Hot compression tests of P92 steel at temperatures in the range of 1 173 to 1 523 K and at strain rates in the range of 0.1 to 10 s^-1 were carried out on a Gleeble-3500 thermal-mechanical simulator, and the corresponding flow curves were measured. The results showed that the flow stress and the peak strain increase with decreasing deformation temperature and increasing strain rate. The critical Z value, below which the complete dynamic reerystallization may occur, was determined to have 4.61 × 10^18. The hot deformation activation energy of the steel was about 437 kJ/mol. The hot deformation equation and the microstructure diagram of P92 steel were obtained. For the convenience of the practical application, the empirical equation for the peak stress can be described as σp=17. 17lnε＋902499/T-524.1.
参考文献
| [1] | Fujio Abe .Precipitate Design for Creep Strengthening of 9 Cr Tempered Martensitie Steel for Ultra Supercritical Power Plants[J].Science and Technology of Advanced Materials,2008,9(01):1. |
| [2] | Hald J .Microstructure and Long-Term Creep Properties of 9-- 12M Cr Steels[J].International Journal of Pressure Vessels and Piping,2008,85(06):30. |
| [3] | Kouichi MARUYAMA;Kota SAWADA;Jun-ichi KOIKE .Strengthening Mechanisms of Creep Resistant Tempered Martensitic Steel[J].ISIJ International,2001(6):641-653. |
| [4] | Sellars C M;Tegart W J M .On the Mechanism of Hot De- formation[J].Acta Metallurgica,1966,14(09):1136. |
| [5] | Jonas J J;Sellars C M;Tegart W J M .Strength and StructureUnder Hot-Working Conditions[J].Metal Reviews,1969,130(14):1. |
| [6] | Sellars C M;Tegart W J M .Hot Workability[J].lnternation al Metallurgical Reviews,1972,17(158):1. |
| [7] | Zener C;Hollomon J H .Effect of Strain Rate Upon the Plastic of Steel[J].Journal of Applied Physics,1944,15(01):22. |
| [8] | WANG Bao zhong;FU Wan tang;LI]Zhi qing et al.Study on Hot Deformation Behavior of 12Cr Ultra-Super-Critical Rotor Steel[J].Materials Science and Engineering,2008,87A(07):108. |
| [9] | M. Carsi;R. Allende;F. Penalba .Simulation of the Forming Behaviour of a Boron Modified P91 Ferritic Steel[J].Steel Research International,2004(1):26-32. |
| [10] | S.F.MEDINA;C.A.HERNANDEZ .GENERAL EXPRESSION OF THE ZENER-HOLLOMON PARAMETER AS A FUNCTION OF THE CHEMICAL COMPOSITION OF LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):137-148. |
| [11] | Rossard C.Mechanical and Structural Behaviour Under Hot Working Conditions[A].London:Institute of Metals and Iron and Steel Institute,1973:175. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%