X.M. Yang
,
D.B. Huang
,
L. T. Kong
,
T.J. Yang
,
Y.S. Xie and D. G. Wang(Institute of Chemical Metallurgy
,
Chinese Academy of Sciences
,
Beijing 100080
,
China)(University of Science and Technology Beijing
,
Beijing 100083
,
China)
金属学报(英文版)
The rate of reducing Fet O in CaO-SiO2-Al2O3-Fet O slags with carbon saturated in molten iron has been determined in a graphite crucible in the temperature range of 1673-1773K. The effects of temperature, slag basicity and FetO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with increasing temperature or FEtO concentration in slags, and the reduction rate has a parabolic relation with the simple basicity or optical basicity of slag, the maximum reduction rate being observed at around CaO/SiO2=1.5 of molten slags. The reduction reaction order is 1. 73 or 1.80, and the reduction activation energy is 299.9 or 295.9 kJ/mol in regard to Fet O weight content or Fet O activity calculated by using regular solution model, respectively. The reduction rate of CaO-SiO2-Al2 O3-Fet O slags with carbon saturated in molten iron is in the range of 0.32-3.48 mol-O/cm2·s.
关键词:
CaO-SiO_2-Al_2O_3-Fe_tO slags
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null