由TEM的电子衍射谱观察证实CuZnAl形状记忆合金中马氏体变态A和B之间实际上是二次孪晶关系,其孪生面(13 20 50)为A:C关系的孪生面(1 2 8)和A:D关系的孪生面(1 0 10)的线性组合。
A secondary twinning orientation relationship between A and B martensitevariants in CruZnAl shape memory alloy was confirmed under TEM observation. The twinplane, (13 20 50), is a linear combination of (1 2 8) and (1 0 10) planes, which are twin