MICROSTRUCTURE IN LASER FUSED HIGH SPEED STEEL W6Mo5Cr4V2(M2)

金属学报(英文版), 1993, 6(1): 36-39.

MICROSTRUCTURE IN LASER FUSED HIGH SPEED STEEL W6Mo5Cr4V2(M2)

LIU Ning CUI Kun Huazhong University of Science and Technology , Wuhan.China DENG Zonggang Hefei University of Technology , Hefei , China CHENG Benpei KONG Jie Institute of Solid State Physics , Academia Sinica , Hefei , China Doctorate student , Department of Mechanical Engineering No.2 , Huazhong University of Science and Technology , Wuhan 430074 , China

Keywords： High speed steel W6Mo5Cr4V2(M2) , null , null

Microstructure of the deepest zone of high speed steel W6Mo5Cr4V2(M2)melt after laser fu-sion was found to be so fine as the ehill zone of a solidified ingot.When narrower chill zoneformed,the long columnar dendrites grow into the melt and then the fine equiaxed cellularstructure appears in upper melt region nearly surface.The substructure of cellular grains anddendrites was observed to consist of martensite and retained austenile,while the carbides asM_6C_■ Cr_7C_3 and MC distributed at their boundaries.It is believed that the highermicrohardness up to HV_(0.1)=865-960 of the laser fused structure of the alloy is due to the oc-currence of martensite.

参考文献

[1]
[2]
[3]
[4]
[5]

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

MICROSTRUCTURE IN LASER FUSED HIGH SPEED STEEL W6Mo5Cr4V2(M2)

参考文献