用硅藻土及木质活性炭为主要原料制备活性炭陶瓷复合材料,通过含炭量、碘吸附值、体积密度、气孔率和抗压强度测试确定最佳制备工艺条件。探讨该活性炭陶瓷复合材料对苯的吸附特性影响,对比分析了活性炭不同添加量、不同烧结温度及不同环境温度对材料苯吸附性能的影响。结果表明适宜的硅藻土与活性炭比值为7∶3,烧成温度为800℃,此时该材料的气孔率达到52.48%,体积密度为1.067 g/cm3,抗压强度为10.466 MPa,碘吸附值为291.24 mg/g,含炭量为25.62%,苯吸附率为9.56%,比表面积为290.72 m2/g。活性炭陶瓷复合材料的苯醛吸附率随着活性炭含量的增加明显加大,但受外界环境温度影响较小。
Diatomite and wood activated carbon were used to produce activated carbon ceramic composite materials.Effect of carbon content of the composites on properties such as iodine absorption,bulk density,porosity and compression strength of the materials were tested and thus the optimal process parameters were determined.The influence of activated carbon content and ambient temperatures on benzene removal capacity was also characterized.The results show that the optimal ratio（by mass） of diatomite to activated carbon is 7 to 3,and the optimal sintering temperature is 800 ℃.The materials with carbon content of 25.62% made under these conditions show the following properties： porosity of 52.48%,buck density of 1.067 g/cm3,compression strength of 10.466 MPa,iodine absorption of 291.24 mg/g,benzene absorption capacity of 9.56 and specific surface area of 290.72 m2/g.The benzene absorption capacity increased significantly with the increasing of activated carbon content but is merely affected by the ambient temperature.
参考文献
| [1] | 龚贵生,张春峰.室内家装空气污染分析及处理方法[J].徐州建筑职业技术学院学报,2008(04):35-37. |
| [2] | 陈金花,卢军.室内空气污染治理的研究进展[J].重庆建筑大学学报,2007(06):108-112. |
| [3] | 蒋绿林,施明恒,高玉明.活性炭对苯蒸汽吸附分离过程的实验研究[J].工程热物理学报,2003(02):274-276. |
| [4] | 赵丽媛,吕剑明,李庆利,范冠锋,文应财.活性炭制备及应用研究进展[J].科学技术与工程,2008(11):2914-2919. |
| [5] | 赵乃勤,魏娜,郭新权,李家俊.铵盐浸渍预处理对活性炭性能的影响[J].材料热处理学报,2004(02):60-63. |
| [6] | Cameron D S;Cooper S J;Dodgson I L .Corbon as supports for precious metal catalysts[J].Catalysis Today,1990,7(02):113-137. |
| [7] | 崔静,赵乃勤,李家俊.活性炭制备及不同品种活性炭的研究进展[J].炭素技术,2005(01):26-31. |
| [8] | 甘琦,周昕,赵斌元,胡克鳌.成型活性炭的制备研究进展[J].材料导报,2006(01):61-63,68. |
| [9] | 梁永仁,罗艳妮,杨志懋,丁秉钧.多孔陶瓷及其制备方法研究进展[J].绝缘材料,2006(02):60-64. |
| [10] | 王宗霞;曾路;王小波 等.硅藻土在扫描电镜下的微观形貌[J].电子显微学报,2006,25(增刊):345-346. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%