为了使研制的页岩-粉煤灰轻骨料更适应工业化生产,设计了不同的焙烧制度,分析了预热温度、升温速率、焙烧温度、焙烧时间等因素对轻骨料性能的影响.研究表明:对轻骨料性能影响显著的是焙烧温度,其次是焙烧时间；预热温度为650℃,升温速度12 ℃/min,焙烧时间15 min,焙烧温度1140℃的制度下,轻骨料的颗粒表观密度为990 kg/m3,颗粒强度达到8.52 MPa,24h吸水率为3.36％,是质轻高强低吸水的轻骨料.改变焙烧制度,使轻骨料的孔结构不同,轻骨料强度随轻骨料孔隙结构、孔隙分布和孔壁厚度的变化而发生改变.
参考文献
| [1] | Fang-Chih Chang;Shang-Lien Lo;Ming-Yu Lee;Chun-Han Ko;Jyh-Dong Lin;Su-Chen Huang;Chu-Fang Wang .Leachability of metals from sludge-based artificial lightweight aggregate[J].Journal of hazardous materials,2007(1/2):98-105. |
| [2] | Su-Chen Huang;Fang-Chih Chang;Shang-Lien Lo;Ming-Yu Lee;Chu-Fang Wang;Jyh-Dong Lin .Production of lightweight aggregates from mining residues, heavy metal sludge, and incinerator fly ash[J].Journal of hazardous materials,2007(1/2):52-58. |
| [3] | Show KY;Lee DJ;Tay JH;Hong SY;Chien CY .Lightweight aggregates from industrial sludge-marine clay mixes[J].Journal of Environmental Engineering,2005(7):1106-1113. |
| [4] | ROBERTO DE'GENNAEO;SOSSIO FABIO GRAZIANO;PIERGIULIO CAPPBLLETTI .Structural Concretes with Waste-Based Lightweight Aggregates: From Landfill to Engineered Materials[J].Environmental Science & Technology: ES&T,2009(18):7123-7129. |
| [5] | 李虎杰,陶军.煤矸石制备高强陶粒的试验研究[J].非金属矿,2010(03):20-22. |
| [6] | 黄旭光,李升宇,段乃亭,鞠润,姜志青.利用油页岩废渣生产陶粒的研究[J].新型建筑材料,2011(11):26-28. |
| [7] | 万军,刘恒波,宋美,贾韶辉,贺深阳.利用赤泥制备高强陶粒的试验研究[J].矿冶工程,2011(05):111-113. |
| [8] | 王佳福,吕剑明.利用城市污泥制备陶粒的研究[J].硅酸盐通报,2012(03):706-710. |
| [9] | 李琳,王晴,王宇,罗海燕.膨胀页岩轻集料的焙烧制度和性能的研究[J].混凝土,2010(10):95-96,106. |
| [10] | 刘军,李振国,王东山,牛晚扬.焙烧制度对矿渣粉煤灰陶粒物理性能的影响[J].沈阳建筑大学学报（自然科学版）,2005(05):511-514. |
| [11] | 钱觉时,罗晖,陈伟,陈平,邓成,岳燕飞,黄义雄.污水污泥页岩陶粒的烧成工艺与性能[J].材料科学与工艺,2010(06):852-856. |
| [12] | 元敬顺,孙婧,岳丽娇,闫杰.热激发张家口尚义页岩的火山灰活性研究[J].硅酸盐通报,2013(03):476-481,485. |
| [13] | 元敬顺,阎杰.碳化硅添加剂对紫色页岩陶粒烧胀性的影响[J].沈阳理工大学学报,2012(05):80-83. |
| [14] | 郭玉顺,丁建彤.粉煤灰陶粒烧胀规律与膨胀机理研究[J].粉煤灰,2003(03):15-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%