energy consumption
American Mineralogist
A natural high-pressure phase of titanium oxide with alpha-PbO2-structure has been found in omphacite from coesite-bearing eclogite at Shima in the Dabie Mountains, China. High-resolution transmission electron microscope observations have revealed an orthorhombic lattice, corresponding to alpha-PbO2-type TiO2, with cell parameters a = 0.461 nm, b = 0.540 nm, c = 0.497 nm and space group Pbcn. It occurs as nanometer-thick (< 2 nm) lamellae between multiple twinned rutile crystals, providing additional evidence of very high-pressure, metamorphism at 7 GPa, 900 degrees C. This implies subduction of continental material to a depth of more than 200 kilometers. alpha-PbO-type TiO2 could be an extremely useful index mineral for ultrahigh-pressure.
关键词:
high-pressure phase;ries crater;rutile;polymorph;titanium
张康侯
贵金属
doi:10.3969/j.issn.1004-0676.2008.02.011
评述了1996～2007年国际上对含金三元合金系相图、相变的研究进展.1996年以来,在主要国际专业刊物上发表了30多个三元金合金系相图的部分等温截面或纵截面,采用实验方法研究相图的工作占了绝大部分.在所研究的上述三元金合金系中,Au-Sn基合金系有11个,Au-Ag基合金系有6个,Au-Cu和Au-Sb基合金系各有4个,Au-Mn和Au-Si基合金系各有2个.这些合金系目前涉及到的主要应用领域为:钎焊材料、电触头材料、电子材料、磁性材料、形状记忆合金材料、金属离子源材料和喷丝头材料等.含金三元合金系的研究反映了当前对新型金合金功能材料的需求动向, 对指导促进相关新合金材料的开发有重要意义.
关键词:
金属材料
,
金合金
,
三元合金系
,
相图
,
进展
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null
American Mineralogist
Our efforts to introduce defects in rutile by conventional mechanical grinding as used for TEM study did not produce any defects or twinning. Experimental SAED patterns of rutile with intercalated alpha-PbO2-type TiO2 lamellae are consistent with those expected from calculated patterns. The values and precision of lattice parameters of alpha-PbO2-type TiO2 derived from such SAED patterns are also consistent with crystal data from X-ray diffraction studies.
关键词:
TiO2;high-resolution transmission electron microscope;Dabie Mountains;UHP metamorphism