制备了SiO2-B2 O3-Al2 O3-Li2O系CBN磨具用微晶玻璃结合剂.采用X衍射分析、热膨胀系数测试、扫描电镜、抗弯强度测试等方法研究了烧结温度对CBN微晶玻璃结合剂相组成、显微形貌和CBN磨具样品力学性能的影响.结果表明:烧结温度高于690℃烧结时,结合剂会析出β-锂霞石(LixAlxSi1-xO2)相;随烧结温度升高,β-锂霞石晶粒尺寸变大,膨胀系数减小,膨胀系数在740℃达到最小值4.21×10-6K-1;当温度超过740℃时,随温度升高β-锂霞石晶粒变小,含量降低,结合剂膨胀系数增大,烧结温度为840℃时,结合剂变为纯玻璃相.在740℃烧结,结合剂的抗弯强度达到最大值147.8 MPa;在790℃下烧结,CBN砂轮试样的抗弯强度达到最大值64.8 MPa.
A Li2O-Al2O3-SiO2 system glass-ceramic bond used in CBN grinding tools was prepared.The effects of sintering temperatures on phase composition,microstructure of the glass-ceramic bond and mechanical properties of the CBN grinding tools were studied by means of X-ray diffraction analysis,thermal expansion coefficient test,scanning electron microscopy and three-point bending test.The results show that when sintering temperature is over 690 ℃,β-eucryptite (Lix Alx Si1-x O2) phase can be precipitated in the bond.As the sintering temperature increasing,the grain size grows and the expansion coefficient of the bond reduces,the expansion coefficient can reach a minimum value of 4.21 × 10-6 K-1 at 740 ℃.When the temperature is over 740 ℃,β-eucryptite crystal begins to dissolve,the expansion coefficient of the bond increases.When the sintering temperature is 840 ℃,the bond is transformed into pure glass phase.When the bond is sintered at 790 ℃,the bending strength of the bond reaches a maximum value of 147.8 MPa.When the CBN grinding wheel is sintered at 790 ℃,the bending strength of the wheel can reach a maximum value of 68.4 MPa.
参考文献
| [1] | C. Guo;Z. Shi;H. Attia;D. McIntosh.Power and Wheel Wear for Grinding Nickel Alloy with Plated CBN Wheels[J].CIRP Annals,20071(1):343-346. |
| [2] | M.J. Jackson.Sintering and vitrification heat treatment of cBN grinding wheels[J].Journal of Materials Processing Technology,20071/3(1/3):232-234. |
| [3] | 张景强;王宛山;于天彪;张松.超高速陶瓷CBN砂轮纳米陶瓷结合剂性能实验研究[J].中国机械工程,2014(1):82-87. |
| [4] | 鲍崇高;宋奕侨;侯书增;杨兴化;杨建锋;姚文静.磨料表面微氧化对cBN磨具磨削性能的影响[J].西安交通大学学报,2015(2):124-129. |
| [5] | 万隆;翟浩冲;胡伟达;刘小磐;张国威;王志起.ZnO/Na2O（mol）对cBN陶瓷砂轮性能的影响[J].湖南大学学报（自然科学版）,2011(9):64-69. |
| [6] | 毛俊波;张凤林;周玉梅.超硬磨具陶瓷结合剂增韧补强的研究进展[J].中国陶瓷,2014(2):1-5,11. |
| [7] | 万隆;周武艺;徐化兵;张志飞;余舜.砂轮微晶玻璃结合剂的研究[J].金刚石与磨料磨具工程,2003(6):33-34,38. |
| [8] | 张红霞;张小福;卢安贤.微晶玻璃在立方氮化硼砂轮结合剂中的应用研究[J].新技术新工艺,2006(5):56-58. |
| [9] | 王春华;杨晓军.低温微晶玻璃结合剂结构和性能的研究[J].金刚石与磨料磨具工程,2011(2):58-61. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%