某氰化渣中金的品位为12.03 g/t,氰化渣里游离金的颗粒极细,并且被铁氧化物包裹,难以解离,属于难浸类金矿。采用改性石硫合剂对氰化渣进行了浸金研究,考察了超细磨时间、氧化剂用量、矿浆pH和搅拌时间对金浸出率的影响。优化实验条件为:超细磨时间2 h、氧化剂CaO2用量0.78 g/500 g、矿浆pH≈11.5、液固比2:1、搅拌浸出时间24 h,金的浸出率达78.57%。

The gold grade in the cyanide residue is 12.03 g/t in a certain gold mine. The fine distribution of free gold wrapped with iron oxide in the cyanide residue usually makes the valuable single mineral difficult to dissociate, as a part of the refractory gold ore. Leaching tests of gold using modified Lime-Sulphur-Synthetic-Solution (MLSS) was investigated to leaching the residue. The influence of gold leaching rate from cyanide residue by superfine grinding time, oxidant dosage, slurry pH and mixing time were discussed. The optimal experimental conditions were determined as follows:ultrafine grinding time 2 h, the dosage of oxidant CaO2 0.78 g/500 g, pH value of 11.5, the liquid-solid ratio 2:1 and stirring leaching time of 24 h. Under the optimal condition, the gold leaching rate was 78.57%.

参考文献

[1] 李怀梅 .氰化渣综合回收铁、金的工艺研究[D].山东理工大学,2012.
[2] 朱忠泗 .硫脲类非氰化浸金药剂的制备及应用研究[D].中南大学,2014.
[3] 冯冲 .硫代硫酸盐浸金的机理及稳定性研究[D].太原理工大学,2014.
[4] 陈江安;周源.某金矿石石硫合剂法浸金工艺研究[J].有色金属(选矿部分),2004(5):16-18.
[5] 周军;兰新哲;宋永辉.改性石硫合剂(ML)浸金试剂稳定性研究[J].稀有金属,2008(4):531-535.
[6] 徐斌 .黝铜矿型铜铅锌硫化矿浮选新药剂及其综合回收新工艺研究[D].中南大学,2013.
[7] 刘有才;朱忠泗;符剑刚;李丽峰;林清泉;李志辉.某金矿石的石硫加碱催化合剂法浸金研究[J].稀有金属,2013(1):123-129.
[8] 傅平丰;孙春宝;康金星;龚道振.石硫合剂法浸金的原理、稳定性及应用研究进展[J].贵金属,2012(2):67-70.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%