通过对7A52合金时效状态的强度、硬度、电阻率和应力腐蚀性能的测试,对比分析了高温预析出对7A52合金T4和T61时效状态应力腐蚀和强度性能的影响.结果表明:高温预析出可以提高7A52-T4和7A52-T61合金的抗应力腐蚀性能,同时其强度和延伸率有所增加;高温预析出处理的7A52-T61合金拉伸强度达500MPa,延伸率13.0%,KISCC达到10.2 MPa·m1/2.
参考文献
| [1] | 林肇琦;孙贵经;陈长治 .中强Al-Zn-Mg合金焊接接头应力腐蚀断裂特点的观察[J].东北工学院学报,1980,3:22-28. |
| [2] | Liao C M .Al-3.7%Zn-2.5%Mg合金在3.5%NaCl溶液中焊接前后的SCC性能[J].铝加工技术,1994,4:43-50. |
| [3] | J.Liu;M.Kulak .A new paradigm in the design of aluminum alloys for aerospace applications[J].Materials Science Forum,2000(1):127-140. |
| [4] | Speidel M O.The Theory of Stress Corrosion Cracking in Alloys[M].Brussels:NATO Scientific Affairs Division,1971 |
| [5] | Najjar D;Magnin T;Warner T J .Influence of critical surface defects and localized competition between anodic dissolution and hydrogen effects during stress corrosion cracking of a 7050 aluminum al[oy[J].Materials Science and Engineering A,1997,A238(02):293-302. |
| [6] | 刘继华,李荻,郭宝兰.7xxx系列Al合金应力腐蚀开裂的研究[J].腐蚀科学与防护技术,2001(04):218-222. |
| [7] | 谷亦杰,李永霞,张永刚,黄正,陈昌麒.7050合金RRA沉淀析出的TEM研究[J].航空材料学报,2000(04):1-7. |
| [8] | Ringer S P;Hono K .Microstructural evolution and age hardening in aluminum alloys:atom probe field-ion microscopy and transmission electron microscopy studies[J].Materials Characterization,2000,44:101-131. |
| [9] | 陈康华,张茁,刘红卫,李松,黄兰萍.近固溶度高温析出对7055铝合金时效强化和应力腐蚀的影响[J].中南工业大学学报(自然科学版),2003(02):114-118. |
| [10] | 张茁,陈康华,刘红卫,李松,黄兰萍.高温预析出对Al-Zn-Mg-Cu铝合金显微组织、强度和应力腐蚀抗力的影响[J].金属热处理,2003(07):13-16. |
| [11] | 李松,陈康华,刘红卫,黄兰萍,张茁.Effect of high-temperature pre-precipitation on mechanical properties and stress corrosion cracking of Al-Zn-Mg alloys[J].中国有色金属学会会刊(英文版),2003(03):585-589. |
| [12] | 杨湘生.铝合金的应力腐蚀开裂[J].铝加工技术,1997(04):45-55. |
| [13] | 林肇琦 .高强铝合金的显微组织与应力腐蚀开裂问题(2)[J].轻金属,1980,6(02):16-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%