研究了退火温度和退火时间对冷轧变形后的Cu-Mg-Te-Y合金组织及性能的影响.结果表明:Cu-Mg-Te-Y合金在冷轧变形后,显微组织呈纤维状,内部晶粒取向改变,硬度提高,导电率降低;经过退火处理后,铜合金硬度下降,导电率回升,提高退火温度可明显提高合金伸长率;随退火时间延长,Mg原子从晶格中脱出,通过位错等扩散通道,在Cu2Te相周围偏聚,使导电率提高,但再结晶新晶粒的出现,晶界增多,使导电率降低,综合作用使合金的导电率明显提高;退火温度在360～390℃,退火时间lh以内时,Cu-Mg-Te-Y合金可以得到最佳的综合性能.
参考文献
| [1] | Li M.;Stubbins JF.;Edwards DJ.;Heuer JK. .Fracture behavior of high-strength, high-conductivity copper alloys[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2000(Pt.B):977-981. |
| [2] | 程智刚,王自东,林国标,张鸿,赵美,张茂奎.热处理工艺对Cu-Cr-Zr合金组织及性能的影响[J].铸造,2008(02):122-125. |
| [3] | Mu SG;Guo FA;Tang YQ;Cao XM;Tang MT .Study on microstructure and properties of aged Cu-Cr-Zr-Mg-RE alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):235-240. |
| [4] | Zhou, HT;Zhong, JW;Zhou, X;Zhao, ZK;Li, QB .Microstructure and properties of Cu-1.0Cr-0.2Zr-0.03Fe alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):225-230. |
| [5] | 沈月,付作鑫,张国全,孔健稳,张吉明,刘满门,胡洁琼,王松,谢明.高强高导铜银合金的研究现状及发展趋势[J].材料导报,2012(13):109-113. |
| [6] | 陆德平 .高强高导电铜合金研究[D].上海交通大学,2007. |
| [7] | Monzen R;Watanabe C .Microstructure and mechanical properties of Cu-Ni-Si alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(0):117-119. |
| [8] | 黄鑫,王德志,曾菊花,林高用.引线框架用KFC铜合金低温形变热处理后的组织与性能[J].机械工程材料,2011(12):59-62. |
| [9] | 贾磊,谢辉,王晓,杨飞,吕振林.高强高导Cu-Ni-Si合金的热处理工艺研究[J].铸造技术,2011(11):1553-1556. |
| [10] | 王涛.论铜合金引线框架材料研究方向[J].有色金属加工,2010(01):4-8,16. |
| [11] | ZHU Da-chuan,TANG Ke,SONG Ming-zhao,TU Ming-jing.Effects of annealing process on electrical conductivity and mechanical property of Cu-Te alloys[J].中国有色金属学会会刊（英文版）,2006(02):459-462. |
| [12] | 卓震宇,倪红军,孙宝德.稀土与硼对铜净化效果的比较[J].铸造,2002(07):435-438. |
| [13] | 朱达川,宋明昭,涂铭旌.铜碲合金时效工艺的研究[J].稀有金属材料与工程,2005(05):807-810. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%