对碳热还原氮化合成O'-Sialon/SiC复合材料进行热力学分析,以我国山西大同土、湖南陶土和长江沙等区域性非金属资源为对象,设计技术路线并进行烧结合成.结果表明当温度达1723 K并继续升温时,SiC相含量增加而O'相含量降低;而在1773 K大同土试样中O'相和SiC相的总量达85%以上(碳含量为化学计量时);SEM微观形貌表明具有一定长径比的Sialon柱晶与细小SiC颗粒均匀分布.原位烧结中晶粒生长机制符合金斯特林格动力方程,温度是控制传质的主要因素.
参考文献
| [1] | Makuntuala Keva;Bressiani J C.[J].Key Engineering Materials,2001(189-191):548. |
| [2] | Kitaoka Satoshi;Kawashima Naoki;Suzuki Toshiyuki et al.[J].Journal of the American Ceramic Society,2001,84(09):1945. |
| [3] | Ke Changming;J.-J. Edrees .Fabrication and Microstructure of Sialonbonded Silicon Carbide[J].Journal of the European Ceramic Society,1999(12):2165-2172. |
| [4] | Vlasova M;Vinokurov V B;Grigor'ev O N et al.[J].Materials Science and Engineering A,2004,366:325. |
| [5] | 张海军;李文超;钟香崇 等.[J].中国稀有金属学报,2000,24(01):25. |
| [6] | J G Lee;IVAN B .[J].Journal of the American Ceramic Society,1979,58(09):869. |
| [7] | Radwan M;Lashiwagi T;Miyamoto Y.[J].Journal of the European Ceramic Society,2003(23):2337. |
| [8] | 潘伟;黄月 等.Method of Sialon Bonded Silicon Carbide Synthesis from River Sand[P].CN:00105941.6,2000. |
| [9] | 王体壮,徐利华,钱扬保,刘明,姚云.碳热还原氮化法制备SiAlON陶瓷材料[J].佛山陶瓷,2004(08):33-36. |
| [10] | 甄强 .O'-Sialon-BN复合材料的研究及相关热力学性质预报[D].北京科技大学,2000. |
| [11] | 周亚栋.无机材料物理化学[M].武汉:华中科技大学出版社,1994 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%