以氮气作载气,采用冷喷涂技术成功地制备了NiCoCrAlY涂层及NiCoCrAlY/ZrO2复合涂层,并研究了涂层表面和横截面的微观结构、粒子之间的结合变形情况以及涂层的显微硬度.结果表明,以氮气作栽气的冷喷涂技术可以制备出结构较致密、硬度高(400～600HV)的NiCoCrAlY涂层;加入氧化锆能提高涂层的显微硬度;粉末颗粒在沉积过程中会发生强烈的塑性变形,变形颗粒边缘处含氧量较高.
参考文献
| [1] | Ichikawa Y;Sakaguchi K;Ogawa K.Deposition mechanisms of cold gas dynamic sprayed MCrAlY coatings[A].北京,2007:54. |
| [2] | Alkimov A P;Kosarev V F;Papyrin A N .A method of cold gas dynamic deposition[J].Doklady Akademii Nauk SSSR,1990,315(05):1062. |
| [3] | Gilmore D L;Dykhuizen R C;Neiser R A et al.Particle velocity and deposition efficiency in the coldspray process[J].Journal of Thermal Spray Technology,1999,8(04):576. |
| [4] | Novoselova T;Fox P;Morgan R;O'Neill W .Experimental study of titanium/aluminium deposits produced by cold gas dynamic spray[J].Surface & Coatings Technology,2006(8):2775-2783. |
| [5] | Bolesta A V;Fomin V M;Sharafutdinov M R et al.Investigation of interface boundary occurring during cold gas-dynamic spraying of metallic particles[J].Nuclear Instruments and Methods in Physics Research A:Accelerators,Spectrometers,Detectors and Associated Equipment,2001,470(1-2):249. |
| [6] | 王静,李相波,王佳.冷喷涂NiCoCrAlY高温合金防护涂层性能研究[J].材料开发与应用,2008(02):48-51. |
| [7] | 李相波,王静,王佳,陈光章.冷喷涂NiCoCrAIY涂层的微观性能研究[J].科技导报,2008(04):56-59. |
| [8] | 王静 .冷喷涂金属/陶瓷涂层制备工艺及涂层性能研究[D].中国海洋大学,2008. |
| [9] | Stoltenoff T;Voyer J;Kreye H.Cold spraying-state of the art and applieability[A].Wolfsburg,Germany,2002:366. |
| [10] | Papyrin A N;Kosarev V F;Klinkov S V.On the interaction of high speed panicles with a substrate under the cold spray[A].Germany:Essen,2002:380. |
| [11] | 鲍泽斌 .冷喷涂纯铜涂层工艺优化设计及其性能研究[D].辽宁工程技术大学,2004. |
| [12] | R. C. Dykhuizen;M. F. Smith;D. L. Gilmore;R. A. Neiser;X. Jiang;S. Sampath .Impact of high velocity cold spray particles[J].Journal of Thermal Spray Technology,1999(4):559-564. |
| [13] | 李文亚,李长久,王豫跃,杨冠军.冷喷涂Cu粒子参量对其碰撞变形行为的影响[J].金属学报,2005(03):282-286. |
| [14] | 高虹,赵良举,曾丹苓,高丽娟.冷喷涂Au纳米粒子在金属表面沉积过程的分子动力学模拟[J].金属学报,2006(11):1158-1164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%