采用密炼机制备了不同组成的茂金属聚乙烯/茂金属乙烯-丙烯共聚物（mPE/mEP）共混体系,利用在线取样-显微分析的方法研究了不同组成mPE/mEP共混体系的微观相态结构,在研究相态结构的基础上,研究了体系的力学性能。结果表明,mPE/mEP共混物呈现明显的两相结构,当mPE体积含量在50%~60%范围内,共混体系形成双连续相,其他组分含量时,形成＂海-岛＂结构形貌。共混物的拉伸强度与共混体系微观相形态的变化有关,断裂伸长率随着mPE含量的增加由2360%降至550%,拉伸模量随着mPE含量的增加由3.5MPa增至102MPa。
Different metallocene polyethylene/metallocene catalyst ethylene-propylene copolymers（mPE/mEP） blend compositions were prepared in mixer.Online-sampling-microscope was employed to study the microscopic phase structure of different compositions of mPE/mEP blends.Besides the structure and morphology of mPE/mEP blends,the mechanical property was also studied.The results show that the two-phase structure is distinctly observed in mPE/mEP blends,the morphology of blends shows co-continuous phase when mPE contents range from 50% to 60%,the ＂sea-island＂ morphology is observed with the other content of components.The tensile strength of blends relates to the microscopic morphology,the elongation at break reduces from 2360% to 550% with increasing mPE content,the tensile modulus increases from 3.5MPa to 102MPa with increasing mPE content.
参考文献
| [1] | Jordens K.;Janzen J.;Rohlfing DC.;Welch MB.;Wilkes GL. .The influence of molecular weight and thermal history on the thermal, rheological, and mechanical properties of metallocene-catalyzed linear polyethylenes[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(19):7175-7192. |
| [2] | D'Agnillo L.;Penlidis A.;Soares JBP. .Controlling molecular weight distributions of polyethylene by combining soluble metallocene MAO catalysts[J].Journal of Polymer Science, Part A. Polymer Chemistry,1998(5):831-840. |
| [3] | Nitta KH.;Tanaka A. .Dynamic mechanical properties of metallocene catalyzed linear polyethylenes[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(3):1219-1226. |
| [4] | M. Razavi-Nouri;J. N. Hay .Theraml and dynamic mechanical properties of metallocene polyethylene[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(21):8621-8627. |
| [5] | Chen JY;Liu XL;Li HL .Improvement in processability of metallocene polyethylene by ultrasound and binary processing aid[J].Journal of Applied Polymer Science,2007(3):1927-1935. |
| [6] | A.D. Johnston;G.M. McNally;A.H. Clarke;W.R. Murphy .Blown Film Processing Characteristics of Metallocene and Conventional Polyethylenes[J].Developments in chemical engineering and mineral processing,2004(1/2):53-66. |
| [7] | Wen-Jun Wang;Zhibin Ye;Hong Fan;Bo-Geng Li;Shiping Zhu .Dynamic mechanical and rheological properties of metallocene-catalyzed long-chain-branched ethylene/propylene copolymers[J].Polymer: The International Journal for the Science and Technology of Polymers,2004(16):5497-5504. |
| [8] | Chen, XH;Ma, GQ;Li, JQ;Jiang, SC;Yuan, XB;Sheng, J .Study on morphology evolution and fractal character of the miscible blend between isotactic polypropylene and copolymer of ethylene and propylene[J].Polymer: The International Journal for the Science and Technology of Polymers,2009(14):3347-3360. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%