采用改进后的PLINT高温可控气氛的微动磨损试验机，研究Inconel 690合金在300℃氮气及法向交变载荷条件下的微动磨损机制和动力学特性。结果表明：微动运行行为与激振频率密切相关，微动的Ft?D曲线呈现摩擦力周期波动的平行四边形型特征，微动运行于滑移区。在300℃氮气环境中，摩擦力的动态变化可以分为5个阶段，即跑合阶段、上升阶段、峰值阶段、下降阶段和稳定阶段。Inconel 690合金的微动损伤行为强烈地依赖于载荷、位移幅值、环境温度、气氛及激振频率等试验条件。从表面损伤形貌看，损伤微结构与试验参数密切相关；由于交变法向力和切向力共同作用，微动产生叠加效应，使剥层现象更加突出。在300℃氮气环境下，Inconel 690合金的损伤机理主要表现为磨粒磨损和剥层。
The fretting wear mechanisms and kinetic behaviours of Inconel690 alloy were investigated on the improved PLINT fretting rig under alternating loads conditions in high-temperature controlled-atmosphere environments. The results show that the fretting running behaviors are closely related to the normal excitation frequency. In parallelogram shapedFt?D curves, the friction fluctuates periodically, and accordingly the fretting runs in the slip regime (SR). Five stages of friction force curves can be observed at 300℃ in nitrogen environment, including initial stage, ascending stage, peak value stage descending stage and steady stage. The fretting wear behaviors for Inconel 690 alloy strongly depend on the normal load, displacement amplitude, temperature, atmosphere, excitation frequency and other test conditions. The super position effect of fretting wear behavior due to the combined effect of alternating normal force and tangential force is produced, so that delamination phenomenon becomes much more prominent. The abrasive wear and delamination are the major mechanisms of Inconel 690 at 300℃ in nitrogen environment.
参考文献
| [1] | Min-Hao ZHU;Zhong-Rong ZHOU.Composite Fretting Wear of Aluminum Alloy[J].Key engineering materials,20072(2):868-873. |
| [2] | 唐辉.世界核电设备与结构将长期面临的一个问题--微动损伤[J].核动力工程,2000(03):221-226,231. |
| [3] | 叶毅;任平弟;张晓宇;郭洪;李长香.高温大气和N 2中Inconel690/1Cr13不锈钢的微动磨损特性[J].中国有色金属学报,2013(7):1900-1906. |
| [4] | 张晓宇;任平弟;张亚非;朱旻昊;周仲荣.Incoloy800合金的高温微动磨损特性[J].中国有色金属学报,2010(8):1545-1551. |
| [5] | 向红先;任平弟;张晓宇;刘建涛;李放.交变载荷条件下NC30Fe合金微动损伤特性研究[J].摩擦学学报,2014(4):437-445. |
| [6] | Jin-Ki Hong;In-Sup Kim.Environment effects on the reciprocating wear of Inconel 690 steam generator tubes[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20037/12(7/12):1174-1182. |
| [7] | Ilsup Chung;Myungho Lee.An experimental study on fretting wear behavior of cross-contacting Inconel 690 tubes[J].Nuclear engineering and design,201110(10):4103-4110. |
| [8] | Sung-Hoon Jeong;Chung-Woo Cho;Young-Ze Lee.Friction and wear of Inconel 690 for steam generator tube in elevated temperature water under fretting condition[J].Tribology International,20053(3):283-288. |
| [9] | Jae Yong Yun;Myung Chul Park;Gyeong Su Shin;Ji Haeng Heo;Dae Il Kim;Seon Jin Kim.Effects of amplitude and frequency on the wear mode change of Inconel 690 SG tube mated with SUS 409[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20141/2(1/2):83-88. |
| [10] | J. Li;Y. H. Lu.Effects of displacement amplitude on fretting wear behaviors and mechanism of Inconel 600 alloy[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):223-230. |
| [11] | Mi, X.;Wang, W. X.;Xiong, X. M.;Qian, H.;Tang, L. C.;Xie, Y. C.;Peng, J. F.;Cai, Z. B.;Zhu, Min-hao.Investigation of fretting wear behavior of Inconel 690 alloy in tube/plate contact configuration[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2015:582-590. |
| [12] | 张晓宇;任平弟;钟发春;朱旻昊;周仲荣.0Cr20Ni32AlTi合金的高温微动磨损及摩擦氧化特性[J].中国有色金属学报（英文版）,2012(4):825-830. |
| [13] | Yun, Jae Yong;Shin, Gyeong Su;Il Kim, Dae;Lee, Ho Sik;Kang, Woong Soon;Kim, Seon Jin.Effect of carbide size and spacing on the fretting wear behavior of Inconel 690 SG tube mated with SUS 409[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2015:252-257. |
| [14] | 辛龙;李杰;陆永浩.Inconel 690合金高温微动磨损特性研究[J].摩擦学学报,2015(4):470-476. |
| [15] | 王文秀;蔡振兵;钱浩;李晨;谢永诚;米雪;彭金方;朱旻昊.不同温度下690合金传热管与抗振条的微动磨损特性[J].中国有色金属学报,2014(11):2777-2783. |
| [16] | Qian LM;Li M;Zhou ZR;Yang H;Shi XY.Comparison of nano-indentation hardness to microhardness[J].Surface & Coatings Technology,20052/3(2/3):264-271. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%