以低相对分子质量的聚丙烯为原料,采用气-固相法制备了聚丙烯的氯化原位接枝共聚物.溶解性测试发现,当氯化聚丙烯(CPP)的氯含量为50.1％时,溶解度可达到90.0％,基本可在二甲苯中完全溶解,但是CPP的附着力相当差,不能满足涂料要求.通过氯化原位接枝共聚(ISCGC)的方法向CPP大分子链引入极性基团可以提高产物的附着力.本研究讨论了单体种类及配比对产物附着力的影响,最终确定了体系为单体甲基丙烯酸缩水甘油酯/马来酸酐共聚接枝时,产物的附着力最佳,可达到0级.
参考文献
| [1] | 马运兰;刘玉明 .氯化聚丙烯的生产技术进展、市场前景及发展建议[J].塑料制造,2008,7:70-73. |
| [2] | 崔小明.氯化聚丙烯的生产应用与市场前景[J].合成材料老化与应用,2002(03):36-39. |
| [3] | Zhaon-Lei Fan;Da-Zhung Liu;Jian-Ji Wang .Study on the Miscibility of Chlorinated Polypropylene with Alkyd Resin by Dilute Solution Viscometry[J].Physics and Chemistry of Liquids,2003(4):391-397. |
| [4] | Lin CW.;Lee WL. .An investigation on the modification of polypropylene by grafting of maleic anhydride based on the aspect of adhesion[J].Journal of Applied Polymer Science,1998(2):383-387. |
| [5] | Xiao HW;Yu FY;Yu Y;Huang SQ .Grafting of glycidyl methylacrylate onto chlorinated polypropylene and its bonding to aluminum flake[J].Journal of Applied Polymer Science,2007(4):2515-2521. |
| [6] | MINOURA Y;UEDA M;MIZUNUMA S .The reaction of polypropylene with maleic anhydride[J].Journal of Applied Polymer Science,1969,13(08):1625-1640. |
| [7] | 聂建华,程江.塑料涂料用马来酸酐接枝氯化聚丙烯的合成与性能[J].电镀与涂饰,2009(12):53-56,59. |
| [8] | 李瑜,李红波,朱一韦,顾一平,井新利.改性氯化聚丙烯的性能与应用[J].中国涂料,2009(04):52-56. |
| [9] | 范忠雷,刘大壮,董雪茹,马向东.马来酸酐接枝率对氯化聚丙烯和醇酸树脂相容性的影响[J].塑料工业,2005(z1):168-170. |
| [10] | 傅和青,黄洪,张心亚,陈焕钦.丙烯酸改性氯化聚丙烯的合成和粘接性能的研究[J].粘接,2004(04):8-10. |
| [11] | 林达,骆琼宇,胡益男,侯琳熙.氯化聚丙烯多元共聚物的制备及粘结作用[J].广东化工,2009(02):7-9. |
| [12] | 肖坤立,周晓东.CPP-g-GMA对聚丙烯及其复合材料涂装性能的改善[J].玻璃钢/复合材料,2009(04):45-48. |
| [13] | WANG S S;ZHAO Z Q;WANG N et al.Structure and mechanism of functionalization of isotactic polypropylene via in situ chlorination graft copolymerization[J].Polymer International,2011,60(07):1068-1077. |
| [14] | 宋志强 .固相法低黏度HCPE的制备、表征及接枝改性研究[D].山东青岛:青岛科技大学,2012. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%