在硫酸介质中以苯胺为单体,采用循环伏安法(CV)合成了聚苯胺(PANI).利用红外光谱(FTIR)、X射线衍射(XRD)、场发射扫描电镜(SEM)等手段对其结构和形貌进行了表征.在2 mol/L KOH电解液中,对合成的聚苯胺粉末构成的电极进行了循环伏安、恒流充放电(CP)及交流阻抗(EIS)等电化学性能测试.结果表明,电化学合成硫酸掺杂的PANI有良好的结晶性并呈现出纳米棒的结构,电流密度为20mA/cm2时,PANI电容器的比电容高达421.11F/g,是一种具有优良应用前景的超级电容器材料.
参考文献
| [1] | Jie Li;Mu Cui;Yanqing Lai;Zhian Zhang;Hai Lu;Jing Fang;Yexiang Liu .Investigation of polyaniline co-doped with Zn~(2+) and H~+ as the electrode material for electrochemical supercapacitors[J].Synthetic Metals,2010(11/12):1228-1233. |
| [2] | 钟新仙,汪艳芳,王芳平,王新宇,王红强,张初华,钟镇妙.不同形貌的甲酸掺杂聚苯胺的电容性能[J].功能材料,2010(01):66-68. |
| [3] | 杨红生,周啸,张庆武.以多层次聚苯胺颗粒为电极活性物质的超级电容器的电化学性能[J].物理化学学报,2005(04):414-418. |
| [4] | T.C. Girija;M.V. Sangaranarayanan .Investigation of polyaniline-coated stainless steel electrodes for electrochemical supercapacitors[J].Synthetic Metals,2006(2/4):244-250. |
| [5] | Hanlu Li;Jixiao Wang;Qingxian Chu;Zhi Wang;Fengbao Zhang;Shichang Wang .Theoretical and experimental specific capacitance of polyaniline in sulfuric acid[J].Journal of Power Sources,2009(2):578-586. |
| [6] | 张连明,谢英男,詹自力,司慧涵,蒋登高.聚苯胺的合成、表征及气敏性能研究[J].胶体与聚合物,2007(02):13-15. |
| [7] | 李晶,赖延清,李颉,刘业翔.导电聚苯胺电极材料在超级电容器中的应用及研究进展[J].材料导报,2006(12):20-23,27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%