热镀锌钢板上单一的铈盐、硅烷钝化膜有一些缺点,对提高其耐蚀性作用不大.为此,将热镀锌钢板先经铈盐溶液处理,再用乙烯基三甲氧基硅烷溶液浸渍,获得了铈盐/硅烷复合钝化膜.采用扫描电镜(SEM)、俄歇电子能谱(AES)、盐水全浸试验和电化学交流阻抗谱(EIS)研究了复合膜层的表面形貌、结构特性和耐蚀性能.结果表明:硅烷膜能较好地填充铈盐转化膜中的裂纹,铈盐/硅烷复合膜层连续、完整、致密,厚400~450 nm,与基体结合较好,复合膜中硅烷膜/铈盐转化膜/锌基体的化学成分呈连续的梯度变化;与热镀锌钢相比,单一铈盐转化膜、硅烷膜的交流阻抗值增加了1个多数量级,复合膜的则增加了约2个数量级,复合膜层的耐蚀性较单一膜层显著增强,且优于常规铬酸盐钝化膜.

参考文献

[1] 张慧敏,伍林,易德莲,华侨,陶茂胜,欧阳兆辉,秦悦.热镀锌钢板无铬钝化膜的改性及其耐蚀性能[J].材料保护,2012(01):4-6.
[2] Aramaki K .A self-healing protective film prepared on zinc by treatment in a Ce(NO3)3 solution and modification with Ce(NO3)3[J].Corrosion Science,2005,47(05):1285-1298.
[3] Montemor MF.;Simoes AM.;Ferreira MGS. .Composition and corrosion behaviour of galvanised steel treated with rare-earth salts: the effect of the cation [Review][J].Progress in Organic Coatings: An International Review Journal,2002(2):111-120.
[4] Mirghasem Hosseini,Habib Ashassi-Sorkhabi,Heshmat Allah Yaghobkhani Ghiasvand.Corrosion Protection of Electro-Galvanized Steel by Green Conversion Coatings[J].稀土学报(英文版),2007(05):537-543.
[5] LU Jin-tang,WU Hai-jiang,KONG Gang,CHE Chun-shan,XU Qiao-yu.Growth and corrosion behavior of rare earth film on hot-dip galvanized steel[J].中国有色金属学会会刊(英文版),2006(06):1397-1401.
[6] T. Van Schaftinghen;C. Le Pen;H. Terryn;F. Horzenberger .Investigation of the barrier properties of silanes on cold rolled steel[J].Electrochimica Acta,2004(17/18):2997-3004.
[7] Zand, BN;Mahdavian, M .Corrosion and adhesion study of polyurethane coating on silane pretreated aluminum[J].Surface & Coatings Technology,2009(12):1677-1681.
[8] Bexell U;Grehk TM .A corrosion study of hot-dip galvanized steel sheet pre-treated with gamma-mereaptopropyltrimethoxysilane[J].Surface & Coatings Technology,2007(26):4734-4742.
[9] 单凤君,王双红,刘常升,齐国超.热镀锌钢板表面氨基硅烷膜的制备及其耐腐蚀性能[J].材料保护,2011(01):6-9.
[10] Zucchi F;Frignani A;Grassi V et al.Organo-silane coatings for AZ31 magnesium alloy corrosion protection[J].Materials Chemistry and Physics,2008,110(2/3):263-268.