The liquid-solid transitions of （Co2Si＋CoSi） and （CoSi＋CoSi2） eutectic alloys were realized in drop tube and the rapid eutectic growth mechanism of intermetallic compounds was examined. The experimental and calculated results indicate that with increasing Co content, the intermetallic compound prefers nucleating primarily. The eutectic microstructures experience the transitions of ＇lamellar-anomalous-divorced＇ eutectic with undercooling. In undercooled state, the growth of CoSi intermetallic compound always lags behind others, and no matter how large the undercooling is, this intermetallic compound grows under the solutal diffusion control The calculated coupled zone demonstrates that （Co2Si＋CoSi） eutectic can form within certain undercooling regime, when the composition is in the range from 23.6% to 25.4% Si. And the calculated coupled zone of （CoSi＋CoSi2） covers a composition range from 40.8% to 43.8% Si.
参考文献
| [1] | D.H. Pi;J.M. Park;G.A. Song;J.H. Han;K.R. Lim;S. Yi;S.H. Yi;D.H. Kim;N.S. Lee;Y. Seo;K.B. Kim .Effect of Si on microstructure and mechanical properties of Fe-based ultrafine eutectic composites[J].Intermetallics,2010(10):1856-1859. |
| [2] | S.F. Lomayeva;A.N. Maratkanova .Structure, phase composition and magnetic properties of Fe-Si-C system due to mechanical activation of Fe-Si alloy in organic liquids[J].Intermetallics,2009(9):714-721. |
| [3] | S.W. Kim;M.K. Cho;Y. Mishima .Hihg temperature thermoelectric properties of p- and n- type beta-FeSi_2 with some dopants[J].Intermetallics,2003(5):399-405. |
| [4] | C. Gras;N. Bernsten;F. Bernard .The mechanically activated combustion reaction in the Fe-Si system: in situ time-resolved synchrotron investigations[J].Intermetallics,2002(3):271-282. |
| [5] | R.A. Varin;Y.K. Song .Effects of environment on fracture toughness of binary and ternary nickel suicide-based intermetallics[J].Intermetallics,2001(8):647-660. |
| [6] | C.-L. Chen;R.C. Thomson .Study on thermal expansion of intermetallics in multicomponent Al-Si alloys by high temperature X-ray diffraction[J].Intermetallics,2010(9):1750-1757. |
| [7] | C.-L Chen;A. Richter;R.C Thomson .Investigation of mechanical properties of intermetallic phases in multi-component Al-Si alloys using hot-stage nanoindentation[J].Intermetallics,2010(4):499-508. |
| [8] | C-L Chen;A. Richter;R.C. Thomson .Mechanical properties of intermetallic phases in multi-component Al-Si alloys using nanoindentation[J].Intermetallics,2009(8):634-641. |
| [9] | D.P. Riley .Synthesis and characterization of SHS bonded Ti_5Si_3 on Ti substrates[J].Intermetallics,2006(7):770-775. |
| [10] | M.J.H. van Dal;D.G.G.M. Huibers;A.A. Kodentsov .Formation of Co-Si intermetallics in bulk diffusion couples[J].Intermetallics,2001(5):409-421. |
| [11] | M.J.H. van Dal;A.A. Kodentsov;F.J.J. van Loo .Formation of Co-Si intermetallics in bulk diffusion couples[J].Intermetallics,2001(6):451-456. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%