本文研究了喷雾热解法制备氧化锆纤维的过程．用醋酸氧锆为前驱体能够制备出直径1～2μm、长度1～5cm的氧化锆纤维．研究了前驱体溶液浓度、表面张力、粘度对产品形貌的影响．通过控制操作条件，可以得到实心或空心纤维．
Zirconia fibers, 1~2μm in diameter and 1~5cm in length, were synthesized by spray pyrolysisof airconyl acetate solutions. The effects of precursor solution concentration, surface tension,viscosity on morphology of the resultant fibers were studied. Solid and hollow fibers were obtainedby controlling the operating parameters.
参考文献
| [1] | 早濑稚博. 国外耐火材料, 1989, (4): 26--33 2 Bracke P, Schurmans H, Verhoest J. Inorganic Fibers and Composite Materials,Pergamon Press, 1984. 35--47 3 Clark D E. Ceram. Eng. Sci. Proc., 1989, 10 (10): 1271--1282 4 Kamiya K, Yoko T. J. Mat. Sci., 1986, 21: 842--848 5 Jada Sivananda, Bauer Jon F. Ceram. Eng. Sci. Proc., 1990: 11 (9--10): 1480--1499 6 Yogo Toshinobu. J. Mat. Sci., 1990, 25: 2394--2398 7 United Paten 3322865 8 周晓东, 古宏晨, Zhang S C. 华东理工大学学报, 审稿中. 9 Zhang S C, MessingGary L, Borden Michael. J. of Am. Ceram. Soc., 1990, 73 (1): 61--67 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%