Effect Of Laser Input Energy On Ausn X Intermetallic Compounds Formation In Solder Joints With Different Thickness Of Au Surface Finish On Pads

W. Liu , C.Q. Wang , Y.H. Tian , M.Y. Li , null , null , null , null

金属学报(英文版)

Formation of AuSn x intermetallic compounds (IMCs) in laser reflowed solder joints was investigated. The results showed that few IMCs formed at the solder/0.1um Au interface. Needlelike AuSn 4 IMCs were observed at the solder/0.5 um Au interface. In Sn-2.0Ag-0.75Cu-3.0Bi and Sn-3.5Ag-0.75Cu solder joints, when the laser input energy was increased, AuSn 4 IMCs changed from a layer to needlelike or dendritic distribution at the solder/0.9 um Au interface. As for the solder joints with 4.0 um thickness of Au surface finish on pads, AuSn 4, AuSn 2, AuSn IMCs, and Au 2Sn phases formed at the interface. Moreover, the content of AuSn x IMCs, such as, AuSn 4 and AuSn 2, which contained high Sn concentration, would become larger as the laser input energy increased. In the Sn-37Pb solder joints with 0.9 um or 4.0 um thickness of the Au surface finish on pads, AuSn 4 IMCs were in netlike distribution. The interspaces between them were filled with Pb-rich phases.

关键词: Laser soldering , null , null

Q相-C2S-C4AF-C12A7系列水泥形成的研究

姜奉华 , 徐德龙

硅酸盐通报 doi:10.3969/j.issn.1001-1625.2004.06.006

通过研究Q相与C2S和Q相与C4AF的共存条件,构造Q相-C2S-C4AF水泥系统,对此系统水泥形成条件进行研究.研究表明:Q相与C2S和Q相与C4AF能够共存,可以组成Q相-C2S-C4AF-C12A7水泥系统.在Q相-C2S-C4AF-C12A7水泥系统中,Q相在1270℃开始生成,随着温度的升高,Q相的生成量逐渐增大;采用V2O5对β-C2S具有较好的稳定作用.随着C4AF量的增加,Q相的量也在增加,同时,烧成温度降低.

关键词: Q相 , Q相-C2S-C4AF水泥 , 形成条件 , 抗压强度

Q460C热处理挽救工艺

刘军刚

物理测试

Q460C钢板由于冶炼和轧制工艺不稳定,经常出现伸长率不合格的问题.论述了不同的热处理工艺对Q460C性能的影响.研究表明:Q460C经过正火后,强度明显降低.经过正火控冷后,强度、韧性均满足生产要求,提高了产品合格率.

关键词: Q460C , 热处理 , 力学性能

Q460C连铸板坯的高温塑性

段双霞 , 孙建林 , 李志恩 , 富平原 , 雷爱民

钢铁研究学报

在Gleeble-1500热模拟机上测定了Q460C连铸坯的热塑性,深入分析了钢Q460C的高温脆化机理,确定了连铸坯的最佳矫直温度.结果表明,钢Q460C高温脆化受变形速率的影响较大,在第Ⅲ脆性区变形速率越低脆化越严重,实验用钢Q460C的低塑性区确定在660～985℃,连铸坯顶弯、矫直温度应高于985℃,有利于提高塑性,避免连铸坯表面裂纹的产生.

关键词: Q460C连铸板坯 , 热模拟 , 高温塑性

Q460C连铸板坯的高温塑性

段双霞 , 孙建林 , 李志恩 , 富平原 , 雷爱民

钢铁研究学报

在Gleeble1500热模拟机上测定了Q460C连铸坯的热塑性，深入分析了钢Q460C的高温脆化机理，确定了连铸坯的最佳矫直温度。结果表明，钢Q460C高温脆化受变形速率的影响较大，在第Ⅲ脆性区变形速率越低脆化越严重，实验用钢Q460C的低塑性区确定在660~985 ℃，连铸坯顶弯、矫直温度应高于985 ℃，有利于提高塑性，避免连铸坯表面裂纹的产生。

关键词: Q460C连铸板坯;热模拟;高温塑性

Q345C钢板表面裂纹金相分析

潘红涛

物理测试 doi:10.3969/j.issn.1001-0777.2007.01.012

文章对Q345C钢板表面产生的裂纹进行了宏观和光学显微镜分析.结果显示:裂纹产生的原因是加热之后在轧制过程中形成的折叠,1号裂纹上出现的大型杂质有可能是压入的氧化铁皮.

关键词: 表裂 , 形状 , 组织

Q相-C2S-C4AF-C12A7水泥作为膨胀剂的研究

姜奉华 , 徐德龙

硅酸盐通报 doi:10.3969/j.issn.1001-1625.2005.04.026

采用普通硅酸盐水泥作为基体、Q相-C2S-C4AF-C12A7水泥作为膨胀剂、加入少量石膏的条件下进行试验研究.研究表明:Q相-C2S-C4AF-C12A7水泥能够作为膨胀组分,调节Q相-C2S-C4AF-C12A7水泥和SO3的量,能够得到所要求的膨胀水泥.从DTA和XRD得知,其膨胀源主要是钙矾石(AFt),它形成的速度及数量,可以通过控制Q相-C2S-C4AF-C12A7水泥和SO3的量来实现.

关键词: 膨胀水泥 , 膨胀剂 , 微观分析 , 钙矾石

超快冷工艺对Q390C钢组织与性能的影响

吴良芹 , 任娟

上海金属

研究了热轧后超快冷工艺对Q390C钢组织与性能的影响.结果表明:超快冷后Q390C钢的组织为珠光体和铁素体,其屈服强度、抗拉强度和断后伸长率分别可达388 MPa、548 MPa和27.3％,-20℃的冲击功为47 J;超快冷工艺提高了Q390C钢的力学性能.

关键词: 超快冷工艺 , 力学性能 , 组织 , 珠光体 , 铁素体

Q相-CA-C12A7体系水泥材料的初步研究

姜奉华

硅酸盐通报 doi:10.3969/j.issn.1001-1625.2005.06.028

在前人研究Q相合成基础上,采用正交实验的方法,研究了Q相-CA-C12A7体系水泥的烧成条件及水化性能.研究结果表明:在Q相-CA-C12A7系统中,Q相的形成温度在1260～1340℃之间;Q相-CA-C12A7系统水泥烧成的最佳条件是温度为1320℃,保温时间为40min.此水泥具有早期强度高,中期强度提高快,后期强度不发生倒缩.

关键词: Q相水泥 , 正交实验 , 烧成条件 , 抗压强度 , 微观分析

Two-step magnetization in a spin-chain system on the triangular lattice: Wang-Landau simulation

Physical Review B

The Wang-Landau algorithm is used to study the thermodynamic and magnetic properties of triangular spin-chain system based on two-dimensional Ising model in order to understand the magnetic-order dynamics in Ca(3)Co(2)O(6) compound. The calculated results demonstrate that the equilibrium state of the rigid spins produces the two-step magnetization curve at low temperature even when the random-exchange term is considered. This work indicates that the four-step magnetization behavior observed experimentally must be due to the nonequilibrium magnetization.

关键词: calcium compounds;exchange interactions (electron);Ising model;magnetisation;thermodynamics;one-dimensional ca3co2o6;density-of-states;compound ca3co2o6;phase-diagram;proteins;crystal