The internal stress induced by a porous layer or passive layer can assist the applied stress to promote dislocation emission and crack propagation, e.9. when the pipeline steel is buried in the soil containing water, resulting in stress corrosion cracking （SCC）. Molecular dynamics （MD） simulation is performed to study the process of dislocation emission and crack propagation in a slab of Fe crystal with and without a porous layer on the surface of the crack. The results show that when there is a porous layer on the surface of the crack, the tensile stress induced by the porous layer can superimpose on the external applied stress and then assist the applied stress to initiate crack tip dislocation emission under lowered stress intensity KI, or stress. To respond to the corrosion accelerated dislocation emission and motion, the crack begins to propagate under lowered stress intensity KI, resulting in SCC.
参考文献
| [1] | I. Cerny;V. Linhart .An evaluation of the resistance of pipeline steels to initiation and early growth of stress corrosion cracks[J].Engineering Fracture Mechanics,2004(4/6):913-921. |
| [2] | J.Q. Wang;A. Atrens .SCC initiation for X65 pipeline steel in the "high" pH carbonate/bicarbonate solution[J].Corrosion Science,2003(10):2199-2217. |
| [3] | Z.Y. Liu;X.G. Li;C.W. Du;Y.F. Cheng;G;Li;C;W;Du;G;L;Zhai;Y;F;Cheng .Stress Corrosion Cracking Behavior Of X70 Pipe Steel In An Acidic Soil Environment[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(8):2251-2257. |
| [4] | G. Van Boven;W. Chen;R. Rogge .The role of residual stress in neutral pH stress corrosion cracking of pipeline steels. Part I: Pitting and cracking occurrence[J].Acta materialia,2007(26):29-42. |
| [5] | B.W. Pan;X. Peng;W.Y. Chu .Stress corrosion cracking of API X-60 pipeline in a soil containing water[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):76-81. |
| [6] | X.Z. Guo;K.W. Gao;W.Y. Chu .Correlation between passive film-induced stress and stress corrosion cracking of alpha-Ti in a methanol solution at various potentials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):1-7. |
| [7] | H. Lu;K.W. Gao .Stress Corrosion Cracking Caused by Passive Film-Induced Tensile Stress[J].Corrosion: The Journal of Science and Engineering,2000(11):1112-1118. |
| [8] | Q. K. Li;Y. Zhang;W. Y. Chu .Molecular dynamics simulation of stress corrosion cracking in Cu_3Au[J].Computational Materials Science,2002(3):510-518. |
| [9] | Q.K. Li;Y. Zhang;S.Q. Shi .Molecular dynamics simulation of dealloyed layer-enhanced dislocation emission and crack propagation[J].Materials Letters,2002(6):927-932. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%