在实验室试制了热镀锌冷轧DP590双相钢,分析了临界区退火温度对双相钢组织性能的影响,并将同种成分的实验室试制双相钢与工业生产双相钢的组织性能作对比,结果表明：热镀锌双相钢在镀锌段易出现贝氏体组织,且随临界区温度的上升,贝氏体组织含量增多,双相钢的强度上升,而塑性下降;工业试制双相钢,贝氏体和马氏体交互附着在铁素体晶界上,它们的体积分数约占29%,抗拉强度为610MPa,伸长率为31.5%,各项性能符合要求。研究得出,通过控制第二相（马氏体＋贝氏体）体积分数和分布形态,能够充分改善热镀锌双相钢的力学性能。
The hot-dip galvanized 590 Mpa grade cold rolling dual phase steels were trial-produced in laboratory.The effects of critical annealing temperature on microstructures and properties were investigated.Microstructures and properties were compared and analyzed between laboratory and industrial products with the same chemical compositions.The results show that the absence of bainite is usual in hot-dip progress;both the bainite content and the ultimate tensile strength increase and the elongation decrease with the increasing of critical annealing temperature.The bainite and martensite volume fraction of industrial products is 29%.The ultimate tensile strength and elongation is 610 MPa and 31.5%,respectively,and the performance meets the requirement.The research indicate that if the volume fraction and distribution patters of the second phase（bainite＋ martensite） can be controlled,the mechanical properties of hot-dip galvanized dual phase will be fully improved.
参考文献
| [1] | Takehide SENUMA .Physical Metallurgy of Modern High Strength Steel Sheets[J].ISIJ International,2001(6):520-532. |
| [2] | 江海涛,唐荻,米振莉.汽车用先进高强度钢的开发及应用进展[J].钢铁研究学报,2007(08):1-6. |
| [3] | LePera Fs .Improved Etching Technique to Emphasize Mar-tensite and Bainite in High-strength Dual-phase Steel[J].Met,1980,32:38. |
| [4] | 马鸣图;吴宝榕.双相钢一物理和力学冶金[M].北京:冶金工业出版社,2009 |
| [5] | 陈杰,唐荻,赵征志,江海涛.热镀锌退火温度对DP780组织和性能的影响[J].热加工工艺,2010(08):155-158. |
| [6] | 徐刚,金光灿,赵征志,赵爱民.退火温度对800MPa级热镀锌双相钢组织性能的影响[J].物理测试,2009(02):22-25. |
| [7] | Kumar, A;Singh, SB;Ray, KK .Influence of bainite/martensite-content on the tensile properties of low carbon dual-phase steels[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):270-282. |
| [8] | Qingge Meng;Jun Li;Jian Wang;Zuogui Zhang;Lixiang Zhang .Effect of water quenching process on microstructure and tensile properties of low alloy cold rolled dual-phase steel[J].Materials & Design,2009(7):2379-2385. |
| [9] | Vanessa M Smith;David L Gard;Gregory A Keoleian .UI-tralight Steel Auto Body-Advanced Vechicle Concepts(UL-SAB-AVC)Report[R].A1S1,Copyright by the International Iron and Steel Institute,Train-ing Session Document,2002. |
| [10] | 袁明生.先进高强度热镀锌钢面临的挑战及其研究[J].世界钢铁,2006(03):10. |
| [11] | Erdogan M;Preiestner R .Effect of Epitaxial Ferrite on Yielding and Plastic Fow in Dual-Phase Steel in Tension and Compression[J].Materials Science and Technology,1999,15:1273. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%