本文研究了大晶粒Ｆｅ_３Ａｌ基合金Ｆｅ—２８Ａｌ—２Ｔｉ合金的高温变形行为。发现该合金在７５０℃到９００℃应变速率为１×１０~（－３）／ｓ时以及在８５０℃一个较宽的应变速率范围内具有超塑性，最佳延伸率可超过５００％。８５０℃不同应变速率下，ｍ值可以从０．２２变化到０．４１金相及ＴＥＭ观察表明变形过程中发生了明显的动态再结晶，并由此导致了大晶粒Ｆｅ_３Ａｌ合金中的超塑性。
High temperature deformation behaviour of Fe-28Al-2Ti alloy with large grains was examined. This alloy showed superplasticity in the temperature range of 750℃ to 900℃ under a strain rate of 1 × 10~(-3)/ s and maintained superplastic it at 850℃ in a relatively wide range of strain rate. The highest m value may exceed 500%. At 850℃ . m value changes from 0.22 to 0.41 under different strain rates. Optical and TEM observations revealed that a dynamic recrystallization process took place with the deformation process and this in turn resulted in the superplasticity in this alloy with large grains Correspondent: LIN Dongliang,professor , Department of Materials Science, Shanghai Jiaotong University,Shanghai 200030
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | McKameyCG,DeVanJH,TortorelliPF,SikkaVK．JMaterRes,1991 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%