目的：针对传统镁合金化学转化膜裂纹尺寸大、耐腐蚀性差等问题，制备一种镁合金磷酸盐/氮化硅双层结构的抗腐蚀复合膜。方法先对镁合金进行传统磷酸盐转化处理，再运用等离子体增强化学气相沉积技术沉积氮化硅膜层，分析复合膜的形貌、元素分布、表面电位及极化曲线，并与磷酸盐转化膜进行对比。结果氮化硅膜层能在磷酸盐转化膜裂纹处选择性优先沉积，从而在相当程度上填补转化膜层的裂纹，形成致密的复合膜结构。具有复合膜结构的镁合金表面电位和腐蚀电位明显高于传统磷酸盐转化处理的镁合金。结论镁合金表面制备磷酸盐/氮化硅双层复合膜后，抗腐蚀能力明显高于传统磷酸盐转化处理的镁合金。
Objective To solve the problems of traditional chemical conversion coatings on magnesium alloy such as large micro-cracks and poor corrosion resistance, a novel phosphate/ silicon nitride compound coating was prepared in this article. Methods First traditional magnesium phosphate conversion treatment was conducted, and then plasma enhanced chemical vapor deposition technology was used to deposit silicon nitride film layer. The morphology, element distribution, surface potential and polarization curve of the composite coating were analyzed, and compared with those of the phosphate conversion coating. Results Silicon nitride film layer could be selectively priorly deposited on the cracking positions of the phosphate conversion coating, and filled the cracks on the conversion coating layer, forming dense composite coating structure. The surface potential and corrosion potential of magne-sium alloy with composite coating structure were significantly higher than those of magnesium alloy treated with traditional phosphate conversion process. Conclusion After preparation of phosphate/ silicon nitride double composite coating on the surface of magnesi-um alloy, the corrosion resistance was significantly higher than that of the magnesium alloy treated with traditional phosphate con-version.
参考文献
| [1] | 兰伟,王第一,陈亮朝.镁合金磷酸盐转化膜的研究现状[J].材料导报,2007(z2):328-329. |
| [2] | 王敬丰,覃彬,吴夏,潘复生,汤爱涛.镁合金防腐蚀技术的研究现状及未来发展方向[J].表面技术,2008(05):71-74. |
| [3] | 蔡启舟,王立世,魏伯康.镁合金防蚀处理的研究现状及动向[J].特种铸造及有色合金,2003(03):33-35. |
| [4] | 李文钊,王波,郭毅,鲁彦玲,杜仕国.AZ91D镁合金表面铈转化膜及环氧/氟碳涂层附着性研究[J].表面技术,2013(03):63-66. |
| [5] | 赵明,吴树森,罗吉荣,李东南.镁合金磷酸盐-高锰酸盐化学转化处理工艺研究[J].特种铸造及有色合金,2005(06):328-329. |
| [6] | 高阳,代明江,向兴华,韦春贝,侯惠君.AZ91D镁合金磷酸盐转化膜的制备及性能[J].电镀与涂饰,2010(10):32-36. |
| [7] | 高福勇,赵明,李婷婷,付亚楠.AZ31镁合金化学转化膜形成的原位成像研究[J].表面技术,2012(04):118-121. |
| [8] | 金华兰,杨湘杰.AZ91D镁合金磷酸盐化学转化膜的组织及性能[J].特种铸造及有色合金,2009(05):441-444. |
| [9] | Bikulcius G.;Burokas V.;Martusiene A.;Matulionis E. .Effects of magnetic fields on the phosphating process[J].Surface & Coatings Technology,2003(2/3):139-143. |
| [10] | 苗斌,贾卫平,吴蒙华,杨帆.磁场作用下电沉积镍层织构及表面形貌分析[J].表面技术,2012(05):30-33. |
| [11] | Wanqiu Zhou;Dayong Shan;En-Hou Han;Wei Ke .Structure and formation mechanism of phosphate conversion coating on die-cast AZ91D magnesium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(2):329-337. |
| [12] | Chong KZ.;Shih TS. .Conversion-coating treatment for magnesium alloys by a permanganate-phosphate solution[J].Materials Chemistry and Physics,2003(1):191-200. |
| [13] | 胡九龙,杭凌侠,周顺.PECVD技术制备低折射率光学薄膜[J].表面技术,2013(02):95-97. |
| [14] | 余京松,马青松,葛曼珍,杨辉,江仲华.氮化硅薄膜的制备技术[J].中国陶瓷工业,1999(01):20-22. |
| [15] | Takahiro Ishizaki;Junko Hieda;Nagahiro Saito;Naobumi Saito;Osamu Takai .Corrosion resistance and chemical stability of super-hydrophobic film deposited on magnesium alloy AZ31 by microwave plasma-enhanced chemical vapor deposition[J].Electrochimica Acta,2010(23):7094-7101. |
| [16] | 刘志平,赵谡玲,徐征,刘金虎,李栋才.PECVD沉积氮化硅膜的工艺研究[J].太阳能学报,2011(01):54-59. |
| [17] | 肖葵,董超芳,李晓刚,魏丹.AZ91D镁合金电偶腐蚀的扫描Kelvin探针研究[J].稀有金属材料与工程,2011(09):1589-1593. |
| [18] | 安英辉,董超芳,肖葵,李晓刚.Kelvin探针测量技术在电化学研究中的应用进展[J].腐蚀科学与防护技术,2008(06):440-444. |
| [19] | ROHWERDER M;HORNUNG E;STRATMANN M .Micro-scopic Aspect of Electrochemical Delamination:an SKPFM Study[J].Electrochemica Acta,2003,48:1235-1243. |
| [20] | 周强,谢中,黄桂芳,周艳明,安錦,王祝盈,陈小林,许建斌.化学镀层的扫描开尔文力显微术（SKFM）研究[J].电子显微学报,2005(03):192-195. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%