以丙氨酸为螯合剂采用软化学法制备了锂锰氧化物.XRD分析结果表明所合成的产物为尖晶石型锰酸锂;采用SEM对产物的形貌进行了表征,结果表明所合成产物主要为棒状,且颗粒大小分布均匀.通过FT-IR及TG/DTA等手段初步探讨了产物的合成机理.采用循环充放电测试考察了产物的电化学性能,结果表明采用此法制备的产物具有优异的电化学性能.
Lithium manganese oxide, as a cathode material for Li-ion battery, was prepared by the sol-gel method with Ala as a chelating agent. The powder samples were confirmed to be a single phase LiMn2O4 by X-ray diffraction (XRD) studies. The textural properties of the powder samples were examined by scanning electron microscope (SEM), showing that the powders mainly consist of rod-shaped particles with uniform particle sizes. The synthesis mechanism of LiMn2O4 was preliminarily investigated by FT-IR and TG-DTA etc. Electrochemical properties of the sample were evaluated with charge and discharge tests. The results show that the samples have excellent electrochemical properties.
参考文献
| [1] | Zhong Qiming, Arman Bonakdarpour, et al. The Electrochem. Soc., 1997, 144 (1): 205-213. [2] Motoharu Saitoh, Misuru Sano, et al. The Electrochem. Soc., 2004, 151(1): A17-A22. [3] Zhang Yuelan, Shin Heon-Cheol, Dong Jian, et al. Solid State Ionics, 2004, 171: 25-31. [4] Wu Hui, LEI Jia-heng, et al. J. of Wuhan Univ. of Tech- Mater. Sci. Ed., 2002, 17 (4): 20-24. [5] Sun Yang-Kook. Solid State Ionics, 1997, 100: 115-125. [6] Hon Y M, Chung H Y, Fung K Z, et al. J. Solid state Chemistry, 2001, 160: 368-376. [7] Kushida K, kuriyana K. Applied Physics Letters, 2000, 76 (16): 2238-3340. [8] Koh Takahashi, Motoharu Saitoh, Mitsuru Sano, et al. J. The Electrochem. Soc., 2004, 151(1): A173-A177. [9] Young Ho Rho, Kiyoshi Kanamura, Takao Umegaki. J. The Electrochem. Soc., 2003, 150(1): A107-A111. [10] G Ting-Kuo Fey, Chen J G, Subramanian V, et al. Materials Chemistry and Physics, 2003, 79: 21-29. [11] Castro-Garcy’a S, Castro-Couceiro A, M A Senari’s-Rodri’guez, et al. Solid State Ionics, 2003, 156: 15-26. [12] Kim Dong-Won, Sun Yang-Kook. Solid State Ionics, 1998, 111: 243-252. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%